Damage Behavior in Unidirectional CFRP Laminates with Ply Discontinuity
Source abstract
Abstract
Abstract This study presents a comprehensive quantitative investigation into the material properties and damage behavior of unidirectional carbon fiber reinforced plastic laminates with ply discontinuities. Laminates with varying resin gap lengths were evaluated. In situ edge observations and X-ray computed tomography were employed to assess the damage processes in the area of the ply discontinuity. These methods examined initially occurring cracks, secondary cracks, and delamination. Some unexpected cracking behavior was observed in this study. For instance, initial cracks were observed to form not at the interface but at a distance from the resin–ply interface, likely due to a constraint condition caused by the chemical shrinkage of the resin during the curing process. Furthermore, all cracks in the resin region curved toward the center, with successively formed cracks having higher curvatures. This behavior can be attributed to the redistribution of principal stresses within the resin pocket following the initial cracks. The matrix cracking was followed by delamination that started from the tips of the matrix cracks and progressed toward the ends of the specimen. Additionally, the number and locations of cracks in the resin pocket were influenced by the length of the resin gap and the uniformity of the thickness and width of the specimen. In addition to the experimental investigation, a stress-based variational analysis was employed to predict crack onset stresses in the laminates. The analysis successfully calculated the energy release rate for laminates with varying resin pocket lengths and provided predictions for crack onset stresses. The analytical predictions demonstrated good agreement with the experimental observations, enhancing the understanding of resin pocket behavior in CFRP laminates.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Mechanical Behavior of Composites · Structural Behavior of Reinforced Concrete · Composite Structure Analysis and Optimization
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (49)
Show source-provided references
1. Ogihara, S., Takeda, N.: Interaction between transverse cracks and delamination during damage progress in CFRP cross-ply laminates. Compos. Sci. Technol. 54(4), 395–404 (1995)10.1016/0266-3538(95)00084-4 ↗
2. Yokozeki, T., Aoki, Y., Ogasawara, T.: Experimental characterization of strength and damage resistance properties of thin-ply carbon fiber/toughened epoxy laminates. Compos. Struct. 82(3), 382–389 (2008)10.1016/j.compstruct.2007.01.015 ↗
3. Deng, H., Mochizuki, A. Fikry, M.J., Abe, S., Ogihara, S., Koyanagi, J.: Numerical and experimental studies for fatigue damage accumulation of CFRP cross-ply laminates based on entropy failure criterion. Materials 16(1) (2023)10.3390/ma16010388 ↗
4. Ogihara, S., Takeda, N., Kobayashi, S., Kobayashi, A.: Effects of stacking sequence on microscopic fatigue damage development in quasi-isotropic CFRP laminates with interlaminar-toughened layers. Compos. Sci. Technol. 59(9), 1387–1398 (1999)10.1016/S0266-3538(98)00180-8 ↗
5. Ramesh, T., Singh, C.V.: Damage and failure of composite materials. Cambridge University Press, Cambridge New York (2012)978-0-521-81942-8
6. Mack, J.P., Mirza, F., Banik, A., Khan, M.H., Tan, K.T.: Hybridization of face sheet in sandwich composites to mitigate low temperature and low velocity impact damage. Compos. Struct. 338, 118101 (2024)10.1016/j.compstruct.2024.118101 ↗
7. Koyanagi, J., Mochizuki, A., Higuchi, R., Tan, V.B.C., Tay, T.E.: Finite element model for simulating entropy-based strength-degradation of carbon-fiber-reinforced plastics subjected to cyclic loadings. Int. J. Fatigue 165, 107204 (2022)10.1016/j.ijfatigue.2022.107204 ↗
8. Isaac, C.W., Ezekwem, C.: A review of the crashworthiness performance of energy absorbing composite structure within the context of materials, manufacturing and maintenance for sustainability. Compos. Struct. 257, 113081 (2021)10.1016/j.compstruct.2020.113081 ↗
9. Willmann, E., Boll, B., Scheel, M., Meißner, R.H., Fiedler, B.: Health monitoring of CFRP laminates under cyclic loading via vibro-acoustic modulation based measurements. Compos. Struct. 308, 116696 (2023)10.1016/j.compstruct.2023.116696 ↗
10. Varughese, B., Mukherjee, A.: A ply drop-off element for analysis of tapered laminated composites. Compos. Struct. 39(1), 123–144 (1997)10.1016/S0263-8223(97)00132-3 ↗
11. Abdulhamid, H., Bouvet, C., Michel, L., Aboissière, J., Minot, C.: Influence of internally dropped-off plies on the impact damage of asymmetrically tapered laminated CFRP. Compos. Part A: Appl. Sci. Manufact. 68, 110–120 (2015)10.1016/j.compositesa.2014.09.024 ↗
12. Mirza, F., Mack, J.P., Banik, A., Khan, M.H., Tan, K.T.: Post impact flexural behavior investigation of hybrid foam-core sandwich composites at extreme arctic temperature. Compos. Sci. Technol. 258, 110897 (2024)10.1016/j.compscitech.2024.110897 ↗
13. Ahamed, J., Joosten, M., Callus, P., Wisnom, M.R., Wang, C.H.: Ply-overlap hybrid technique for joining dissimilar composite materials. Mater. Des. 100, 157–167 (2016)10.1016/j.matdes.2016.03.112 ↗
14. Xie, C., Wan, Y., Wang, L., Yu, X., Ma, Y.: Experimental investigation on the compression-after-double-impact behaviors of GFRP laminates embedded with aluminum mesh. Polym. Compos. 1–11 (2024)10.1002/pc.29094 ↗
15. Ravichandran, B., Balasubramanian, M.: Joining methods for fiber reinforced polymer FRP composites a critical review. Compos. Part A: Applied Science and Manuf. 186, 108394 (2024)10.1016/j.compositesa.2024.108394 ↗
16. Chen, Y., Wan, Y., Li, C., Zhang, J.: Tensile behavior of mechanical joint for GFRP/metal mesh hybrid laminate after low-velocity impact. Polym. Compos. 1–14 (2025)10.1002/pc.29463 ↗
17. Endalew, A.M., Woo, K., Cairns, D.S.: Effect of drilling-induced defects on progressive damage of open-hole composite laminates under compression. Adv. Compos. Mater. 31(4), 399–427 (2022)10.1080/09243046.2021.2021358 ↗
18. Zhang, Y., Zhou, Z., Pan, S., Tan, Z.: Comparison on failure behavior of three-dimensional woven carbon/carbon composites joints subjected to out-of-plane loading at room and high temperature. Compos. Commun. 23, 100567 (2021)10.1016/j.coco.2020.100567 ↗
19. Oromiehie, E., Prusty, B.G., Compston, P., Rajan, G.: Automated fibre placement based composite structures: Review on the defects, impacts and inspections techniques. Compos. Struct. 224, 110987 (2019)10.1016/j.compstruct.2019.110987 ↗
20. Minakuchi, S., Simacek, P., Advani, S.G.: In-situ consolidation deformation of composite laminate with gaps of various widths. Compos. Part A: Appl. Sci. Manuf. 180, 108054 (2024)10.1016/j.compositesa.2024.108054 ↗
21. Cui, W., Wisnom, M.R., Jones, M.: An experimental and analytical study of delamination of unidirectional specimens with cut central plies. J. Reinf. Plast. Compos. 13(8), 722–739 (1994)10.1177/073168449401300804 ↗
22. Ganesan, R., Liu, D.Y.: Progressive failure and post-buckling response of tapered composite plates under uni-axial compression. Compos. Struct. 82(2), 159–176 (2008)10.1016/j.compstruct.2006.12.014 ↗
23. Fikry, M.J., Vinogradov, V., Ogihara, S.: Mechanical properties and damage behavior of tapered unidirectional CFRP laminates. Mech. Eng. J. 10(4), 23–00079–23–00079 (2023)10.1299/mej.23-00079 ↗
24. Gan, K.W., Allegri, G., Hallett, S.R.: A simplified layered beam approach for predicting ply drop delamination in thick composite laminates. Mater. Des. 108, 570–580 (2016)10.1016/j.matdes.2016.06.105 ↗
25. Fish, J., Lee, S.: Delamination of tapered composite structures. Eng. Fracture Mech. 34, 43–54 (1989)10.1016/0013-7944(89)90241-5 ↗
26. Botting, A.D., Vizzini, A.J., Lee, S.W.: Effect of ply-drop configuration on delamination strength of tapered composite structures. AIAA J. 34, 1650–1656 (1996)10.2514/3.13285 ↗
27. He, K., Hoa, S.V., Ganesan, R.: The study of tapered laminated composite structures: a review. Composit. Sci. Technol. 60(14), 2643–2657 (2000)10.1016/S0266-3538(00)00138-X ↗
28. Zhang, B., Kawashita, L.F., Jones, M.I., Lander, J.K., Hallett, S.R.: An experimental and numerical investigation into damage mechanisms in tapered laminates under tensile loading. Compos. Part A: Appl. Sci. Manuf. 133, 105862 (2020)10.1016/j.compositesa.2020.105862 ↗
29. Fikry, M.J., Vinogradov, V., Ogihara, S.: Experimental observation and modeling of resin pocket cracking in unidirectional laminates with ply discontinuity. Compos. Sci. Technol. 218, 109175 (2022)10.1016/j.compscitech.2021.109175 ↗
30. Nakatani, H., Nakaya, K., Matsuba, A., Kouno, Y., Ogihara, S.: Effect of prepreg cut on the mechanical properties in CFRP laminates. J. Solid Mech. Mater. Eng. 5(12), 742–752 (2011)10.1299/jmmp.5.742 ↗
31. Nakatani, H., Nakaya, K., Matsuba, A., Kouno, Y., Ogihara, S.: Damage behavior in unidirectional CFRP laminates with fiber discontinuity. Trans. JSME, Series A 79(799), 294–303 (2013)10.1299/kikaia.79.294 ↗
32. Nakatani, H., Nagata, Y., Kitamura, R., Matsuba, A., Kouno, Y., Ogihara, S.: Damage behavior in CFRP laminates containing fiber discontinuities of different sizes. Trans. JSME 81(831), 15–00226 (2015)
33. Nagata, Y., Nakatani, H., Matsuba, A., Kouno, Y., Ogihara, S.: Effect of fiber discontinuity on mechanical properties of interlaminar-toughened CFRP laminates. Trans. JSME 81(825), 14–00699 (2015)
34. Fikry, M.J., Wang, Q., Irita, M., Ri, S., Toyama, N., Vinogradov, V., Ogihara, S.: Measurement of microscopic strain distributions of CFRP laminates with fiber discontinuities by sampling moiré method. Adv. Compos. Mater. 31(3), 273–288 (2022)10.1080/09243046.2021.1975208 ↗
35. Fikry, M.J., Vinogradov, V., Ogihara, S.: Analytical prediction of the local young’s modulus in CFRP laminate with ply discontinuity: a variational approach. Adv. Compos. Mater. 32(6), 843–865 (2023)10.1080/09243046.2023.2165873 ↗
36. Fikry, M.J., Ogihara, S., Vinogradov, V.: The effect of matrix cracking on mechanical properties in frp laminates. Mech. Adv. Mater. Modern Process. 4(3), 1–16 (2018)
37. Fikry, M.J., Ogihara, S.: Damage behaviors in cross-ply cloth CFRP laminates cured at different temperatures. Mech. Eng. J. 7(5), 20–00383 (2020)10.1299/mej.20-00383 ↗
38. Fikry, M.J., Terashi, N., Koizumi, K., Ogihara, S.: Inhibition of interlaminar damage in CFRP laminates by inserting non-woven carbon fiber interlaminar reinforced tissue. Adv. Compos. Mater. 1–21 (2024)10.1080/09243046.2024.2439653 ↗
39. Zarrelli, M., Skordos, A.A., Partridge, I.K.: Investigation of cure induced shrinkage in unreinforced epoxy resin. Plast. Rubber Compos. 31(9), 377–384 (2002)10.1179/146580102225006350 ↗
40. Kravchenko, O.G., Li, C., Strachan, A., Kravchenko, S.G., Pipes, R.B.: Prediction of the chemical and thermal shrinkage in a thermoset polymer. Compos. Part A: Appl. Sci. Manuf. 66, 35–43 (2014)10.1016/j.compositesa.2014.07.002 ↗
41. Groves, S.E., Harris, C.E., Highsmith, A.L., Allen, D.H., Norvell, R.G.: An experimental and analytical treatment of matrix cracking in cross-ply laminates. Exper. Mech. 27(1), 73–79 (1987)10.1007/BF02318867 ↗
42. Hu, S., Bark, J.S., Nairn, J.A.: On the phenomenon of curved microcracks in [(s)/90n]s laminates: Their shapes, initiation angles and locations. Compos. Sci. Technol. 47(4), 321–329 (1993)10.1016/0266-3538(93)90001-W ↗
43. Jalalvand, M., Wisnom, M.R., Hosseini-Toudeshky, H., Mohammadi, B.: Experimental and numerical study of oblique transverse cracking in cross-ply laminates under tension. Compos. Part A: Appl. Sci. Manuf. 67, 140–148 (2014)10.1016/j.compositesa.2014.08.004 ↗
44. Fikry, M.J., Ogihara, S., Vinogradov, V.: Application of dic to deformation measurement around damages in CFRP cross-ply laminates. Mech. Eng. J. 6(3), 19–00003 (2019)10.1299/mej.19-00003 ↗
45. Hashin, Z.: Analysis of cracked laminates: a variational approach. Mech. Mater. 4(2), 121–136 (1985)10.1016/0167-6636(85)90011-0 ↗
46. Hajikazemi, M., Sadr, M.H.: A variational model for stress analysis in cracked laminates with arbitrary symmetric lay-up under general in-plane loading. Int. J. Solids Struct. 51(2), 516–529 (2014)10.1016/j.ijsolstr.2013.10.024 ↗
47. Hajikazemi, M., Sadr, M.H.: Stiffness reduction of cracked general symmetric laminates using a variational approach. Int. J. Solids Struct. 51(7), 1483–1493 (2014)10.1016/j.ijsolstr.2013.12.040 ↗
48. Hajikazemi, M., Sadr, M.H., Hosseini-Toudeshky, H., Mohammadi, B.: Thermo-elastic constants of cracked symmetric laminates: A refined variational approach. Int. J. Mech. Sci. 89, 47–57 (2014)10.1016/j.ijmecsci.2014.08.008 ↗
49. Vinogradov, V.: A variational method for analysis of laminates with parallel arrays of intralaminar cracks. Int. J. Numerical Methods Eng. 120(5), 666–705 (2019)10.1002/nme.6152 ↗