Thermal Degradation and Decomposition of FR4 Laminate PCB Substrates Joined by Friction Riveting
Source abstract
Abstract
Abstract This study investigates the thermal degradation and chemical transformations of friction-riveted glass fiber-reinforced epoxy laminate (FR4) printed circuit boards (PCBs) with different copper configurations. The primary objective is to identify the critical degradation temperatures and the impact of copper layers on joint integrity and thermal stability. Cross-sectional analyses revealed that joints produced at 250 °C exhibited minimal rivet deformation, while those at 360 °C showed significant deformation and increased epoxy degradation. Thermal analyses, including Differential Scanning Calorimetry (DSC) and Thermogravimetric Analysis (TGA), identified critical degradation temperatures at 327 °C for FR4-I Cu with a single copper layer and 329 °C for FR4-II Cu with double copper layers. The presence of the additional copper layer in FR4-II Cu significantly improved thermal stability, with total mass loss reduced from 29.8% (FR4-I Cu) to 23.5% (FR4-II Cu) at a heating rate of 20 °C/min. The loss of flame-retardant components at elevated temperatures raises concerns for the fire safety of PCBs in electronic devices. These findings highlight the importance of selecting appropriate FR4 configurations for applications exposed to high temperatures, enhancing reliability and safety in the electronics industry.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Additive Manufacturing and 3D Printing Technologies · Fiber-reinforced polymer composites · Mechanical Behavior of Composites
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (27)
Show source-provided references
1. Smith, C.: Thermochemical and physical properties of printed circuit board laminates and other polymers used in the electronics industry. Polym. Test. 52, 234–245 (2016). https://doi.org/10.1016/j.polymertesting.2016.04.01710.1016/j.polymertesting.2016.04.017 ↗
2. Capricho, J.C., Fox, B., Hameed, N.: Multifunctionality in Epoxy resins. Polym. Rev. 60(1), 1–41 (2020). https://doi.org/10.1080/15583724.2019.165006310.1080/15583724.2019.1650063 ↗
3. Favstritsky, N.A., Wang, J.L.: Flame retardant brominated styrene-based polymers. VI. Synthesis and characterization of dibromostyrene graft latices. United States (1995)
4. Chulikavit, N., Huynh, T., Khatibi, A., et al.: Thermal degradation and flame spread characteristics of epoxy polymer composites incorporating mycelium. Sci. Rep. 13, 17812 (2023). https://doi.org/10.1038/s41598-023-45097-010.1038/s41598-023-45097-0 ↗
5. Azam, S., Munshi, S., Hassan, M.K., Fragoso, A.: Temperature-dependent sheet resistance and surface characterization of Thin Copper films Bonded to FR4 Composite under mechanical vibrations. Applied Sciences; 13(13):7941 (2023). https://doi.org/10.3390/app1313794110.3390/app13137941 ↗
6. Paczkowski, M., Reddy, S.: Solder mask strategies for Surface Mount Assembly. Soldering Surf. Mt. Technol. 5(2), 12–19 (1993). https://doi.org/10.1108/eb03782210.1108/eb037822 ↗
7. Polanský, R., Prosr, P., Čermák, M.: Determination of the thermal endurance of PCB FR4 epoxy laminates via thermal analyses. Polym. Degrad. Stab. 105, 107–115 (2014). https://doi.org/10.1016/j.polymdegradstab.2014.03.04310.1016/j.polymdegradstab.2014.03.043 ↗
8. Mumby, S.J.: An overview of laminate materials with enhanced dielectric properties. J. Electron. Mater. 18(2), 241–250 (1989). https://doi.org/10.1007/bf0265741510.1007/bf02657415 ↗
9. Kırbaş, B.: Effect of perlite on the thermal conductivity, thermal degradation, and mechanical properties of epoxy materials. High Perform. Polym. 34(8), 880–888 (2022). https://doi.org/10.1177/0954008322109214710.1177/09540083221092147 ↗
10. Sun, S., Yu, Q., Yu, B., Zhou, F.: New Progress in the Application of Flame-Retardant Modified Epoxy Resins and Fire-Retardant Coatings. In Coatings,13, Issue 10, p. 1663 (2023). https://doi.org/10.3390/coatings1310166310.3390/coatings13101663 ↗
11. Lau, J.H.: Solder Joint Reliability: Theory and Applications. Van Nostrand Reinhold (1991)10.1007/978-1-4615-3910-0 ↗
12. Jiang, N., Zhang, L., Liu, Z.Q., Sun, L., Long, W.M., He, P., Xiong, M.Y., Zhao, M.: Reliability issues of lead-free solder joints in electronic devices. Sci. Technol. Adv. Mater. 20(1), 876–901 (2019). https://doi.org/10.1080/14686996.2019.164007210.1080/14686996.2019.1640072 ↗
13. Pecht, M.: Prognostics and Health Management of Electronics. Wiley-Interscience (2003)
14. Coombs, C.F.: Jr. Printed Circuits Handbook, 6th edn. McGraw-Hill Education (2008)
15. Budynas, R.G., Nisbett, J.K.: Shigley’s Mechanical Engineering Design, 10th edn. McGraw-Hill Education (2015)
16. Rodrigues, C.F., Blaga, L., Klusemann, B.: Friction riveting of FR4 substrates for printed circuit boards: Influence of process parameters on process temperature development and joint properties. J. Mater. Res. Technol. 24, 4639–4649 (2023). https://doi.org/10.1016/j.jmrt.2023.04.09210.1016/j.jmrt.2023.04.092 ↗
17. Amancio-Filho, S.T., Roeder, J., Nunes, S., dos Santos, J., Beckmann, F.: Thermal degradation of polyetherimide joined by friction riveting (FricRiveting). Part I: Influence of rotation speed. Polym. Degrad. Stab. 93(8), 1529–1538 (2008). https://doi.org/10.1016/j.polymdegradstab.2008.05.01910.1016/j.polymdegradstab.2008.05.019 ↗
18. Amancio-Filho, S.T., Blaga, L.A.: Joining of Polymer-Metal Hybrid Structures. Wiley (2018)10.1002/9781119429807 ↗
19. Rodrigues, C.F., Blaga, L., dos Santos, J., Canto, L., Hage, E., Amancio-Filho, S.: FricRiveting of aluminum 2024-T351 and polycarbonate: Temperature evolution, microstructure and mechanical performance. J. Mater. Process. Technol. 214(10), 2029–2039 (2014). https://doi.org/10.1016/j.jmatprotec.2013.12.01810.1016/j.jmatprotec.2013.12.018 ↗
20. Rodrigues, C.F., Boas, M.C.V., Blaga, L., et al.: Application of Friction Riveting technique for the assembly of electronic components on printed circuit boards (PCB). Int. J. Adv. Manuf. Technol. (2024). https://doi.org/10.1007/s00170-024-14054-010.1007/s00170-024-14054-0 ↗
21. Chike, K.E., Myrick, M.L., Lyon, R.E., Angel, S.M.: Raman and Near-Infrared studies of an Epoxy Resin. Appl. Spectrosc. 47(10), 1631–1635 (1993). https://doi.org/10.1366/000370293433471410.1366/0003702934334714 ↗
22. Cabanelas, J.C., Antonelli, C., San Miguel, V., Serrano, B., Baselga, J.: Spectroscopic analysis of Epoxy/Thermoplastic blends. In: Parameswaranpillai, J., Hameed, N., Pionteck, J., Woo, E. (eds.) Handbook of Epoxy Blends. Springer (2017). https://doi.org/10.1007/978-3-319-40043-3_20 Cham10.1007/978-3-319-40043-3_20 ↗
23. Wen, H., Zhang, X., Xia, R., Yang, Z., Wu, Y.: Thermal Decomposition Properties of Epoxy Resin in SF6/N2 Mixture. In Materials,12, Issue 1, p. 75 (2018). https://doi.org/10.3390/ma1201007510.3390/ma12010075 ↗
24. Hu, M., Tang, B., Liang, Q., Luo, Z., Luo, C., Wang, J., Zhang, L., Zhu, L.: Monitoring and prediction of thermal failure of high-voltage switchgear insulation materials by studying the thermodynamic properties of FR-4 epoxy resin and the characteristic gas of thermal decomposition. Journal of Physics: Conference Series, 2387(1), 012028 (2022). https://doi.org/10.1088/1742-6596/2387/1/01202810.1088/1742-6596/2387/1/012028 ↗
25. Tait, J., Edwards, H., Farwell, D., Yarwood, J.: Fourier transform Raman spectroscopic examination of two amine-based epoxy resin crosslinking agents. Spectrochim. Acta Part A Mol. Biomol. Spectrosc. 51(12), 2101–2106 (1995). https://doi.org/10.1016/0584-8539(95)01456-510.1016/0584-8539(95)01456-5 ↗
26. Xue, G.: Fourier transform Raman spectroscopy and its application for the analysis of polymeric materials. Prog. Polym. Sci. 22, 313–406 (1997). https://doi.org/10.1016/S0079-6700(96)00006-810.1016/S0079-6700(96)00006-8 ↗
27. Qiu, C., Luo, J., Ling, Y., Lu, Z., Ni, L., Chen, Y., Zou, H., Heng, Z., Liang, M.: Thermal degradation behavior and mechanism of Organosilicon Modified Epoxy Resin. Macromol. Chem. Phys. 223(20) (2022). https://doi.org/10.1002/macp.20220016410.1002/macp.202200164 ↗