Effect of polymer molar mass and montmorillonite content on polymer flooding using a glass micromodel

Abstract Generally, the nanoclay dispersions in polymer of different materials reveal rheological and morphological behaviors. In this research, the effects of the sodium montmorillonite and molar mass of the hydrolyzed polyacrylamide were experimentally investigated on the oil recovery factor (Estimation of in-place oil to recoverable oil) at the pore scale using a glass micromodel. Experiments were designed based on Central Composite Design method for high molar mass clay polymer nanocomposites (HCPN) and low molar mass clay polymer nanocomposites (LCPN). Two quadratic models were thus developed to predict oil recovery of both clay polymer nanocomposites (CPN). According to the images of the micromodel pores with the nanoclay, the oil droplets changed to emulsion in the solution, making them pass easily through the pores. Optimization results showed that the oil recovery for HCPN with 1493 ppm of polymer concentration and with nanoclay mass ratio of 1, was about 79. Also, for LCPN with 2306 ppm of polymer concentration, and 0.85 mass ratio of nanoclay the oil recovery was reached to 74. Furthermore, the obtained results of scanning electron microscope, energy-dispersive X-ray spectroscopy and X-Ray diffraction appropriately confirmed dispersion of nanoparticles in solution of both optimal CPN. Moreover, the thermal gravimetric analysis presented an increase of thermal strength in the presence of nanomaterials. In addition, both CPN of HCPN and LCPN indicated non-Newtonian behavior. However, in the frequency