The promoting effect of palygorskite on CeO2-WO3-TiO2 catalyst for the selective catalytic reduction of NOx with NH3
Source abstract
Abstract
Abstract A series of CeO2-WO3-Pal/TiO2 catalysts were prepared by doping with different contents of palygorskite (Pal). More importantly, the CeO2-WO3–20%Pal/TiO2 catalyst prepared by impregnation method showed excellent performance for selective catalytic reduction (SCR) NOx with NH3. In more detail, the NO conversion could reach to 82% at 240 °C and keep above 92% in the range of 280–400 °C. According to the NH3-TPD tests, the surface acidity of the CeO2-WO3–20%Pal/TiO2 catalyst was increased obviously, which is beneficial to the NH3 adsorption in the SCR reaction. Besides, through XRD, XPS, Raman spectra and TEM characterizations, it suggested that the active species cerium and tungsten were uniformly dispersed on the surface of Pal, and it is very important for the improvement of SCR performance. In a word, the optimum Pal proportion was helpful to improve the catalyst catalytic performance, so it was more widely used in the SCR process.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Catalytic Processes in Materials Science · Catalysis and Oxidation Reactions · Industrial Gas Emission Control
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (57)
Show source-provided references
1. Role of V2O5-WO3/H2Ti3O7-nanotube-model catalysts in the enhancement of the catalytic activity for the SCR-NH3 process10.1016/j.cej.2014.01.002 ↗
2. NO-NH3 coadsorption on vanadia/titania catalysts: determination of the reduction degree of vanadium10.1016/S0926-3373(00)00214-9 ↗
3. Enhanced activity of tungsten modified CeO2/TiO2 for selective catalytic reduction of NOx with ammonia10.1016/j.cattod.2010.01.062 ↗
4. Low-temperature activity and mechanism of WO3-modified CeO2-TiO2 catalyst under NH3-NO/NO2 SCR conditions10.1016/j.pnsc.2012.07.004 ↗
5. Effect of Ni doping in NixMn1-xTi10 (x = 0.1-0.5) on activity and SO2 resistance for NH3-SCR of NO studied with in situ DRIFTS10.1039/C7CY00672A ↗
6. Multivariate analysis of the effect of biodiesel-derived contaminants on V2O5-WO3/TiO2 SCR catalysts10.1016/j.apcatb.2015.10.045 ↗
7. Promotional effect of Nb additive on the activity and hydrothermal stability for the selective catalytic reduction of NOx with NH3 over CeZrOx catalyst10.1016/j.apcatb.2015.06.055 ↗
8. Effect of vanadia and tungsten loadings on the physical and chemical characteristics of V2O5-WO3/TiO2 catalysts10.1016/j.molcata.2003.07.016 ↗
9. The co-effect of Sb and Nb on the SCR performance of the V2O5/TiO2 catalyst10.1016/j.jcis.2011.11.026 ↗
10. Systematic XPS studies of metal oxides, hydroxides and peroxides10.1039/a908800h ↗
11. Preparation and characterization of CeO2/TiO2 catalysts for selective catalytic reduction of NO with NH310.1016/j.catcom.2009.11.024 ↗
12. Novel approach for a cerium-based highly efficient catalyst with excellent NH3-SCR performance10.1039/C4CY00926F ↗
13. A PDGF/VEGF homologue provides new insights into the nucleus grafting operation and immune response in the pearl oyster pinctada fucata10.1016/j.gene.2017.09.019 ↗
14. Cerium modified MnTiOx/attapulgite catalyst for low-temperature selective catalytic reduction of NOx with NH310.1557/jmr.2018.242 ↗
15. Recent progress on establishing structure-activity relationship of catalysts for selective catalytic reduction (SCR) of NOx with NH310.1007/s10563-017-9237-y ↗
16. An environmentally friendly wide temperature CeWTiOx catalyst with superior performance for the selective catalytic reduction NOx with NH310.1016/j.jiec.2018.09.006 ↗
17. Activity and characterization of a Ce-W-Ti oxide catalyst prepared by a single step sol-gel method for selective catalytic reduction of NO with NH310.1016/j.fuel.2015.01.061 ↗
18. A novel CeO2-MoO3-WO3/TiO2 catalyst for selective catalytic reduction of NO with NH310.1016/j.catcom.2017.10.002 ↗
19. Selective catalytic reduction of NO with NH3 over novel iron-tungsten mixed oxide catalyst in a broad temperature range10.1039/C5CY00605H ↗
20. Comparison of the structures and mechanism of arsenic deactivation of CeO2-MoO3 and CeO2-WO3 SCR catalysts10.1021/acs.jpcc.6b03687 ↗
21. La1-xCexMnO3/attapulgite nanocomposites as catalysts for NO reduction with NH3 at low temperature10.1016/j.partic.2016.01.003 ↗
22. Dynamic response of east asian greater white-fronted geese to changes of environment during migration: use of multi-temporal species distribution model10.1016/j.ecolmodel.2017.06.004 ↗
23. Effect of manganese substitution on the structure and activity of iron titanate catalyst for the selective catalytic reduction of NO with NH310.1016/j.apcatb.2009.09.029 ↗
24. Combined spectroscopic and theoretical approach to sulfur-poisoning on Cu-supported Ti-Zr mixed oxide catalyst in the selective catalytic reduction of NOx10.1021/cs5005739 ↗
25. A comparative study of different natural palygorskite clays for fabricating cost-efficient and eco-friendly iron red composite pigments10.1016/j.clay.2018.10.008 ↗
26. Characterization of WOx/CeO2 catalysts and their reactivity in the isomerization of hexane10.1016/j.jcat.2004.01.008 ↗
27. A highly effective catalyst of Sm-MnOx for the NH3-SCR of NOx at low temperature: promotional role of Sm and its catalytic performance10.1021/acscatal.5b00747 ↗
28. Flame-made WO3/CeOx-TiO2 catalysts for selective catalytic reduction of NOx by NH310.1021/acscatal.5b01580 ↗
29. Alkali metal poisoning of a CeO2-WO3 catalyst used in the selective catalytic reduction of NOx with NH3: an experimental and theoretical study10.1021/es203619w ↗
30. Identification of the active sites on CeO2-WO3 catalysts for SCR of NOx with NH3: an in situ IR and Raman spectroscopy study10.1016/j.apcatb.2013.04.043 ↗
31. MnOx-CeO2 mixed oxides prepared by co-precipitation for selective catalytic reduction of NO with NH3 at low temperatures10.1016/j.apcatb.2004.01.023 ↗
32. A superior Ce-W-Ti mixed oxide catalyst for the selective catalytic reduction of NOx with NH3
33. The use of ceria for the selective catalytic reduction of NOx with NH310.1016/S1872-2067(14)60155-8 ↗
34. A highly efficient CeWOx catalyst for the selective catalytic reduction of NOx with NH310.1039/C5CY01282A ↗
35. Low temperature NH3-SCR over Zr and Ce pillared clay based catalysts10.1016/j.fuproc.2013.10.026 ↗
36. Homogeneous MnOx-CeO2 pellets prepared by a one-step hydrolysis process for low-temperature NH3-SCR10.1016/j.powtec.2013.11.015 ↗
37. Shape effect of TiO2 in VOx/TiO2 catalysts for selective reduction of NO by NH310.1039/C5TA02897C ↗
38. Influence of support on the activity of Mn supported catalysts for SCR of NO with ammonia10.1016/j.cattod.2011.09.018 ↗
39. In situ synthesis of CuSAPO-34/cordierite and its selective catalytic reduction of nitrogen oxides in vehicle exhaust: the effect of HF10.1016/j.fuel.2012.09.046 ↗
40. In-situ hydrothermal synthesis of Cu-SSZ-13/cordierite for the catalytic removal of NOx from diesel vehicles by NH310.1016/j.cej.2014.10.086 ↗
41. Improved activity of W-modified MnOx-TiO2 catalysts for the selective catalytic reduction of NO with NH310.1016/j.cej.2015.12.002 ↗
42. Evaluation of Ce(III) and Gd(III) adsorption from aqueous solution using CTS-g-(AA-co-SS)/ISC hybrid hydrogel adsorbent10.1016/S1002-0721(17)60966-9 ↗
43. Cerium-loaded MnOx/attapulgite catalyst for the low-temperature NH3-selective catalytic reduction10.1016/j.jiec.2017.01.034 ↗
44. Deactivation of a Ce/TiO2 catalyst by SO2 in the selective catalytic reduction of NO by NH310.1021/jp8088148 ↗
45. NOx emission reduction and its effects on ozone during the 2008 olympic games10.1021/es200675v ↗
46. In situ supported MnOx-CeOx on carbon nanotubes for the low-temperature selective catalytic reduction of NO with NH310.1039/c2nr33006g ↗
47. Highly effective removal of methylene blue using functionalized attapulgite via hydrothermal process10.1016/j.jes.2014.12.014 ↗
48. One pot synthesis of highly efficient mesoporous ceria-titanium catalyst for selective catalytic reduction of NO10.1039/C6RA17840E ↗
49. Gold supported on ceria nanotubes for CO oxidation10.1016/j.apsusc.2017.04.158 ↗
50. Control synthesis of CeO2 nanomaterials supported gold for catalytic oxidation of carbon monoxide
51. Solvothermal synthesis of well-designed ceria-tin-titanium catalysts with enhanced catalytic performance for wide temperature NH3-SCR reaction10.1016/j.apcatb.2017.12.030 ↗
52. Promotion of redox and stability features of doped Ce-W-Ti for NH3-SCR reaction over a wide temperature range10.1016/j.apsusc.2016.04.090 ↗
53. V2O5-decorated Mn-Fe/attapulgite catalyst with high SO2 tolerance for SCR of NOx with NH3 at low temperature10.1016/j.cej.2017.06.015 ↗
54. A comparative study of metal oxide and sulfate catalysts for selective catalytic reduction of NO with NH310.1080/09593330.2016.1226393 ↗
55. Highly efficient mesoporous V2O5/WO3-TiO2 catalyst for selective catalytic reduction of NOx: effect of the valence of V on the catalytic performance10.1007/s10563-017-9229-y ↗
56. Controlled synthesis of TiO2 shape and effect on the catalytic performance for selective catalytic reduction of NOx with NH310.1007/s10563-018-9244-7 ↗
57. Morphology-controlled synthesis of 3D flower-like TiO2 and the superior performance for selective catalytic reduction of NOx with NH310.1016/j.cej.2018.03.035 ↗