Efficiency of layered double hydroxides in epoxy coating as corrosion inhibitor reservoirs for carbon steel
Source abstract
Abstract
Layered double hydroxides (LDH) are considered as interesting containers for corrosion inhibitors, since they exhibit high ability to release inhibitor as well as to capture aggressive ions from aqueous solution. Epoxy containing organo-modified LDH filler intercalated with ethylenediamine-N,N′-disuccinate anions (EDDS), [Zn2Al(OH)6]+ [EDDS]4−0.25 . 2H2O (LDH-EDDS) with loading from 0% to 1.25% were coated onto carbon steel plates. The efficiency of these coatings against corrosion (barrier properties and release of inhibitors) was assessed by using electrochemical impedance spectroscopy. The evolution of the impedance modulus |Z| at low frequency range during time showed that the 0.75% organo-modified LDH-containing epoxy (thickness 80 μm) exhibited the highest corrosion resistance in the series and the associated value of |Z| at 3 mHz (1010 Ω cm2 after 21 days of immersion in 0.1 mol L−1 NaCl solution) placed it among the best solutions published so far using organo-modified LDH as cargo carrying a corrosion inhibitor. The behavior of this polymer composite was compared to the free-LDH coating by plotting the resistivity profiles along the coating thickness as a function of time. These results showed that (i) the presence of 0.75% LDH-EDDS in the epoxy coating delayed the penetration of water molecules, and (ii) limited corrosion of carbon steel. The efficiency of the organo-modified filler to inhibit the corrosion process was explained by an exchange between interleaved species occurring from released EDDS4− anions and aggressive Cl− ions being captured.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Corrosion Behavior and Inhibition · Layered Double Hydroxides Synthesis and Applications · Concrete Corrosion and Durability
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (61)
Show source-provided references
1. A comparative study on corrosion inhibitive effect of nitrate and phosphate intercalated Zn-Al-layered double hydroxides (LDHs) nanocontainers incorporated into a hybrid silane layer and their effect on cathodic delamination of epoxy topcoat10.1016/j.corsci.2016.12.001 ↗
2. Constant-phase-element behavior caused by inhomogeneous water uptake in anti-corrosion coatings10.1016/j.electacta.2012.09.061 ↗
3. Synthesis of silane functionalized LDH-modified nanopowders to improve compatibility and enhance corrosion protection for epoxy coatings10.3390/molecules29040819 ↗
4. A review on self-healing coatings applied to Mg alloys and their electrochemical evaluation techniques10.20964/2020.04.36 ↗
5. Synergistic effect of imidazole dicarboxylic acid and Zn2+ simultaneously doped in halloysite nanotubes to improve protection of epoxy ester coating10.1016/j.porgcoat.2019.03.021 ↗
6. Synergy effect between layer double hydroxide (LDH) and EDDS for corrosion inhibition of carbon steel10.1016/j.clay.2022.106497 ↗
7. Layered double hydroxides intercalated with methyl orange as a controlled-release corrosion inhibitor for iron in chloride media10.1088/2632-959X/abe2b6 ↗
8. Comparison of different methods for measuring the passive film thickness on metals10.1016/j.electacta.2015.12.173 ↗
9. Amalysis of the non-ideal capacitive behaviour for high impedance organic coatings10.1016/j.porgcoat.2014.02.008 ↗
10. Effect of hysical barrier and anion-exchange process of nitrate-intercalated ZnAl layered double hydroxide films grown on Al n corrosion protection10.1016/j.surfcoat.2021.127436 ↗
11. Layered double hydroxide (LDH) for multi-functionalized corrosion protection of metals: a review10.1016/j.jmst.2021.05.078 ↗
12. A comparative study of chloride adsorption ability and corrosion protection effect in epoxy coatings of various layered double hydroxides10.3390/coatings12111631 ↗
13. Improved EIS analysis of the electrochemical behaviour of carbon steel I alkalne solution10.1016/j.electacta.2017.06.096 ↗
14. Identification of resistivity distributions in dielectric layers by measurement model analysis of impedance spectroscopy10.1016/j.electacta.2016.09.136 ↗
15. A waterborne epoxy composite coating with smart corrosion resistance based on 2-phenylbenzimidazole-5-sulfonic acid/layered double hydroxide composite10.3390/molecules28135199 ↗
16. Electrochemical impedance spectroscopy of epoxy-vinyl coating in aqueous medium analyzed by dipolar relaxation of polymer10.1149/1.1512667 ↗
17. Preparation of gallic acid intercalated layered double hydroxide for enhanced corrosion protection of epoxy coatings10.3390/coatings13010128 ↗
18. A dielectric study of water uptake in epoxy resin systems10.1002/app.44717 ↗
19. Corrosion protection mechanisms of carbon steel by an epoxy resin containing indole-3 butyric acid modified clay10.1016/j.porgcoat.2010.08.004 ↗
20. Layered double hydroxides as containers of inhibitors in organic coatings for corrosion protection of carbon steel10.1016/j.porgcoat.2011.10.020 ↗
21. Waterborne epoxy coating with excellent barrier and self-healing properties for long-term corrosion protection10.1016/j.ijoes.2024.100486 ↗
22. Amino acid motif intercalated in an inorganic layered phosphate container for improved steel protection: experimental and computational evaluation10.1016/j.colsurfa.2024.133266 ↗
23. Constant-phase-element behavior caused by resistivity distributions in films: I. Theory10.1149/1.3499564 ↗
24. Costant-phase-element behavior caused by resistivity distributions in films: II. Applications10.1149/1.3499565 ↗
25. Layered double hydroxides (LDHs) for coating applications
26. Anti-corrosion improvement of epoxy coating by the synergistic effect of barrier shielding and slow-release based on phytic acid intercalated hydrotalcite10.1002/app.54459 ↗
27. EIS characterization of thick flawed organic coatings aged under cathodic protection in seawater10.1016/j.electacta.2005.07.049 ↗
28. Zinc-layered hydroxide salt intercalated with molybdate anions as a new smart nanocontainer for active corrosion protection of carbon steel10.1021/acsami.0c02378 ↗
29. Combination of layered-based materials as an innovative strategy for improving active corrosion protection of carbon steel
30. Cataphoretic deposition of an epoxy coating with the incorporation of Ti3C2Tx@Mg-Al layered double hydroxide for long-term active corrosion protection effect
31. Another approach in analysis of paint coatings with EIS measurement: phase angle at high frequencies10.1016/j.corsci.2006.03.012 ↗
32. Potential of epoxy coating containing ionic liquid as anti-corrosion coating: evaluation of barrier properties10.1016/j.surfcoat.2024.130376 ↗
33. Construction of an epoxy coating with excellent protection performance on the AA 2024-T3 using ion-exchange materials loaded with eco-friendly corrosion inhibitors
34. Fabricating epoxy composite coating having self-healing/barrier anti-corrosion functions utilizing ion-exchange/pH-sensitive phosphate-doped ZIF8 MOF decorated Zn-Al-LDH nano-layers10.1016/j.surfcoat.2023.130284 ↗
35. Functional and smart coatings for corrosion protection: a review of recent advances10.1016/j.surfcoat.2014.06.031 ↗
36. Determination of resistivity profiles in anti-corrosion coatings from constant-phase element parameters10.1016/j.porgcoat.2013.12.013 ↗
37. Impedance analysis of the distributed resistivity of coatings in dry and wet conditions10.1016/j.electacta.2015.02.109 ↗
38. Impedance stufy of the influence of chromates on the properties of waterborne coatings deposited on 2024 aluminium alloy10.1016/j.corsci.2016.03.030 ↗
39. Determination of water uptake in organi coatings deposited on 2024 aluinium alloy: comparison between impedance measurements and gravimetry10.1016/j.porgcoat.2017.07.004 ↗
40. Corrosion inhibition of carbon steel by hydrotalcites modified with different organic carboxylic acids for organic coatings
41. Electrochemical impedance spectroscopy and dielectric properties of polymer: application to PEEK thermally sprayed coating10.1016/j.electacta.2004.01.057 ↗
42. Enhanced graphical representation of electrochemical impedance data10.1149/1.2168377 ↗
43. Performance evaluation of layered double hydroxides containing benzotriazole and nitrogen oxides as autonomic protection particules against corrosion10.1155/2021/6630194 ↗
44. Ni-Fe-MoO42− LDHs/epoxy resin varnish: a composite coating on carbon steel for long-time and active corrosion protection10.1016/j.porgcoat.2019.105514 ↗
45. Novel inorganic host layered double hydroxides intercalated with guest organic inhibitors for anticorrosion applications10.1021/am900495r ↗
46. Incorporation of layered double hydroxides modified with benzotriazole into an epoxy resin for the corrosion protection of Zn-Mg coated steel10.1016/j.porgcoat.2020.105894 ↗
47. The inhibitory and comparative effects of Zn-Al layered double hydroxide microcontainers intercalated with benzotriazole and nitrite for corrosion protection coatings on AISI 1010 carbon steel10.1590/s1517-707620200002.1064 ↗
48. Active anti-corrosion of epoxy coating by nitrite ions intercalated MgAl LDH10.1016/j.jhazmat.2020.122215 ↗
49. Controlled preparation of MgAl-layered double hydroxide/graphene hybrids and their applications for metal protection10.1021/acs.iecr.9b01742 ↗
50. Reviewing the current status of layered double hydroxide-based smart nanocontainers for corrosion inhibiting applications
51. Improving the corrosion protection ability of epoxy coating using CaAl LDH intercalated with 2-mercaptobenzothiazole as a pigment on steel substrate
52. Zn-Al layered double hydroxides as chloride nanotraps in active protective coatings10.1016/j.corsci.2011.10.003 ↗
53. Active anticorrosion and self-healing coatings: a review with focus on multi-action smart coating strategies10.1016/j.jmst.2021.11.042 ↗
54. Corrosion resistance of waterborne epoxy coatings by incorporation of dopamine treated mesoporous-TiO2 particles10.3390/coatings8060209 ↗
55. Anticorrosive waterborne epoxy (EP) coatings based on sodium tripolysphosphate-pillared layered double hydroxides (STPP-LDHs)10.1016/j.porgcoat.2019.04.055 ↗
56. Chloride adsorption on aminobenzoate intercalated layered double hydroxides: kinetic, thermodynamic and equilibrium studies10.1016/j.clay.2020.105495 ↗
57. Corrosion protection mechanism study of nitrite-modified CaAl-LDH in epoxy coatings10.3390/coatings13071166 ↗
58. An investigation on the corrosion behavior of the epoxy coating embedded with mesoporous silica nanocontainer loaded by sulfamethazine inhibitor10.1016/j.porgcoat.2018.12.022 ↗
59. Electrochemical impedance spectroscopy evaluation of corrosion protection of XC35 carbon steel by hyallosite nanotube-filled epoxy composite coatings in 3.5% NaCl solution10.20964/2019.05.09 ↗
60. Enhancing the corrosion resistance of waterborne epoxy coating by fumarate intercalated LDHs prepared by high gravity technology
61. Active protection coatings with layered double hydroxides nanocontainers of corrosion inhibitor10.1016/j.corsci.2009.10.020 ↗