Optimization of microstructure and mechanical performance of clay-rich sand-washing slurry-based geopolymers
Source abstract
Abstract
As a byproduct of sand-washing process, sand-washing slurry (SWS) showed a potential geopolymer precursor due to the abundant clay minerals. This study investigated the impact of calcination temperature of SWS and SiO 2/Na 2O ratio of alkaline solution on the microstructure and mechanical properties of SWS-based geopolymers. The analysis results indicated that at a calcination temperature of 550 °C, some clay minerals in SWS underwent a transition from crystalline to amorphous phases, resulting in increased amounts of amorphous Si and Al, thereby enhancing their alkaline reactivity. However, due to the low content of amorphous phases, the formed geopolymer structure was loose, leading to lower compressive strength. Compared to geopolymer treated at 550 °C, the geopolymer produced under temperatures ranging from 650 °C to 750 °C exhibited denser microstructures and higher compressive strength. The improvement in performance was attributed to more clay minerals undergoing dehydroxylation reactions, resulting in more amorphous Si and Al participating in the polymerization reaction. Nevertheless, upon reaching a calcination temperature of 850 °C, the microstructure of the formed geopolymers became loose with diminished compressive strength due to reduced activity of Si and Al in the amorphous phase. Furthermore, under a calcination temperature of 750 °C, the amorphous content in geopolymers with SiO 2/Na 2O ratios in the alkaline solution of 0.8 and 1.4 was 62.4 % and 64.5 %, respectively, while decreasing to 54.5 % in geopolymers with a ratio of 2. Geopolymers with a SiO 2/Na 2O ratio of 1.4 exhibited denser microstructures and higher compressive strength, indicating that alkaline solutions with this ratio promoted the formation of more amorphous materials and enhanced geopolymer strength. These findings suggested that calcination around 750 °C improved the microstructure and mechanical properties of SWS-based geopolymers, with the appropriate SiO 2/Na 2O ratio in alkaline solutions facilitating geopolymerization.
Source: expertdata · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Concrete and Cement Materials Research · Recycling and utilization of industrial and municipal waste in materials production · Innovations in Concrete and Construction Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (79)
Show source-provided references
1. Effect of cement addition, solution resting time and curing characteristics on fly ash based geopolymer concrete performance10.1016/j.conbuildmat.2016.07.043 ↗
2. Comparison of the microstructure and the compressive strength of two geopolymers derived from metakaolin and an industrial sludge10.1016/j.conbuildmat.2017.04.127 ↗
3. Effect of structural and textural properties of a ceramic industrial sludge and kaolin on the hardened geopolymer properties10.1016/j.clay.2018.05.029 ↗
4. Synthesis and characterization of mesoporous geopolymer based on Moroccan kaolinite rich clay10.1016/j.clay.2020.105764 ↗
5. Reactivity and leaching potential of municipal solid waste incineration (MSWI) bottom ash as supplementary cementitious material and precursor for alkali-activated materials10.1016/j.conbuildmat.2023.133890 ↗
6. Effect of Na2O content, SiO2/Na2O molar ratio, and curing conditions on the compressive strength of FA-based geopolymer10.1016/j.conbuildmat.2017.04.004 ↗
7. Davidovits · 2013 · 1
8. Valorization of non-beneficiated clays as supplementary cementitious materials in the production of cement-based mortar
9. Kaolin: soil, rock and ore from the mineral to the magmatic, sedimentary and metamorphic environments10.1016/j.earscirev.2016.07.003 ↗
10. Core-shell structured ceramsite made by excavated soil and expanded perlite through cold-bonded technology10.1016/j.conbuildmat.2021.124941 ↗
11. Geopolymer technology: the current state of the art10.1007/s10853-006-0637-z ↗
12. Fabrication of geopolymers from untreated kaolin clay for construction purposes10.1007/s10706-018-0597-5 ↗
13. The origin of the pozzolanic activity of calcined clay minerals: a comparison between kaolinite, illite and montmorillonite10.1016/j.cemconres.2010.09.013 ↗
14. Thermally treated clay sediments as geopolymer source material10.1016/j.clay.2015.01.027 ↗
15. Pozzolanic reactivity of a calcined interstratified illite/smectite (70/30) clay10.1016/j.cemconres.2015.08.006 ↗
16. Understanding the thermal activation behavior of montmorillonite and kaolinite at atomic level by ReaxFF molecular dynamics simulations10.1016/j.clay.2024.107313 ↗
17. Thermally and mechanically treated Greek palygorskite clay as a pozzolanic material10.1016/j.clay.2021.106306 ↗
18. Carbonation resistance of calcined clay-ground granulated blast furnace slag alkali-activated mortar10.1016/j.conbuildmat.2023.131811 ↗
19. Muscovite dehydroxylation—high-temperature studies
20. Pozzolanic reactivity of pure calcined clays10.1016/j.clay.2016.08.003 ↗
21. Correlation between initial SiO2/Al2O3, Na2O/Al2O3, Na2O/SiO2 and H2O/Na2O ratios on phase and microstructure of reaction products of metakaolin-rice husk ash geopolymer10.1016/j.conbuildmat.2019.07.146 ↗
22. Smectite clay waste as an additive for Portland cement10.1016/j.cemconcomp.2020.103710 ↗
23. Effect of quartz powder on mid-strength fly ash geopolymers at short curing time and low curing temperature10.1016/j.conbuildmat.2022.127153 ↗
24. Structural and chemical properties of thermally treated geopolymer samples10.1016/j.ceramint.2017.02.066 ↗
25. Effect of heat treatment on structure transformation and activities of kaolinite
26. Use of infrared spectroscopy to study geopolymerization of heterogeneous amorphous aluminosilicates10.1021/la026127e ↗
27. Influence of coal-measure kaolinite with different types on the preparation of kaolinite nanotube10.1016/j.clay.2023.107179 ↗
28. Structure and properties of clay-based geopolymer cements: a review10.1016/j.pmatsci.2016.08.002 ↗
29. Experimental study of the mechanical and thermal properties of metakaolin based geopolymer stabilized soil during low temperature curing10.1016/j.coldregions.2023.104085 ↗
30. Baseline studies of the clay minerals society source clays: infrared methods10.1346/CCMN.2001.0490508 ↗
31. Enhancing reactivity in muscovitic clays: mechanical activation as a sustainable alternative to thermal activation for cement production10.1016/j.clay.2024.107266 ↗
32. Alkali activation behaviour of un-calcined montmorillonite and illite clay minerals10.1016/j.clay.2018.09.011 ↗
33. Phase formation behaviour in alkali activation of clay mixtures10.1016/j.clay.2019.03.037 ↗
34. Evaluation of the optimal process of thermal activation of kaolins10.1016/j.scient.2011.07.011 ↗
35. Traditional and new applications for kaolin, smectite, and palygorskite: a general overview10.1016/S0169-1317(00)00016-8 ↗
36. Use of OPC to improve setting and early strength properties of low calcium fly ash geopolymer concrete cured at room temperature10.1016/j.cemconcomp.2014.08.008 ↗
37. Using calcium carbide residue as an alkaline activator for glass powder–clay geopolymer10.1016/j.conbuildmat.2018.06.190 ↗
38. Calcined clays as supplementary cementitious materials: a comparison between palygorskite and kaolinite10.1016/j.conbuildmat.2024.135180 ↗
39. Reaction mechanisms of calcined kaolin processing waste-based geopolymers in the presence of low alkali activator solution10.1016/j.conbuildmat.2019.06.116 ↗
40. Attenuated total reflectance Fourier transform infrared analysis of fly ash geopolymer gel aging10.1021/la700713g ↗
41. Dissolution processes, hydrolysis and condensation reactions during geopolymer synthesis: part II. High Si/Al ratio systems10.1007/s10853-006-0818-9 ↗
42. A novel raw material for geopolymers: coal-based synthetic natural gas slag10.1016/j.jclepro.2020.121238 ↗
43. Future of clay-based construction materials – a review10.1016/j.conbuildmat.2019.03.206 ↗
44. Durability assessment of mechanochemically activated geopolymer concrete with a low molarity alkali solution
45. Sicilian clay sediments as precursor for alkali activated materials10.1016/j.clay.2024.107350 ↗
46. A review on microwave irradiation to the properties of geopolymers: mechanisms and challenges10.1016/j.conbuildmat.2021.123491 ↗
47. High-efficiency utilization of waste shield slurry: a geopolymeric flocculation-filtration-solidification method10.1016/j.conbuildmat.2023.131569 ↗
48. Solidification/stabilization treatment of Hong Kong marine deposits slurry at high water content by ISSA and GGBS10.1016/j.conbuildmat.2023.130817 ↗
49. Loading and in vitro release of ibuprofen in tubular halloysite10.1016/j.clay.2014.01.018 ↗
50. Mechanical and microstructural properties of metakaolin-based geopolymer cements from sodium waterglass and phosphoric acid solution as hardeners: a comparative study10.1016/j.clay.2017.02.002 ↗
51. Geopolymerization reaction, microstructure and simulation of metakaolin-based geopolymers at extended Si/Al ratios10.1016/j.cemconcomp.2017.01.014 ↗
52. Reexamining calcination of kaolinite for the synthesis of metakaolin geopolymers-roles of dehydroxylation and recrystallization10.1016/j.jnoncrysol.2017.01.024 ↗
53. Stabilization/solidification of sand-washing slurry used for porous cold-bonded ceramsite10.1016/j.cemconcomp.2022.104771 ↗
54. Optimizing raw material composition and alkali content in low silicon-aluminum tailings-based geopolymers10.1016/j.conbuildmat.2023.133339 ↗
55. Thermal behaviors of clay minerals as key components and additives for fired brick properties: a review
56. Intrinsic sulfuric acid resistance of C-(N)-A-S-H and N-A-S-H gels produced by alkali-activation of synthetic calcium aluminosilicate precursors10.1016/j.cemconres.2022.107068 ↗
57. Dissolution processes, hydrolysis and condensation reactions during geopolymer synthesis: part I - low Si/Al ratio systems10.1007/s10853-006-0820-2 ↗
58. Solubility of precursors and carbonation of waterglass-free geopolymers10.1007/s42860-020-00096-4 ↗
59. Solubility of calcined kaolinite, montmorillonite, and illite in high molar NaOH and suitability as precursors for geopolymers10.1007/s42860-022-00185-6 ↗
60. Micromechanical properties of geopolymers with different calcined clay precursors10.1016/j.clay.2024.107259 ↗
61. Density functional modeling of the local structure of kaolinite subjected to thermal dehydroxylation10.1021/jp911108d ↗
62. Montmorillonite geopolymer porous membrane as electrolyte framework for compression resistance supercapacitor application10.1016/j.ceramint.2024.03.194 ↗
63. Optimization of mechanical performance of limestone calcined clay cement: effects of calcination temperature of nanosized tubular halloysite, gypsum content, and water/binder ratio10.1016/j.conbuildmat.2023.131709 ↗
64. Novel application of sustainable coal-derived char in cement soil stabilization10.1016/j.conbuildmat.2024.134960 ↗
65. Changes in structure, morphology, porosity, and surface activity of mesoporous halloysite nanotubes under heating10.1346/CCMN.2012.0600602 ↗
66. Sustainability of the polymer SH reinforced recycled granite residual soil: properties, physicochemical mechanism, and applications10.1007/s11368-022-03294-w ↗
67. Addition of alkaline solutions and fibers for the reinforcement of kaolinite-containing granite residual soil10.1016/j.clay.2022.106644 ↗
68. Optimized reinforcement of granite residual soil using a cement and alkaline solution: a coupling effect10.1016/j.jrmge.2024.01.009 ↗
69. Using fly ash to partially substitute metakaolin in geopolymer synthesis10.1016/j.clay.2013.12.025 ↗
70. Geopolymerization of halloysite via alkali-activation: dependence of microstructures on precalcination10.1016/j.clay.2019.105375 ↗
71. Effect of curing conditions on the microstructure and mechanical performance of geopolymers derived from nanosized tubular halloysite10.1016/j.conbuildmat.2020.121186 ↗
72. Influence of SiO2 /Na2O molar ratio on mechanical properties and durability of metakaolin-fly ash blend alkali-activated sustainable mortar incorporating manufactured sand10.1016/j.jmrt.2022.04.041 ↗
73. Mechanical behavior of intact completely decomposed granite soils along multi-stage loading–unloading path10.1016/j.enggeo.2019.105242 ↗
74. Experimental investigations of hydraulic and mechanical properties of granite residual soil improved with cement addition10.1016/j.conbuildmat.2021.126016 ↗
75. XRD-based quantitative analysis of clay minerals using reference intensity ratios, mineral intensity factors, Rietveld, and full pattern summation methods: a critical review
76. Influence of metakaolin and calcined montmorillonite on the hydration of calcium sulphoaluminate cement
77. Recycling and optimum utilization of engineering sediment waste into low-carbon geopolymer paste for sustainable infrastructure10.1016/j.jclepro.2022.135549 ↗
78. Adsorbents based on montmorillonite for contaminant removal from water: a review10.1016/j.clay.2015.12.024 ↗
79. Microwave treatment effect on the enhanced basicity of porous clay heterostructured composites derived from Laponite