A novel approach for preparing exfoliated UV-cured polymer/LDH nanocomposites via pre-exfoliated organic LDH
Source abstract
Abstract
Abstract A novel approach to prepare the exfoliated polymer/layered double hydroxide (LDH) nanocomposites was proposed by synthesizing a pre-exfoliated organic LDH (LDH-SH) firstly, then blended into an acrylic resin, and irradiated by a medium pressure mercury lamp. The LDH-SH was prepared by intercalating LDH with sodium dodecyl sulfate, and then γ-(2,3-epoxypropoxy) propyl trimethoxysilane, followed by grafting with trimethylolpropane thioglycolic acetate. From the X-ray diffraction (XRD) analysis, high resolution scanning electron microscope (HR-SEM) and high resolution transmission electron microscope (HR-TEM) observation, the LDH-SH lost its ordered stacking-structure and was totally pre-exfoliated. After UV irradiation, the formed polymer/LDH nanocomposite possessed the exfoliated microstructure from the transmission electron microscope (TEM) and HR-TEM observations. The dynamic mechanical thermal analyzer (DMTA) results showed that the storage modulus of nanocomposite with 5% LDH-SH loading increased to 44.2 MPa from 34.6 MPa of the pure polymer, while the tensile strength and persoz hardness were enhanced to 9.3 MPa and 107 s compared with 8.5 MPa and 87 s of the pure polymer, respectively.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Layered Double Hydroxides Synthesis and Applications · Synthesis and properties of polymers · Silicone and Siloxane Chemistry
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (30)
Show source-provided references
1. Mg–Al layered double hydroxide nanoparticles: evaluation of the thermal stability in polypropylene matrix10.1016/j.clay.2010.12.024 ↗
2. Mechanical and flame-retardant properties of epoxy/Mg–Al LDH composites10.1016/j.compositesa.2010.11.005 ↗
3. Synthesis of poly(butylene terephtahlate) nanocomposites using anionic clays10.1016/j.eurpolymj.2008.09.039 ↗
4. Preparation of clay/epoxy nanocomposites by layered-double-hydroxide initiated self-polymerization10.1016/j.polymer.2008.08.062 ↗
5. Synthesis and characterization of biodegradable poly(L-lactide)/layered double hydroxide nanocomposites10.1016/j.compscitech.2009.09.012 ↗
6. Alkyl sulfonate modified LDH: effect of alkyl chain length on intercalation behavior, particle morphology and thermal stability10.1016/j.clay.2008.12.020 ↗
7. The thermal degradation of poly(methyl methacrylate) nanocomposites with montmorillonite, layered double hydroxides and carbon nanotubes10.1002/pat.697 ↗
8. Recent progress in the synthesis and application of organically modified hydrotalcites10.1524/zkri.2009.1153 ↗
9. Molecular shape recognition-structure correlation in a phenylalanine-based polymer-silica composite by surface-initiated atom transfer radical polymerization10.1016/j.polymer.2008.10.017 ↗
10. Thermal properties of epoxy resin nanocomposites based on hydrotalcite10.1016/j.polymdegradstab.2010.10.006 ↗
11. Preparation and properties of LDHs/epoxy nanocomposites10.1016/S0032-3861(03)00579-2 ↗
12. Preparation and characterization of Mg–Al layered double hydroxides intercalated with benzenesulfonate and benzenedisulfonate10.1016/j.micromeso.2008.01.029 ↗
13. Preparation of layered double hydroxides intercalated with organic anions and their application in LDH/poly(butyl methacrylate) nanocomposites10.1016/j.clay.2009.11.012 ↗
14. Layered double hydroxide nanoparticles in gene and drug delivery10.1517/17425240903130585 ↗
15. Composite hydrogels: robust carriers for catalytic nanoparticles10.1002/macp.200600534 ↗
16. Strengthening and toughening effects of layered double hydroxide and hyperbranched polymer on epoxy resin10.1016/j.porgcoat.2009.03.006 ↗
17. Preparation and properties of polymer/LDH nanocomposite used for UV curing coatings10.1016/j.porgcoat.2009.04.001 ↗
18. A brief history of the Athens conference on organic coatings, science and technology10.1016/S0300-9440(00)00118-1 ↗
19. Nanometric dispersion of a Mg/Al layered double hydroxide into a chemically modified polycaprolactone10.1021/bm0605964 ↗
20. Aluminum-containing layered double hydroxides: the thermal, mechanical, and fire properties of (nano)composites of poly(methyl methacrylate)10.1039/b802553c ↗
21. Multiarm organic compounds for use as reversible chain-transfer agents in living radical polymerizations10.1016/S0040-4039(02)01497-1 ↗
22. Fabrication and characterization of new semiconducting nanomaterials composed of natural layered silicates (Na+-MMT), natural rubber (NR), and polypyrrole (PPy)10.1016/j.polymer.2009.07.003 ↗
23. Morphology and thermal stabilization mechanism of LLDPE/MMT and LLDPE/LDH nanocomposites10.1016/j.polymer.2005.12.017 ↗
24. Effect of surfactant concentration on the stacking modes of organo-silylated layered double hydroxides10.1016/j.clay.2009.06.007 ↗
25. Synthesis of organo cobalt–aluminum layered double hydroxide via a novel single-step self-assembling method and its use as flame retardant nanofiller in PP10.1021/la102449m ↗
26. Preparation and properties of exfoliated nanocomposites through intercalated a photoinitiator into LDH interlayer used for UV curing coatings10.1016/j.porgcoat.2010.05.007 ↗
27. Preparation and properties of UV-cured acrylated silane intercalated polymer/LDH nanocomposite10.1016/j.materresbull.2010.09.029 ↗
28. Zahouily · Proc. RadTech Europe · 2001 · 583
29. Zahouily · Proc. RadTech. North Am. · 2002 · 309
30. Preparation and flame resistance properties of revolutionary self-extinguishing epoxy nanocomposites based on layered double hydroxides10.1016/j.polymer.2005.07.050 ↗