Biomass derived palygorskite–carbon nanocomposites: Synthesis, characterisation and affinity to dye compounds

Abstract Clay minerals can act as a uniform dispersion medium for nano-sized carbon particles. However, literature on the preparation and characteristics of palygorskite–carbon nanocomposites is scant. Using a hydrothermal carbonisation technique this study developed two nanocomposites on fibrous palygorskite from starch: the first without a post-synthesis treatment (Composite 1); and the second with an activation at 550 °C for 3 h (ramp at 10 °C min − 1 ) under CO 2 environment (200 mL min − 1 ) (Composite 2). A uniform dispersion of nano-scale carbon spheres was formed on partially destroyed palygorskite structures. Composite 2, which indicated the formation of graphitised carbon nanoparticles, generated a 17-fold greater specific surface area than Composite 1 and also created micro- and mesopores in its structure. The nanocomposites, especially in Composite 1, contained organic surface functional groups (C H, C C, C O) and indicated variable affinity to cationic and anionic dye compounds. While Composite 2 adsorbed a larger amount of anionic orange II dye (23 mg g − 1 ), Composite 1 adsorbed more cationic methylene blue (46.3 mg g − 1 ). Isothermal and kinetic modelling of the adsorption data indicated that in addition to electrostatic attraction for methylene blue adsorption on both nanocomposites, a pore diffusion mechanism was involved and the boundary resistance was greater for orange II than methylene blue adsorption. Being a material developed from green biomass (starch) and an abundant natural resource (palygorskite), these nanocomposites have immense potential for application in environmental remediation including in situ immobilisation of contaminants in soil.