Effect of ultrasound on preparation of porous materials from vermiculite

Abstract High- and low-charge vermiculites from Spain (Santa Olalla and Ojen) were sonicated in an ultrasonic liquid processor to produce changes in particle size, morphology and structural ordering. The ultimate aim of this treatment was to prepare 18 A Al-pillared vermiculites. Sonication caused a rise of the S BET from the initial value 1 m 2 g − 1 of the raw samples to 36 and 54 m 2 g − 1 for the Santa Olalla and Ojen samples, respectively. The XRD study shows that the crystal structure of both minerals remains practically unchanged by sonication. However, the 00l diffraction broadens due to a significant delamination process, yielding values of particle thickness of 185 and 260 A for the low- and high-charged vermiculites, respectively. The sonicated Santa Olalla sample (high-charge) treated with Al 13 solution shows a d 00l powder diffraction peak at 14 A, whereas the sonicated Ojen sample (low-charge) shows peaks at 14 and 18 A. The 18 A diffraction peak is preserved at high temperatures (550 °C) and it is responsible of an increase of surface area and microporosity. The ultrasound treatment of low-charge vermiculite from Ojen is a new method for obtaining 18 A Al-pillared vermiculites. The ultrasound treatment using H 2 O 2 in the medium produces a significant delamination and a decrease of the particle size and the layer charge leading to the Al–polymer intercalation.