Thermal, optical and dielectric properties of Zn–Al layered double hydroxide

Abstract Zn–Al–NO 3 –layered double hydroxide (Zn–Al–NO 3 –LDH) was prepared by the co-precipitation method at a constant pH of 7 and a ratio of Zn/Al = 4. A thermal treatment was performed for LDH at various temperatures. Powder XRD patterns showed that the layered structure of the LDH samples was stable below 200 °C, which was also confirmed by thermogravimetric (TGA) and differential thermal (DTA) analyses. Infrared spectra of the samples showed the characteristic peaks of LDH, and changes of these peaks were observed when thermal treatment was performed above 150 °C. Diffuse reflectance spectroscopy of the samples showed more than one energy gap at calcination temperatures below200 °C. In samples calcined at 200 °C and above only one energy gap was observed at approximately 3.3 eV. The photocatalytic activity was found to increase with the increase of the ZnO crystal size, which can be achieved by increasing the calcination temperature of the samples. Because of the presence of water molecules and anionic NO 3 − in the interlayer of the LDH, the dielectric response of the calcined LDH can be described by an anomalous low frequency dispersion using the second type of Universal Power Law for calcination temperatures below 200 °C. The dielectric response of the calcined LDH above 150 °C displays the dielectric relaxation behaviour of ZnO because of the formation of a ZnO phase in the LDH within this temperature range.