Silane functionalization of sodium montmorillonite nanoclay and its effect on rheological and mechanical properties of HDPE/clay nanocomposites

Abstract The present research reveals novel results about the silane functionalization of sodium montmorillonite (Na-Mt) by comparing the interlayer space and thermal stability of the nanofiller at different initial silane concentrations. XRD and TGA results indicate an increased d 001 and a high thermal stability for the silane-modified Na-Mt, which makes it a promising nanofiller for polymer nanocomposites. The amounts of intercalation and chemical grafting are estimated from TGA results using equations developed in this work; the silane intercalation is found to be the highest (0.504 mmol/g clay) for 9 mmol/g clay initial silane concentration, which is consistent with the d 001 -value (22.6 A). Intercalation increases with increase in initial silane concentration up to 9 mmol (intercalated amount ≈ 0.504 mmol/g clay), then decreases at higher concentrations, e.g., 15 mmol silane have an intercalated amount of 0.405 mmol/g clay. However, the chemical grafting value for 15 mmol silane is greater (0.18 mmol/g clay) relative to that of the 9 mmol silane initial concentration (0.15 mmol/g clay). This can be explained by the occurrence of the side reactions at the edges for 15 mmol silane, which reduces the intercalation amount. The rheological and tensile properties of HDPE/silane functionalized clay suggest that the storage modulus, damping factor and mechanical behavior of the composites depend on the clay nanofiller, as well as the nanocomposite preparation procedure (i.e. masterbatch technique). The tensile modulus showed ~ 15% enhancement for 85%HDPE/15%PEMA/2% modified clay over the pure polymer. TEM images revealed a well-dispersed clay structure for the HDPE/2 wt% modified-clay/PEMA nanocomposite that is prepared through the masterbatch technique.