Factors influencing the hydration of layered double hydroxides (LDHs) and the appearance of an intermediate second staging phase

Abstract The hydration of layered double hydroxides (LDHs) was investigated by changing the interlayer anion species, the Mg/Al ratio of the LDH hosts and the relative humidity (RH). The anions were CO 3 2− , Cl − , Br − , NO 3 − , I − , SO 4 2− , and ClO 4 − (listed in the order of ion size, small to large) and LDHs with Mg/Al = 1.90 (LDH2) and 2.91 (LDH3) were used. Their XRD profiles were measured by an XRD diffractometer while controlling the RH in the range 0–95% at 25 °C. Only I − , SO 4 2− , and ClO 4 − LDH2s and SO 4 2− LDH3 showed a large step-wise basal-spacing expansion, 0.24–0.28 nm, under high RH conditions (> ca. 60%) probably due to the insertion of one water layer into the interlayer space. Such hydration occurred more favorably for the LDHs with larger anions and those with a higher layer charge (LDH2). Among them, I − and ClO 4 − LDH2s exhibited the second staging – alternate stacking of hydrated (H) and non-hydrated (NH) interlayers – in the intermediate RH region.