Effects of a refractory metal protective barrier on uranium carbonitride ceramic–metallic composites exposed to a high temperature hydrogen environment

Uranium nitride has been under consideration at NASA and the Department of Energy for nuclear thermal propulsion applications intended for deep space exploration vehicles. It is critical to the success of the technology development that the behavior of the fuel system is properly characterized in operational environments. This body of work fabricated ceramic metal composites consisting of uranium ceramic fuel in a molybdenum and molybdenum–tungsten metal matrix, both with and without an exterior molybdenum barrier. Specimens were introduced to a high temperature hydrogen environment and characterized through x-ray diffraction, scanning electron microscopy, and energy dispersive spectroscopy to identify characteristic changes. A portion of the specimens was fabricated with a 1.27 mm thick molybdenum barrier in order to isolate the material from the hydrogen environment. Instability of the uranium nitride occurred as low as 2073 K, leading to aggressive instability approaching 2658 K. Carbon reactions with the metal matrix were observed as well as alloying between the uranium and metal matrix constituents. The liquid uranium resulting from the instability of the uranium nitride was observed to attack the grain boundaries of the refractory metal, resulting in the formation of a liquid uranium molybdenum eutectic melt. Specimens encased in a barrier experienced similar results. The authors conclude this is a significant challenge to applications of this cermet at these temperatures. Alternate configurations with resilient hermetic seals or lower temperature applications such as power reactors may have more success.