Structural and optical characterization of dilute Bi-doped GaN nanostructures grown by molecular beam epitaxy
Source abstract
Abstract
We have carried out detailed studies on the epitaxy and characterization of dilute Bi-doped GaN nanostructures. A comprehensive investigation of Bi-doped GaN nanowires and quasi-film epitaxial growth conditions has been performed. Scanning electron microscopy studies show that lowering the GaBiN growth temperature causes gradual changes in top c-plane nanowire morphology due to the incremental incorporation of foreign Bi atoms. This trend is further substantiated by the secondary ion mass spectroscopy analysis of a multi-layer Bi-doped GaN quasi-film. However, it is also found that the amount of Bi incorporation into the GaN lattice is relatively independent of the N2 flow rate variation under the growth conditions investigated. Furthermore, room-temperature micro-Raman spectra show that there are additional peaks near 530, 650, and 729 cm−1 wave numbers in the Bi-doped GaN samples, which can primarily be attributed to Bi local vibrational modes, indicative of a small amount of Bi incorporation in the GaN lattice. Moreover, phonon calculations with density functional theory indicate that Bi replacing the N sites is the likely origin of the experimentally measured Raman modes. X-ray photoelectron spectroscopy measurements have also been obtained to deduce the electronic interaction between the Bi dopant atom and the GaN nanostructure. Such one-dimensional nanowires permit the synthesis of dislocation-free highly mismatched alloys due to strain relaxation, allowing efficient light absorption and charge carrier extraction that is relevant for solar energy harvesting and artificial photosynthesis.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: GaN-based semiconductor devices and materials · Ga2O3 and related materials · ZnO doping and properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Electrical Engineering and Computer Science, University of Michigan 1 , 1301 Beal Avenue, Ann Arbor, Michigan 48109, USA
Department of Materials Science and Engineering, University of Michigan 2 , 2300 Hayward St., Ann Arbor, Michigan 48109, USA
Funding
Army Research Office · U.S. Department of Energy
References (48)
Show source-provided references
1. Phys. Rev. Lett. · 1999 · 82 · 122110.1103/physrevlett.82.1221 ↗
2. Phys. Rev. Lett. · 2000 · 85 · 155210.1103/physrevlett.85.1552 ↗
3. J. Mater. Chem. A · 2023 · 11 · 542710.1039/D2TA09967E ↗
4. J. Mater. Chem. A · 2016 · 4 · 280110.1039/C5TA07364B ↗
5. J. Cryst. Growth · 2002 · 234 · 34310.1016/s0022-0248(01)01716-x ↗
6. Phys. Status Solidi A · 2002 · 192 · 44110.1002/1521-396X(200208)192:2<441::AID-PSSA441>3.0.CO;2-U ↗
7. Jpn. J. Appl. Phys. · 1996 · 35 · L163410.1143/jjap.35.l1634 ↗
8. Semicond. Sci. Technol. · 2001 · 16 · 10310.1088/0268-1242/16/2/308 ↗
9. J. Cryst. Growth · 2003 · 247 · 3510.1016/s0022-0248(02)01914-0 ↗
10. J. Vac. Sci. Technol. B · 2001 · 19 · 142610.1116/1.1374627 ↗
11. Appl. Phys. Lett. · 2000 · 76 · 100910.1063/1.125922 ↗
12. Appl. Phys. Lett. · 2001 · 79 · 305910.1063/1.1415774 ↗
13. Appl. Phys. Lett. · 2007 · 91 · 05190910.1063/1.2768312 ↗
14. Appl. Phys. Lett. · 2006 · 88 · 20111210.1063/1.2205180 ↗
15. Phys. Rev. Lett. · 2006 · 97 · 06720510.1103/PhysRevLett.97.067205 ↗
16. Appl. Phys. Lett. · 2003 · 82 · 224510.1063/1.1565499 ↗
17. Appl. Phys. Lett. · 1999 · 74 · 125410.1063/1.123516 ↗
18. Phys. Rev. B · 2004 · 70 · 11521410.1103/PhysRevB.70.115214 ↗
19. Phys. Rev. B · 2005 · 71 · 15520110.1103/PhysRevB.71.155201 ↗
20. J. Cryst. Growth · 2011 · 323 · 6010.1016/j.jcrysgro.2010.11.064 ↗
21. Phys. Rev. B · 2002 · 65 · 11520310.1103/physrevb.65.115203 ↗
22. Phys. Status Solidi A · 2012 · 209 · 41910.1002/pssa.201100312 ↗
23. J. Cryst. Growth · 2003 · 251 · 44910.1016/s0022-0248(02)02217-0 ↗
24. J. Chem. Phys. · 1956 · 24 · 43910.1063/1.1742493 ↗
25. Semiconductors · 2015 · 49 · 27910.1134/s1063782615030021 ↗
26. Solid State Commun. · 2012 · 152 · 170010.1016/j.ssc.2012.04.071 ↗
27. Phys. Rev. B · 2003 · 68 · 19520510.1103/PhysRevB.68.195205 ↗
28. J. Mater. Res. · 2011 · 26 · 288710.1557/jmr.2011.376 ↗
29. Phys. Status Solidi C · 2012 · 9 · 158610.1002/pssc.201100582 ↗
30. J. Alloys Compd. · 2012 · 530 · 3610.1016/j.jallcom.2012.03.088 ↗
31. J. Semicond. · 2014 · 35 · 12200210.1088/1674-4926/35/12/122002 ↗
32. Nano Lett. · 2011 · 11 · 235310.1021/nl2006802 ↗
33. Proc. Natl. Acad. Sci. U. S. A. · 2020 · 117 · 133010.1073/pnas.1911159117 ↗
34. J. Mater. Chem. A · 2022 · 10 · 786910.1039/d2ta00032f ↗
35. Appl. Phys. Lett. · 2010 · 97 · 14191910.1063/1.3499753 ↗
36. J. Electron. Mater. · 2013 · 42 · 2610.1007/s11664-012-2323-z ↗
37. Phys. Status Solidi A · 2005 · 202 · 85010.1002/pssa.200461411 ↗
38. Appl. Phys. Lett. · 2004 · 84 · 89710.1063/1.1645668 ↗
39. J. Phys.: Condens. Matter · 2002 · 14 · R96710.1088/0953-8984/14/38/201 ↗
40. Appl. Phys. Lett. · 2021 · 118 · 01210110.1063/5.0029761 ↗
41. Appl. Phys. Lett. · 2019 · 126 · 08570410.1063/1.5109735 ↗
42. J. Appl. Phys. · 2003 · 94 · 438910.1063/1.1606521 ↗
43. Appl. Phys. Lett. · 2017 · 111 · 06110110.1063/1.4997450 ↗
44. Nanoscale · 2014 · 6 · 997010.1039/c4nr01608d ↗
45. J. Appl. Phys. · 2015 · 118 · 15530110.1063/1.4933276 ↗
46. Cryst. Growth Des. · 2017 · 17 · 341110.1021/acs.cgd.7b00365 ↗
47. Appl. Phys. Lett. · 1997 · 70 · 215610.1063/1.118944 ↗
48. Appl. Phys. Lett. · 2013 · 102 · 20160410.1063/1.4807736 ↗