Phase-selective growth of κ- vs β-Ga2O3 and (InxGa1−x)2O3 by In-mediated metal exchange catalysis in plasma-assisted molecular beam epitaxy

A. Ardenghi, O. Bierwagen, J. Lähnemann, E. Luna, J. Kler, A. Falkenstein, M. Martin, A. Sacchi, P. Mazzolini

APL Materials· Volume 12· Issue 10

Abstract

Its large intrinsic polarization makes the metastable κ-Ga2O3 polymorph appealing for multiple applications, and the In-incorporation into both κ and β-Ga2O3 allows us to engineer their bandgap on the low-end side. In this work, we provide practical guidelines to grow thin films of single phase κ-, β-Ga2O3 as well as their (InxGa1−x)2O3 alloys up to x = 0.14 and x = 0.17, respectively, using In-mediated metal exchange catalysis in plasma-assisted molecular beam epitaxy (MEXCAT-MBE). The role of substrate temperature, oxidizing power, growth rate, and choice of substrate on phase formation and In-incorporation is investigated. As a result, the κ phase can be stabilized in a narrow deposition window irrespective of the choice of substrate [(i) α-Al2O3 (0001), (ii) 20 nm of (2̄01) β-Ga2O3 on α-Al2O3 (0001), and (iii) (2̄01) β-Ga2O3 single crystal]. Low growth rates/metal fluxes as well as growth temperatures above 700 °C tend to stabilize the β-phase independently. Lower growth temperatures and/or O-richer deposition atmospheres allow to increase the In-incorporation in both polymorphs. Finally, we also demonstrate the possibility to grow (2̄01) β-Ga2O3 on top of α-Al2O3 (0001) at temperatures at least 100 °C above those achievable with conventional non-catalyzed MBE, opening the road for better crystal quality in heteroepitaxy.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Ga2O3 and related materials · Advanced Photocatalysis Techniques · ZnO doping and properties

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Paul-Drude-Institut für Festkörperelektronik, Leibniz-Institut im Forschungsverbund Berlin e.V. 1 , Hausvogteiplatz 5-7, 10117 Berlin,

Institute of Physical Chemistry, RWTH Aachen University 2 , D-52056 Aachen,

Department of Mathematical, Physical and Computer Sciences, University of Parma 3 , Parco Area delle Scienze 7/A, 43124 Parma,

Funding

Deutsche Forschungsgemeinschaft · COST Action: CA20116

References (50)

Show source-provided references
1. APL Mater. · 2022 · 10 · 02920110.1063/5.0060327 ↗
2. ECS J. Solid State Sci. Technol. · 2017 · 6 · Q300710.1149/2.0021702jss ↗
3. Jpn. J. Appl. Phys. · 2016 · 55 · 1202A210.7567/jjap.55.1202a2 ↗
4. J. Cryst. Growth · 2021 · 556 · 12599010.1016/j.jcrysgro.2020.125990 ↗
5. J. Cryst. Growth · 2004 · 270 · 42010.1016/j.jcrysgro.2004.06.027 ↗
6. Appl. Phys. Lett. · 2020 · 117 · 22210210.1063/5.0027870 ↗
7. Appl. Phys. Express · 2017 · 10 · 04110210.7567/apex.10.041102 ↗
8. Appl. Phys. Lett. · 2022 · 121 · 04210910.1063/5.0087987 ↗
9. Appl. Phys. Lett. · 2022 · 121 · 07210810.1063/5.0101132 ↗
10. APL Mater. · 2023 · 11 · 04110210.1063/5.0139622 ↗
11. J. Appl. Phys. · 2023 · 133 · 03570210.1063/5.0131285 ↗
12. ACS Appl. Mater. Interfaces · 2021 · 13 · 280710.1021/acsami.0c16021 ↗
13. Inorg. Chem. · 2016 · 55 · 01207910.1021/acs.inorgchem.6b02244 ↗
14. Appl. Phys. Express · 2016 · 9 · 04110210.7567/APEX.9.041102 ↗
15. Appl. Phys. Express · 2020 · 13 · 06100910.35848/1882-0786/ab9168 ↗
16. Appl. Phys. Lett. · 2018 · 112 · 16210110.1063/1.5019721 ↗
17. J. Alloys Compd. · 2023 · 936 · 16831510.1016/j.jallcom.2022.168315 ↗
18. ACS Appl. Electron. Mater. · 2021 · 3 · 79510.1021/acsaelm.0c00947 ↗
19. Mater. Today Phys. · 2023 · 31 · 10100210.1016/j.mtphys.2023.101002 ↗
20. ECS J. Solid State Sci. Technol. · 2020 · 9 · 04501410.1149/2162-8777/ab8b4c ↗
21. Adv. Funct. Mater. · 2023 · 33 · 220782110.1002/adfm.202207821 ↗
22. J. Appl. Phys. · 2015 · 118 · 08530110.1063/1.4929417 ↗
23. ACS Omega · 2020 · 5 · 02958510.1021/acsomega.0c04634 ↗
24. J. Mater. Chem. C · 2020 · 8 · 01097510.1039/d0tc02743j ↗
25. APL Mater. · 2019 · 7 · 07990110.1063/1.5099518 ↗
26. Jpn. J. Appl. Phys. · 2016 · 55 · 1202BC10.7567/jjap.55.1202bc ↗
27. Phys. Rev. Lett. · 2017 · 119 · 19600110.1103/physrevlett.119.196001 ↗
28. Phys. Rev. Appl. · 2017 · 8 · 05400210.1103/physrevapplied.8.054002 ↗
29. J. Cryst. Growth · 2016 · 443 · 2510.1016/j.jcrysgro.2016.03.013 ↗
30. APL Mater. · 2020 · 8 · 01110710.1063/1.5135772 ↗
31. Appl. Phys. Lett. · 2020 · 117 · 22210510.1063/5.0031300 ↗
32. APL Mater. · 2020 · 8 · 02110410.1063/1.5135930 ↗
33. J. Appl. Phys. · 2022 · 132 · 19530410.1063/5.0127232 ↗
34. J. Phys. D: Appl. Phys. · 2020 · 53 · 48510510.1088/1361-6463/abaf7d ↗
35. Jpn. J. Appl. Phys. · 2023 · 62 · SF101310.35848/1347-4065/acbe04 ↗
36. APL Mater. · 2019 · 7 · 02251110.1063/1.5054386 ↗
37. Acta Mater. · 2017 · 140 · 41110.1016/j.actamat.2017.08.062 ↗
38. J. Appl. Crystallogr. · 2011 · 44 · 127210.1107/s0021889811038970 ↗
39. Phys. Status Solidi B · 2023 · 260 · 220053510.1002/pssb.202200535 ↗
40. Adv. Mater. · 2022 · 34 · 220421710.1002/adma.202204217 ↗
41. CrystEngComm · 2017 · 19 · 150910.1039/c7ce00123a ↗
42. CrystEngComm · 2018 · 20 · 188210.1039/c7ce02103h ↗
43. APL Mater. · 2019 · 7 · 02252510.1063/1.5054394 ↗
44. APL Mater. · 2023 · 11 · 09111410.1063/5.0167736 ↗
45. ACS Appl. Mater. Interfaces · 2024 · 16 · 1279310.1021/acsami.3c19095 ↗
46. Cryst. Growth Des. · 2021 · 21 · 639310.1021/acs.cgd.1c00863 ↗
47. Phys. Status Solidi A · 2013 · 210 · 173810.1002/pssa.201329040 ↗
48. Phys. Rev. Mater. · 2020 · 4 · 10460210.1103/physrevmaterials.4.104602 ↗
49. Phys. Status Solidi A · 2018 · 215 · 170046710.1002/pssa.201700467 ↗
50. CrystEngComm · 2022 · 24 · 323910.1039/d2ce00042c ↗