Effects of surface finish and mechanical training on Ni-Ti sheets for elastocaloric cooling

Kurt Engelbrecht, Jaka Tušek, Simone Sanna, Dan Eriksen, Oleg V. Mishin, Christian R. H. Bahl, Nini Pryds

APL Materials· Volume 4· Issue 6

Abstract

Elastocaloric cooling has emerged as a promising alternative to vapor compression in recent years. Although the technology has the potential to be more efficient than current technologies, there are many technical challenges that must be overcome to realize devices with high performance and acceptable durability. We study the effects of surface finish and training techniques on dog bone shaped polycrystalline samples of NiTi. The fatigue life of several samples with four different surface finishes was measured and it was shown that a smooth surface, especially at the edges, greatly improved fatigue life. The effects of training both on the structure of the materials and the thermal response to an applied strain was studied. The load profile for the first few cycles was shown to change the thermal response to strain, the structure of the material at failure while the final structure of the material was weakly influenced by the surface finish.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Shape Memory Alloy Transformations · High Entropy Alloys Studies · Adhesion, Friction, and Surface Interactions

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Technical University of Denmark 1 Department of Energy Conversion and Storage, , DK-4000 Roskilde, Denmark

University of Ljubljana 2 Faculty of Mechanical Engineering, , Aškerčeva 6, 1000 Ljubljana, Slovenia

Technical University of Denmark 3 Department of Wind Energy, , DK-4000 Roskilde, Denmark

Funding

Slovenian Research Agency

References (32)

Show source-provided references
1. Adv. Energy Mater. · 2012 · 14 · 1010.1002/adem.201100178 ↗
2. Nat. Mater. · 2014 · 13 · 43910.1038/nmat3951 ↗
3. Int. J. Refrig. · 2015 · 57 · 28810.1016/j.ijrefrig.2015.06.008 ↗
4. Int. J. Refrig. · 2016 · 62 · 17710.1016/j.ijrefrig.2015.10.019 ↗
5. Adv. Energy Mater. · 2015 · 5 · 150036110.1002/aenm.201500361 ↗
7. Int. J. Refrig. · 2015 · 54 · 8810.1016/j.ijrefrig.2015.03.001 ↗
8. Appl. Phys. Lett. · 2015 · 106 · 20190310.1063/1.4921531 ↗
9. Scr. Mater. · 2016 · 114 · 110.1016/j.scriptamat.2015.11.021 ↗
10. Appl. Phys. Lett. · 2015 · 107 · 08190510.1063/1.4929395 ↗
11. Appl. Phys. Lett. · 2012 · 101 · 07390410.1063/1.4746257 ↗
12. Acta Mater. · 2014 · 81 · 910.1016/j.actamat.2014.08.006 ↗
13. J. Appl. Phys. · 2015 · 117 · 12490110.1063/1.4913878 ↗
14. Shape Mem. Superelasticity · 2015 · 1 · 13210.1007/s40830-015-0021-4 ↗
15. Appl. Phys. Lett. · 2013 · 103 · 21190410.1063/1.4832339 ↗
16. Acta Mater. · 2015 · 87 · 810.1016/j.actamat.2015.01.004 ↗
17. Science · 2015 · 348 · 100410.1126/science.1261164 ↗
18. Exp. Mech. · 2006 · 46 · 53110.1007/s11340-006-8351-y ↗
19. Continuum Mech. Thermodyn. · 2006 · 18 · 8310.1007/s00161-006-0022-9 ↗
20. Acta Mater. · 1997 · 45 · 68310.1016/S1359-6454(96)00189-9 ↗
21. Shape Mem. Superelasticity · 2015 · 1 · 14210.1007/s40830-015-0014-3 ↗
22. J. Mod. Opt. · 2010 · 57 · 170010.1080/09500341003725748 ↗
23. Z. Metallkd. · 2002 · 93 · 310.3139/146.020003 ↗
24. Metall. Trans. A · 1986 · 17 · 11510.1007/BF02644447 ↗
25. Mech. Mater. · 1998 · 30 · 14110.1016/S0167-6636(98)00041-6 ↗
26. Mater. Sci. Eng.: A · 2008 · 481-482 · 14210.1016/j.msea.2007.01.182 ↗
27. J. Mech. Phys. Solids · 2005 · 53 · 171910.1016/j.jmps.2005.03.005 ↗
28. Int. J. Plast. · 1998 · 13 · 83710.1016/S0749-6419(97)00062-4 ↗
29. Int. J. Plast. · 2000 · 16 · 54110.1016/S0749-6419(99)00075-3 ↗
30. Acta Mater. · 2015 · 94 · 25710.1016/j.actamat.2015.04.039 ↗
31. Mater. Sci. Eng.: A · 1991 · 145 · 15110.1016/0921-5093(91)90244-H ↗
32. Scr. Metall. · 1975 · 9 · 127710.1016/0036-9748(75)90424-X ↗