Conductivity and power factor enhancement of n-type semiconducting polymers using sodium silica gel dopant

This work demonstrates the use of sodium silica gel (Na-SG) particles as a reducing agent for n-type conjugated polymers to improve the conductivity and thermoelectric properties. Substantial increase in the electrical conductivity (σ, from 10−7 to 10−3 S/cm in air) was observed in two naphthalenetetracarboxylic diimide solution-processable n-type polymers, one of which was designed and synthesized in our lab. Systematic investigations of electrical conductivity were done by varying the weight percentage of Na-SG in the polymers. Additional evidence for the reduction process was obtained from electron spin resonance spectroscopy and control experiments involving nonreducing silica particles and non-electron-accepting polystyrene. The Seebeck coefficient S of the highest conductivity sample was measured and found to be in agreement with an empirical model. All the electrical conductivity and Seebeck coefficients measurements were performed in ambient atmosphere.