The role of boron related defects in limiting charge carrier lifetime in 4H–SiC epitaxial layers
Source abstract
Abstract
One of the main challenges in realizing 4H–SiC (silicon carbide)-based bipolar devices is the improvement of minority carrier lifetime in as-grown epitaxial layers. Although Z1/2 has been identified as the dominant carrier lifetime limiting defect, we report on B-related centers being another dominant source of recombination and acting as lifetime limiting defects in 4H–SiC epitaxial layers. Combining time-resolved photoluminescence (TRPL) measurement in near band edge emission and 530 nm, deep level transient spectroscopy, and minority carrier transient spectroscopy (MCTS), it was found that B related deep levels in the lower half of the bandgap are responsible for killing the minority carriers in n-type, 4H–SiC epitaxial layers when the concentration of Z1/2 is already low. The impact of these centers on the charge carrier dynamics is investigated by correlating the MCTS results with temperature-dependent TRPL decay measurements. It is shown that the influence of shallow B acceptors on the minority carrier lifetime becomes neutralized at temperatures above ∼422 K. Instead, the deep B related acceptor level, known as the D-center, remains active until temperatures above ∼570 K. Moreover, a correlation between the deep level concentrations, minority carrier lifetimes, and growth parameters indicates that intentional nitrogen doping hinders the formation of deep B acceptor levels. Furthermore, tuning growth parameters, including growth temperature and C/Si ratio, is shown to be crucial for improving the minority carrier lifetime in as-grown 4H–SiC epitaxial layers.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Silicon Carbide Semiconductor Technologies · Semiconductor materials and devices
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Department of Physics, Chemistry, and Biology (IFM), Linköping University 1 , SE-581 83 Linköping, Sweden
Advanced Power Semiconductor Laboratory, ETH Zürich 2 , 8092 Zürich, Switzerland
Department of Physics, University of Oslo 3 , 0316 Oslo, Norway
Science Institute, University of Iceland 4 , IS-107 Reykjavík, Iceland
Funding
Swedish Energy Agency · Swedish Research Council · Research Council of Norway · Norwegian Micro- and Nano-Fabrication Facility · ETH Zurich Postdoctoral Fellowship
References (35)
Show source-provided references
1. Current status and perspectives of ultrahigh-voltage SiC power devices10.1016/j.mssp.2017.10.010 ↗
2. Characteristics of 600, 1200, and 3300 V planar SiC-MOSFETs for energy conversion applications10.1109/ted.2014.2358581 ↗
3. Jpn. J. Appl. Phys. · 2015 · 54 · 09800410.7567/jjap.54.098004 ↗
4. Mater. Sci. Forum · 2014 · 778–780 · 17910.4028/www.scientific.net/msf.778-780.179 ↗
5. Very high growth rate of 4H–SiC epilayers using the chlorinated precursor methyltrichlorosilane (MTS)10.1016/j.jcrysgro.2007.07.002 ↗
6. 4H–SiC epitaxial growth with chlorine addition10.1002/cvde.200506465 ↗
7. J. Cryst. Growth · 2013 · 362 · 17010.1016/j.jcrysgro.2011.09.061 ↗
8. Formation mechanism of horizontal-half-loop arrays and stacking fault expansion behavior in thick SiC epitaxial layers10.1063/5.0092889 ↗
9. High quality 4H–SiC homo-epitaxial wafer using the optimal C/Si ratio10.1016/j.jcrysgro.2019.125302 ↗
10. Reduction of structural defects in thick 4H–SiC epitaxial layers grown on 4° off-axis substrates10.1063/1.4809928 ↗
11. Conductivity modulated on-axis 4H–SiC 10+ kV PiN diodes
12. Mater. Sci. Forum · 2022 · 1062 · 19010.4028/p-97jy4p ↗
13. IEEE J. Emerging Sel. Top. Power Electron. · 2020 · 8 · 23910.1109/jestpe.2019.2951801 ↗
14. J. Appl. Phys. · 2003 · 93 · 470810.1063/1.1543240 ↗
15. J. Appl. Phys. · 2010 · 108 · 08372110.1063/1.3498818 ↗
16. Cryst. Growth Des. · 2014 · 14 · 410410.1021/cg5007154 ↗
17. Appl. Phys. Express · 2010 · 3 · 12120110.1143/apex.3.121201 ↗
18. Elimination of carbon vacancies in 4H–SiC employing thermodynamic equilibrium conditions at moderate temperatures10.1063/1.4938242 ↗
19. J. Appl. Phys. · 2009 · 105 · 12351810.1063/1.3147903 ↗
20. Appl. Phys. Lett. · 2006 · 88 · 05211010.1063/1.2170144 ↗
21. Appl. Phys. Lett. · 2007 · 90 · 20210910.1063/1.2740580 ↗
22. Negative-U system of carbon vacancy in 4H–SiC10.1103/physrevlett.109.187603 ↗
23. J. Cryst. Growth · 2013 · 381 · 4310.1016/j.jcrysgro.2013.06.037 ↗
24. Elimination of the major deep levels in n- and p-type 4H–SiC by two-step thermal treatment10.1143/apex.2.091101 ↗
25. Enhanced annealing of the Z1/2 defect in 4H–SiC epilayers10.1063/1.2829776 ↗
26. Deep level transient fourier spectroscopy (DLTFS)—A technique for the analysis of deep level properties10.1016/0038-1101(88)90071-8 ↗
27. Phys. Status Solidi A · 2011 · 208 · 279010.1002/pssa.201127260 ↗
28. J. Phys. D: Appl. Phys. · 2019 · 52 · 10LT0110.1088/1361-6463/aaf8e9 ↗
29. Phys. Rev. B · 1980 · 22 · 284210.1103/physrevb.22.2842 ↗
30. Long carrier lifetime in 4H–SiC epilayers using chlorinated precursors10.4028/www.scientific.net/msf.615-617.291 ↗
31. I. D. Booker, “Carrier lifetime relevant deep levels in SiC,” Ph.D. thesis, Linköping University, Semiconductor Materials, Faculty of Science and Engineering, 2015.10.3384/diss.diva-121515 ↗
32. Pseudodonor nature of the DI defect in 4H–SiC10.1063/1.1334907 ↗
33. Phys. Status Solidi A · 1997 · 162 · 27710.1002/1521-396x(199707)162:1<277::aid-pssa277>3.0.co;2-c ↗
34. Minority carrier trap in n-type 4H–SiC Schottky barrier diodes10.3390/cryst9070328 ↗
35. Theory of shallow and deep boron defects in 4H–SiC10.1103/physrevb.106.224112 ↗