Elastocaloric effects in ultra-fine grained NiTi microwires processed by cold-drawing
Source abstract
Abstract
Efficient elastocaloric cooling in shape memory alloys requires a stable superelastic behavior in which high yield strength is needed. Here Ni50.4Ti49.6 microwires with diameter 130 μm and ultra-fine grains ∼30 nm were prepared by multi-step cold-drawing and low-temperature annealing. Enhanced cyclic stability of the elastocaloric effects induced by the superelastic training was demonstrated. The pre-trained microwire showed a stable ΔSe 43 J/(kg K) with a broad working temperature range ΔT ∼ 70 K. The superelastic trained microwire, with giant and stable ΔSe over a wide working temperature window, may act as a promising elastocaloric cooling material for minor-sized devices.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Shape Memory Alloy Transformations · Ferroelectric and Piezoelectric Materials · Magnetic and transport properties of perovskites and related materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Materials Science and Engineering, Harbin Institute of Technology , Harbin 150001, China
Funding
National Key R&D Program of China · National Natural Science Foundation of China · China Postdoctoral Science Foundation
References (39)
Show source-provided references
1. Adv. Mater. · 2017 · 29 · 160360710.1002/adma.201603607 ↗
2. APL Mater. · 2016 · 4 · 06410710.1063/1.4953433 ↗
3. Sci. Rep. · 2016 · 6 · 2550010.1038/srep31903 ↗
4. AIP Adv. · 2015 · 5 · 06715310.1063/1.4922871 ↗
5. Science · 2006 · 311 · 127010.1126/science.1123811 ↗
6. Science · 2008 · 321 · 82110.1126/science.1159655 ↗
7. Int. J. Refrig. · 2015 · 54 · 8810.1016/j.ijrefrig.2015.03.001 ↗
8. Smart Mater. Struct. · 2016 · 25 · 08503710.1088/0964-1726/25/8/085037 ↗
9. Adv. Mater. · 2014 · 26 · 613210.1002/adma.201401935 ↗
10. Scr. Mater. · 2017 · 134 · 4210.1016/j.scriptamat.2017.02.026 ↗
11. Mater. Today: Proc. · 2015 · 2 · S97110.1016/j.matpr.2015.07.443 ↗
12. Appl. Phys. Lett. · 2012 · 101 · 7390410.1063/1.4746257 ↗
13. Int. J. Refrig. · 2016 · 64 · 110.1016/j.ijrefrig.2015.12.001 ↗
14. J. Alloys Compd. · 2015 · 630 · 24410.1016/j.jallcom.2015.01.040 ↗
15. Acta Mater. · 2015 · 96 · 42010.1016/j.actamat.2015.06.011 ↗
16. Acta Mater. · 2015 · 96 · 29210.1016/j.actamat.2015.05.054 ↗
17. Appl. Phys. Lett. · 2015 · 106 · 20190310.1063/1.4921531 ↗
18. Appl. Phys. Lett. · 2014 · 105 · 16190510.1063/1.4899147 ↗
19. Acta Mater. · 2014 · 81 · 910.1016/j.actamat.2014.08.006 ↗
20. Appl. Phys. Lett. · 2016 · 108 · 07190210.1063/1.4942009 ↗
21. Appl. Phys. Lett. · 2013 · 103 · 21190410.1063/1.4832339 ↗
22. Funct. Mater. Lett. · 2009 · 2 · 7310.1142/s1793604709000594 ↗
23. J. Appl. Phys. · 2015 · 117 · 12490110.1063/1.4913878 ↗
24. Appl. Phys. Lett. · 2012 · 101 · 09190310.1063/1.4748307 ↗
25. APL Mater. · 2016 · 4 · 06410210.1063/1.4948271 ↗
26. Acta Mater. · 2011 · 59 · 53710.1016/j.actamat.2010.09.057 ↗
27. J. Alloys Compd. · 2016 · 688 · 6210.1016/j.jallcom.2016.07.168 ↗
28. Acta Mater. · 2015 · 95 · 3710.1016/j.actamat.2015.05.015 ↗
29. Acta Mater. · 2010 · 58 · 450310.1016/j.actamat.2010.04.046 ↗
30. Phys. Rev. Lett. · 2008 · 100 · 12590110.1103/physrevlett.100.125901 ↗
31. Metall. Trans. A · 1986 · 17 · 11510.1007/bf02644447 ↗
32. Mater. Sci. Eng.: A · 2008 · 481-482 · 14210.1016/j.msea.2007.01.182 ↗
33. Acta Mater. · 2004 · 52 · 338310.1016/j.actamat.2004.03.038 ↗
34. J. Alloys Compd. · 2015 · 645 · 33510.1016/j.jallcom.2015.05.118 ↗
35. J. Alloys Compd. · 2015 · 622 · 62210.1016/j.jallcom.2014.10.142 ↗
36. Shape Mem. Superelasticity · 2016 · 2 · 9510.1007/s40830-016-0054-3 ↗
37. Appl. Phys. Lett. · 2014 · 105 · 24190110.1063/1.4904419 ↗
38. Mater. Des. · 2016 · 92 · 93210.1016/j.matdes.2015.12.118 ↗
39. Appl. Phys. Lett. · 2010 · 96 · 07191210.1063/1.3309755 ↗