Peculiarities of Sol-Gel Synthesis of Aluminum-Magnesium Spinel
Source abstract
Abstract
The results of studies of the chemical and mineralogical characteristics of alumina-containing wastes of the gas processing industry and the possibilities of their use for the synthesis of aluminum-magnesium spinel are presented. The optimal condition for the synthesis of MgAl2O4 spinel by the sol-gel method using alumina-containing waste is found to be 1000°C temperature and 120 min soaking.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Aerogels and thermal insulation · Pigment Synthesis and Properties · Recycling and utilization of industrial and municipal waste in materials production
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (15)
Show source-provided references
1. J. F. Rufner, R. H. R. Castro, T. Holland, and K. van Benthem, “Mechanical properties of individual MgAl2O4 agglomerates and their effects on densification,” Acta Mater., No. 69, 187 – 195 (2014).10.1016/j.actamat.2014.01.051 ↗
2. J. A. Wollmershauser, B. N. Feigelson, S. B. Qadri, and G. R. Villalobos, “Transparent nanocrystalline spinel by room temperature high-pressure compaction,” Scr. Mater., No. 69, 334 – 337 (2013).10.1016/j.scriptamat.2013.05.014 ↗
3. L. Zarazúa-Villalobos, J. L. Téllez-Jurado, N. Vargas-Becerril, and G. Fantozzi, “Synthesis of magnesium aluminate spinel nanopowder by sol-gel and low-temperature processing,” J. Sol-Gel Sci. Technol., No. 85, 110 – 120 (2018).10.1007/s10971-017-4526-5 ↗
4. R. Sarkar, “Refractory applications of magnesium aluminate spinel,” Int. Ceram. Refract. Manual, No. 1, 11 – 14 (2010).
5. R. Sarkar and S. Sahoo, “Effect of raw materials on formation and densification of magnesium aluminate spinel,” Ceram. Int., 40, 16719 – 16725 (2014).10.1016/j.ceramint.2014.08.037 ↗
6. S. Adison, J. Sirithan, J. Supatra, and S. Karn, “Synthesis and sintering of magnesium aluminate spinel nanopowders prepared by precipitation method using ammonium hydrogen carbonate as a precipitant,” Key Eng. Mater., 690, 224 – 229 (2016).10.4028/www.scientific.net/KEM.690.224 ↗
7. X. Zhang, “Hydrothermal synthesis and catalytic performance of high-surface-area mesoporous nanocrystallite MgAl2O4 as catalyst support,” Mater. Chem. Phys., 116, 415 – 420 (2009).10.1016/j.matchemphys.2009.04.012 ↗
8. R. Iano°, I. Lazâu, and C. Pâcurariu, “Solution combustion synthesis of MgAl2O4 using fuel mixtures,” Mater. Res. Bull., 43, 3408 – 3415 (2008).10.1016/j.materresbull.2008.02.003 ↗
9. C. T. Wang, L. S. Lin, and S. J. Yang, “Preparation of MgAl2O4 spinel powders via freeze-drying of alkoxide precursors,” J. Am. Ceram. Soc., 75, 2240 – 2243 (1992).10.1111/j.1151-2916.1992.tb04490.x ↗
10. S. Sanjabi and A. Obeydavi, “Synthesis and characterization of nanocrystalline MgAl2O4 spinel via modified sol-gel method,” J. Alloys Compd., 645, 535 – 540 (2015).10.1016/j.jallcom.2015.05.107 ↗
11. W. Liu, J. Yang, H. Xu, et al., “Effects of chelation reactions between metal alkoxide and acetylacetone on the preparation of MgAl2O4 powders by sol-gel process,” Adv. Powder Technol., 24, 436 – 440 (2013).10.1016/j.apt.2012.09.006 ↗
12. ASTM Standards. Pt 17. Refractories, Glass, Ceramic Materials, Carbon and Graphite Products, ASTM, Philadelphia (2005), pp. 7 – 9, 51 – 61.
13. Z. R. Kadyrova, S. K. Tuganova, and A. A. Éminov, “High-temperature interaction between calcium and strontium titanodisilicates,” Glass Ceram., 68(11 – 12), 413 – 415 (2011) [Steklo Keram., No. 12, 31 – 33 (2011)].10.1007/s10717-012-9402-8 ↗
14. Sh. M. Niyazova, Z. R. Kadyrova, Kh. L. Usmanov, and F. G. Khomidov, “Ñhemical and mineralogical studies of magmatic rocks of Uzbekistan for obtaining heat-insulating materials,” Glass Ceram., 75(11 – 12), 491 – 495 (2019) [Steklo Keram., No. 12, 40 – 44 (2018)].10.1007/s10717-019-00119-0 ↗
15. Al. A. Eminov, Z. R. Kadyrova, and M. Iskandarova, “Gas processing waste is a promising raw material for formulating the composition of ceramic grinding bodies,” Steklo Keram., No. 1, 43 – 48 (2021).10.1007/s10717-021-00344-6 ↗