Glass formation and crystallization of high lead content PbO-B2O3 compositions

The glass-forming and undercooling ability of PbO-B2O3 melts in the 2PbO.B2O3 to 4PbO.B2O3 composition range were studied. The glass formation propensities were investigated as a function of cooling rate and sample mass. A qualitative investigation of the crystallization process(es) preventing glass formation was made, and it was concluded that under normal circumstances heterogeneous nucleation was the common occurrence. Hence, it was concluded that such compositions are prime candidates for containerless experiments aboard the Space Shuttle.