Calcium-barium sulfo-ferritealuminate series minerals
Source abstract
Abstract
Based on the dominant mineral in barium-bearing sulfoaluminate calcium cement C2·75B1·25A3S¯, the calcium-barium sulfo-ferritealuminate series minerals were synthesised by replacing Al3+ with a different equivalent of Fe3+. The microstructure was investigated by means of X-ray diffraction, dynamic thermal analysis/thermogravimetric analysis, scanning electron microscopy–energy dispersive spectroscopy (SEM–EDS). The results indicated that the optimal molar composition of Fe3+ ions was from 0·5 to 1·7. The optimum composition was C2·75B1·25A1·5Fe1·5S¯. At this level, the strength at 1, 3 and 28 days could reach 64, 77·75 and 86·62 MPa, respectively.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Geomechanics and Mining Engineering · Grouting, Rheology, and Soil Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Materials Science and Engineering, University of Jinan, China
References (8)
Show source-provided references
1. 10.1016/j.cemconres.2004.02.02110.1016/j.cemconres.2004.02.021 ↗
2. Chang J. · Bulletin of the Chinese Ceramic Society · 2004 · 5 · No. 21
3. 10.1016/S0008-8846(97)00091-410.1016/S0008-8846(97)00091-4 ↗
4. Yan P. · Advances in Cement Research · 1993 · 18 · 63
5. Chang J. Study on New Type Ba-bearing Cement, 1998, Master's degree thesis. Wuhan University of Technology, Wuhan, China.
6. Sui T. · China Cement · 2006 · 3 · 59
7. Pan Z. · Journal of University of Jinan (Science and Technology) · 2008 · 22 · 20
8. Chang J. · Journal of the Chinese Ceramic Society · 2005 · 33 · 1032