A reaction range for hydration of calcium sulfoaluminate with calcium sulfate and calcium hydroxide: theory and experimental validation
Source abstract
Abstract
To better investigate and understand the hydration of calcium sulfoaluminate (CSA) cement, a theory reaction range for the hydration of CSA with calcium sulfate and calcium hydroxide was established by theoretical calculation with a hypothetical hydration reaction system. With different amounts of calcium sulfate and calcium hydroxide in the reaction systems, their hydration processes, hydration products and stoichiometric water/solid ratios showed regular changes. A preliminary experimental validation was made by analysing the hydration products (curing time 28 d and water/solid ratio of 10) of several composition points in the theory reaction range by means of x-ray diffraction and thermogravimetric analysis. The process for calculation of the theory reaction range and some of the experimental validation results are presented in this paper.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Drilling and Well Engineering · Grouting, Rheology, and Soil Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
School of Civil Engineering, Dalian University of Technology, Dalian, China (corresponding author: )
School of Civil Engineering, Dalian University of Technology, Dalian, China
References (40)
Show source-provided references
1. 10.1016/j.cemconres.2014.07.00910.1016/j.cemconres.2014.07.009 ↗
2. 10.1016/j.cemconres.2015.02.01110.1016/j.cemconres.2015.02.011 ↗
3. 10.1016/S0008-8846(96)00164-010.1016/S0008-8846(96)00164-0 ↗
4. 10.1016/j.cemconres.2013.11.01110.1016/j.cemconres.2013.11.011 ↗
5. CRD (Cement Research Division) · Journal of the Chinese Ceramic Society · 1978 · 4 · 123
6. 10.1016/j.cemconres.2014.05.01010.1016/j.cemconres.2014.05.010 ↗
7. 10.1080/19648189.2010.969324810.1080/19648189.2010.9693248 ↗
8. Didamony HE · Ceramics-Silikáty · 2012 · 56 · 389
9. 10.1016/j.cemconres.2013.07.01010.1016/j.cemconres.2013.07.010 ↗
10. 10.1016/j.cemconres.2004.01.02110.1016/j.cemconres.2004.01.021 ↗
11. 10.1016/S0008-8846(01)00649-410.1016/S0008-8846(01)00649-4 ↗
12. 10.1016/0008-8846(89)90038-010.1016/0008-8846(89)90038-0 ↗
13. 10.1016/j.cemconres.2013.03.00110.1016/j.cemconres.2013.03.001 ↗
14. 10.1016/0008-8846(92)90019-R10.1016/0008-8846(92)90019-R ↗
15. 10.1016/j.cemconres.2010.11.01210.1016/j.cemconres.2010.11.012 ↗
16. 10.1016/0008-8846(89)90069-010.1016/0008-8846(89)90069-0 ↗
17. 10.1016/0008-8846(95)00168-910.1016/0008-8846(95)00168-9 ↗
18. 10.1016/0040-6031(85)85888-310.1016/0040-6031(85)85888-3 ↗
19. Martin D · Ceramics · 2005 · 49 · 104
20. 10.1111/j.1151-2916.1973.tb12503.x10.1111/j.1151-2916.1973.tb12503.x ↗
21. 10.1016/j.conbuildmat.2010.09.01510.1016/j.conbuildmat.2010.09.015 ↗
22. 10.1016/S0008-8846(99)00048-410.1016/S0008-8846(99)00048-4 ↗
23. 10.1016/0008-8846(81)90032-610.1016/0008-8846(81)90032-6 ↗
24. 10.1016/0008-8846(82)90104-110.1016/0008-8846(82)90104-1 ↗
25. 10.1016/0008-8846(82)90011-410.1016/0008-8846(82)90011-4 ↗
26. 10.1007/BF0213503510.1007/BF02135035 ↗
27. 10.1016/j.cemconres.2013.01.00810.1016/j.cemconres.2013.01.008 ↗
28. Song J · Journal of the American Ceramic Society · 2002 · 85 · 53510.1111/j.1151-2916.2002.tb00129.x ↗
29. Su MZ · 1992 · 1 · 317
30. 10.1016/j.conbuildmat.2014.11.00610.1016/j.conbuildmat.2014.11.006 ↗
31. 10.1680/adcr.1989.2.5.2910.1680/adcr.1989.2.5.29 ↗
32. 10.1016/j.cemconres.2013.01.01510.1016/j.cemconres.2013.01.015 ↗
33. Wang L · Advances in Cement Research · 1996 · 8 · 12710.1680/adcr.1996.8.31.127 ↗
34. Wang YM · 1999
35. Winnefeld F · ZKG International · 2009 · 62 · 42
36. 10.1007/s10973-009-0582-610.1007/s10973-009-0582-6 ↗
37. 10.1016/j.cemconres.2009.08.01410.1016/j.cemconres.2009.08.014 ↗
38. 10.1016/j.cemconres.2011.06.00310.1016/j.cemconres.2011.06.003 ↗
39. 10.1680/adcr.2002.14.4.14110.1680/adcr.2002.14.4.141 ↗
40. 10.1680/adcr.1999.11.1.1510.1680/adcr.1999.11.1.15 ↗