Effect of temperature on the initial properties of calcium sulfoaluminate binders synthesised at 1100°C
Source abstract
Abstract
In this investigation, it was studied the effect of curing temperature on the mechanical properties of pastes made with calcium sulfoaluminate cements synthesised from industrial wastes at a relatively low temperature of 1100°C. Fluorgypsum, fly ash, aluminium slag and calcium carbonate were used as raw materials. The main phases of synthesis were calcium sulfoaluminate and gehlenite. Pastes were prepared with different water/cement ratios, 15–25 wt-% hemihydrate and cured at 20 and 40°C. It was found that with higher total amounts of sulphates and increase in temperature, compressive strength is enhanced in the first days of curing and setting times decreased. Ettringite was found to be the main reaction product forming dense structures over time. Calcium sulphates hydration changed the ettringite formation causing fluctuations in the strength development, nevertheless, in some cases the strength surpassed 40 MPa at 28 days. Microstructures and hydration products were studied by SEM and XRD.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Concrete and Cement Materials Research · Recycling and utilization of industrial and municipal waste in materials production · Innovations in Concrete and Construction Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Universidad Autónoma de Coahuila – UAdeC, Facultad de Ingeniería, Arteaga, México
Centro de Investigación y de Estudios Avanzados del IPN, CINVESTAV Unidad Saltillo, Ramos Arizpe, México
Centro Nacional de Metrología, CENAM, El Marqués, México
References (30)
Show source-provided references
1. 10.1016/j.cemconcomp.2011.08.00110.1016/j.cemconcomp.2011.08.001 ↗
2. 10.1016/j.conbuildmat.2015.02.08510.1016/j.conbuildmat.2015.02.085 ↗
3. 10.1016/j.cemconres.2007.09.00810.1016/j.cemconres.2007.09.008 ↗
4. Olivier JGJ
5. 10.1680/jadcr.18.0001910.1680/jadcr.18.00019 ↗
6. 10.1680/adcr.1996.8.31.12710.1680/adcr.1996.8.31.127 ↗
7. 10.1016/0008-8846(94)90030-210.1016/0008-8846(94)90030-2 ↗
8. 10.1016/j.cemconcomp.2014.01.00910.1016/j.cemconcomp.2014.01.009 ↗
9. 10.1016/S0008-8846(99)00072-110.1016/S0008-8846(99)00072-1 ↗
10. 10.1680/adcr.1999.11.1.3510.1680/adcr.1999.11.1.35 ↗
11. 10.1016/j.jclepro.2017.05.05510.1016/j.jclepro.2017.05.055 ↗
12. 10.1016/j.jhazmat.2007.06.11810.1016/j.jhazmat.2007.06.118 ↗
13. 10.1016/j.cemconcomp.2003.10.00210.1016/j.cemconcomp.2003.10.002 ↗
14. 10.1016/S0008-8846(01)00579-810.1016/S0008-8846(01)00579-8 ↗
15. 10.4028/www.scientific.net/kem.334-335.42110.4028/www.scientific.net/kem.334-335.421 ↗
16. 10.1016/j.minpro.2012.03.01110.1016/j.minpro.2012.03.011 ↗
17. Wang Y · 1999
18. 10.1016/j.cemconres.2011.03.00610.1016/j.cemconres.2011.03.006 ↗
19. 10.1016/j.conbuildmat.2018.12.05410.1016/j.conbuildmat.2018.12.054 ↗
20. 10.1016/j.cemconres.2013.03.00110.1016/j.cemconres.2013.03.001 ↗
21. 10.1016/j.cemconcomp.2010.03.01010.1016/j.cemconcomp.2010.03.010 ↗
22. 10.1617/s11527-016-0960-z10.1617/s11527-016-0960-z ↗
23. ASTM, International · 2017
24. ONNCCE. (2002). NMX-C-085-ONNCCE-2002, Construction industry – Hydraulic cements – Standard test method for mechanical mixing of hydraulic cement pastes and mortars. In Spanish. México, D.F.
25. 10.1016/S0008-8846(00)00328-810.1016/S0008-8846(00)00328-8 ↗
26. 10.1016/j.cemconres.2006.02.01410.1016/j.cemconres.2006.02.014 ↗
27. ASTM, International · 2004
28. ONNCCE. (2004). NMX-C-414-ONNCCE-2004, Construction industry – Hydraulic cements – Specifications and testing methods. In Spanish. México. D. F.
29. 10.1016/j.cemconres.2013.06.00810.1016/j.cemconres.2013.06.008 ↗
30. Zhang L, Glasser FP, Dhir RK, et al. New concretes based on calcium sulfoaluminate cement. modern concrete materials: binders, additions and admixtures. Thomas Telford; 2015. p. 261–274. https://www.icevirtuallibrary.com/doi/abs/10.1680/mcmbaaa.28227.0027.