Oxidation response of a SiCf/SiC CMC with a HfB 2 -based coating in an arc jet test
Source abstract
Abstract
The behaviour of a SiC-fibre-reinforced composite with a graded matrix was investigated in an arc jet facility. The graded matrix was comprised of several layers of silicon carbide that transition to a mixed SiC-HfB2 top layer and was sealed with an HfB2-SiC coating. Samples were exposed to maximum specific total enthalpy hypersonic flow between 14 and 17 MJ kg−1 under stagnation pressures between 2700 and 3050 Pa for hold times of between 137 and 395 s. The resulting sample surface temperatures ranged between 1600 and 1950°C. Spectral emissivity at about 1 μm was calculated using a pyrometer capable of switching between one and two color modes and was shown to decrease with oxidation and removal of SiO2 from the surface. The impacts of the surface chemistry changes during oxidation and of active oxidation were investigated.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Advanced materials and composites · Diamond and Carbon-based Materials Research
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Materials and Manufacturing Directorate, Air Force Research Laboratory, Wright Patterson AFB, OH, USA
UES, Inc., Dayton, OH, USA
Centro Italiano Ricerche Aerospaziali, Capua, Italy
SOCHE, Dayton, OH, USA
Funding
Air Force Research Laboratory
References (28)
Show source-provided references
1. 10.1016/j.jascer.2014.07.00410.1016/j.jascer.2014.07.004 ↗
2. 10.1016/j.msea.2005.08.20410.1016/j.msea.2005.08.204 ↗
3. 10.1016/S0008-6223(97)00207-810.1016/S0008-6223(97)00207-8 ↗
4. 10.1016/j.carbon.2009.01.00210.1016/j.carbon.2009.01.002 ↗
5. 10.1016/0955-2219(96)00025-810.1016/0955-2219(96)00025-8 ↗
6. 10.1111/ijac.1265910.1111/ijac.12659 ↗
7. 10.1016/j.jeurceramsoc.2010.02.01310.1016/j.jeurceramsoc.2010.02.013 ↗
8. 10.1016/j.msea.2007.02.04010.1016/j.msea.2007.02.040 ↗
9. 10.1016/j.ceramint.2012.10.27310.1016/j.ceramint.2012.10.273 ↗
10. 10.1016/j.surfcoat.2005.11.12210.1016/j.surfcoat.2005.11.122 ↗
11. 10.1016/S1270-9638(03)00054-310.1016/S1270-9638(03)00054-3 ↗
12. 10.1023/B:JMSC.0000041689.90456.af10.1023/B:JMSC.0000041689.90456.af ↗
13. 10.1007/s11085-010-9216-410.1007/s11085-010-9216-4 ↗
14. Wuchina E · Electrochem Soc Interface · 2007 · 16 · 3010.1149/2.F04074IF ↗
15. 10.1016/j.surfcoat.2017.01.01910.1016/j.surfcoat.2017.01.019 ↗
16. 10.1111/ijac.1245310.1111/ijac.12453 ↗
17. 10.1111/ijac.1280510.1111/ijac.12805 ↗
18. Krasnov NF. · 1970
19. 10.1016/j.actaastro.2007.01.04610.1016/j.actaastro.2007.01.046 ↗
20. 10.1016/j.jeurceramsoc.2007.11.02110.1016/j.jeurceramsoc.2007.11.021 ↗
21. 10.1007/BF0054447410.1007/BF00544474 ↗
22. 10.1023/A:101794282665710.1023/A:1017942826657 ↗
23. 10.1016/j.jeurceramsoc.2010.01.02910.1016/j.jeurceramsoc.2010.01.029 ↗
24. 10.1111/j.1551-2916.2008.02325.x10.1111/j.1551-2916.2008.02325.x ↗
25. 10.1023/B:HITE.0000026157.04515.1810.1023/B:HITE.0000026157.04515.18 ↗
26. Ohlhorst C, Vaughn WL, Lewis RK, et al. Arc jet results on candidate high temperature coatings for NASA’s NGLT refractory composite leading edge task. Place: NASA Langley; 2003. (NASA Technical Reports Server; 20040040337).
27. 10.1016/j.ast.2009.12.00410.1016/j.ast.2009.12.004 ↗
28. 10.1016/j.jeurceramsoc.2008.12.01110.1016/j.jeurceramsoc.2008.12.011 ↗