Electrocaloric properties of 0.7Pb(Mg 1/3 Nb 2/3 )O 3 –0.3PbTiO 3 ceramics with different grain sizes
Source abstract
Abstract
We have investigated the electrocaloric (EC) properties of the ceramic 0.7Pb(Mg1/3Nb2/3)O3–0.3PbTiO3. A variety of samples with different median grain sizes, i.e., 1.0, 2.2 and 4.0 μm, and relative densities of about 96% were prepared using atmospheric sintering at 1200oC for 2, 8 and 16 h. The ceramic material with a median grain size of 2.2 μm exhibited the highest value for the EC temperature change, i.e., 1.27 K at 60 kV cm−1, measured with a high-resolution calorimeter. This value is 25 and 19% higher than the value for the ceramics with the finer and the coarser grains, respectively.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Ferroelectric and Piezoelectric Materials · Microwave Dielectric Ceramics Synthesis · Multiferroics and related materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (27)
Show source-provided references
1. 10.1016/j.pmatsci.2012.02.00110.1016/j.pmatsci.2012.02.001 ↗
2. 10.1038/nmat395110.1038/nmat3951 ↗
3. Lu S. G. · 2010 · 99
4. 10.1007/978-3-642-40264-7_710.1007/978-3-642-40264-7_7 ↗
5. 10.1080/0015019810822349610.1080/00150198108223496 ↗
6. Bai Y. · Appl. Phys. Lett. · 2013 · 103 · 1
7. 10.1111/j.1151-2916.1997.tb02927.x10.1111/j.1151-2916.1997.tb02927.x ↗
8. 10.1063/1.148312010.1063/1.1483120 ↗
9. 10.1179/174367509X1247236460099510.1179/174367509X12472364600995 ↗
10. Uršič H. · Jpn. J. Appl. Phys. · 2013 · 52 · 1
11. 10.1179/174367509X1247236460107510.1179/174367509X12472364601075 ↗
12. Plaznik U. · Appl. Phys. Lett. · 2015 · 106 · 1
13. Rožič B. · J. Appl. Phys. · 2011 · 110 · 1
14. 10.1016/j.physletb.2012.06.06210.1016/j.physletb.2012.06.062 ↗
15. 10.1007/978-3-642-40264-7_310.1007/978-3-642-40264-7_3 ↗
16. 10.1038/162329b010.1038/162329b0 ↗
17. 10.1080/00150193.2011.59474210.1080/00150193.2011.594742 ↗
18. 10.1063/1.36186510.1063/1.361865 ↗
19. Singh A. K. · Phys. Rev. B · 2003 · 67 · 1
20. 10.1016/j.actamat.2005.09.02010.1016/j.actamat.2005.09.020 ↗
21. 10.1111/j.1551-2916.2008.02714.x10.1111/j.1551-2916.2008.02714.x ↗
22. 10.1088/0953-8984/15/40/02510.1088/0953-8984/15/40/025 ↗
23. 10.1002/(SICI)1521-4079(1998)33:5<827::AID-CRAT827>3.0.CO;2-H10.1002/(SICI)1521-4079(1998)33:5<827::AID-CRAT827>3.0.CO;2-H ↗
24. 10.1111/j.1151-2916.2002.tb00572.x10.1111/j.1151-2916.2002.tb00572.x ↗
25. 10.1557/JMR.1993.088010.1557/JMR.1993.0880 ↗
26. 10.1016/0038-1098(69)90688-710.1016/0038-1098(69)90688-7 ↗
27. 10.1016/j.jeurceramsoc.2015.09.03110.1016/j.jeurceramsoc.2015.09.031 ↗