Micro‐Raman spectroscopy of indentation induced phase transformation in nanozirconia ceramics

AbstractMicro‐Raman spectroscopy has been employed as an effective technique to determine the phase transformations in nanostructured yttria stabilised zirconia (YSZ) ceramics with different yttria contents. Samples have been prepared with varying mean grain sizes by a slip casting route followed by a microwave assisted two‐step sintering cycle starting with aqueous nanozirconia suspensions. Indents were generated using a Vickers pyramidal indenter at different loads, and the resulting phase transformations were mapped using micro‐Raman spectroscopy. The results were compared to those of a commercial submicrometre 3 mol.% YSZ. The amount of transformation was found to be much lower for nanozirconia compared to the submicrometre zirconia with similar yttria content.