Kinetics investigation of alumina ceramics corrosion in nitric acid

The most widely used ceramic material is aluminium oxide, known as alumina. Due to its superior properties such as chemical stability, high wear resistance, refractoriness and so on, it is ideal for applications in aggressive environment. This type of environment often includes exposure to corrosive solids, liquids and gases. When ceramics come in contact with corrosive medium, several corrosion mechanisms can occur, depending on a number of parameters. Therefore, the corrosion behaviour of cold isostatically pressed (CIP) high purity alumina ceramics was observed under different conditions: 0.5, 1.25 and 2 mol dm ⁻³ of nitric acid at 25°C, 40°C and 55°C through 10 days. Purity of used alumina ceramics was 99.8345 wt. % with 0.1655 wt. % of both sintering aid (MgO) and impurities (SiO ₂ , CaO, Na ₂ O and Fe ₂ O ₃ ). The results show that Al ₂ O ₃ ceramics exhibit good corrosion resistance in nitric acid. Al ₂ O ₃ corrosion behaviour varies depending on the temperature, time and HNO ₃ concentration. In view of the reaction kinetics, it proceeds in the near-parabolic law in HNO ₃ aqueous solution and decreases with an increase of the HNO ₃ concentration.