journal article·2018-10-03

Effects of heat treatment temperatures on microstructures and mechanical properties of the chopped carbon fibres SiC composites

Hui Mei, Hui Zhang, Weizhao Huang, Ming Han, Yawei Xu, Laifei Cheng

Advances in Applied Ceramics· Volume 117· Issue 7
Publisher page

Abstract

A simple wet papermaking technique was used to fabricate chopped carbon fibre paper (Csf-paper) with random fibre orientation and self-supporting network structures in this work. The Csf-papers were laminated layer by layer and further infiltrated with PyC interface and SiC matrix via chemical vapour infiltration (CVI) to obtain Csf/SiC composites. The effects of heat treatment temperatures on microstructures, phase composition, and mechanical properties were investigated. Results showed that the Csf-paper has played a good self-supporting role and its fibres form a completely random fibre orientation in 2D plane. The fibres almost remained undamaged and unbroken during the CVI. Proper heat treatment could improve the mechanical properties. At 1200°C, the maximum values of flexural strength and Young's modulus reached about 306 MPa and 196.5 GPa, respectively. Meanwhile, compared with tape casting, reaction sintering and spark plasma sintering, composites fabricated by wet papermaking and CVI can improve the mechanical properties.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Advanced ceramic materials synthesis · Fiber-reinforced polymer composites · Aluminum Alloys Composites Properties

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Science and Technology on Thermostructural Composite Materials Laboratory, Northwestern Polytechnical University, Xi’an, People’s Republic of China

Funding

National Natural Science Foundation of China · Program for New Century Excellent Talents in University

References (25)

Show source-provided references
1. 10.1016/j.msea.2012.08.13310.1016/j.msea.2012.08.133 ↗
2. 10.1016/j.msea.2012.01.11810.1016/j.msea.2012.01.118 ↗
3. 10.1016/j.surfcoat.2007.08.03710.1016/j.surfcoat.2007.08.037 ↗
4. 10.1016/j.msea.2012.09.02710.1016/j.msea.2012.09.027 ↗
5. 10.1016/j.compscitech.2008.07.00110.1016/j.compscitech.2008.07.001 ↗
6. 10.1016/j.jeurceramsoc.2006.04.01910.1016/j.jeurceramsoc.2006.04.019 ↗
7. 10.1016/j.msea.2009.08.00410.1016/j.msea.2009.08.004 ↗
8. 10.1016/j.compscitech.2012.01.01410.1016/j.compscitech.2012.01.014 ↗
9. 10.1111/ijac.1214910.1111/ijac.12149 ↗
10. 10.1016/j.ceramint.2011.08.02410.1016/j.ceramint.2011.08.024 ↗
11. 10.1016/j.msea.2013.09.01410.1016/j.msea.2013.09.014 ↗
12. 10.2109/jcersj.114.32310.2109/jcersj.114.323 ↗
13. 10.1016/j.ceramint.2011.08.05810.1016/j.ceramint.2011.08.058 ↗
14. 10.1016/j.ceramint.2012.02.05310.1016/j.ceramint.2012.02.053 ↗
15. 10.1016/j.msea.2012.04.10210.1016/j.msea.2012.04.102 ↗
16. 10.1016/j.ceramint.2016.03.03110.1016/j.ceramint.2016.03.031 ↗
17. 10.1016/S0022-0248(98)01215-910.1016/S0022-0248(98)01215-9 ↗
18. 10.1007/BF0110722010.1007/BF01107220 ↗
19. 10.1016/j.jeurceramsoc.2007.09.00910.1016/j.jeurceramsoc.2007.09.009 ↗
20. 10.1016/j.ceramint.2005.08.00410.1016/j.ceramint.2005.08.004 ↗
21. 10.1016/j.compscitech.2008.08.01510.1016/j.compscitech.2008.08.015 ↗
22. 10.1016/j.carbon.2012.11.00110.1016/j.carbon.2012.11.001 ↗
23. 10.1016/0001-6160(89)90291-510.1016/0001-6160(89)90291-5 ↗
24. 10.1016/S1359-835X(97)00128-010.1016/S1359-835X(97)00128-0 ↗
25. 10.1016/j.jnucmat.2004.04.15710.1016/j.jnucmat.2004.04.157 ↗