Physical and mechanical properties of hexagonal boron nitride ceramic fabricated by pressureless sintering without additive
Source abstract
Abstract
Hexagonal boron nitride hBN ceramic was successfully fabricated by pressureless sintering at 2100C using submicrometre hBN powders without any sintering additive. The as-prepared hBN ceramic showed a room temperature flexural strength of 30.7MPa. Its flexural strength increased with the increment of temperature in N2 atmosphere, and it retained a strength of 57.2MPa nearly two times of the room temperature strength at 1600C due to clean grain boundaries with no glassy phase. Additionally, the as-prepared hBN ceramic showed a high thermal conductivity of 31.76Wm1k1 and a good thermal shock resistance, which retained a relatively high residual flexural strength of 22.6MPa 73.5 of the original flexural strength at T800C. The as-prepared hBN ceramic presents a good application prospect at high temperature.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Boron and Carbon Nanomaterials Research · MXene and MAX Phase Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (20)
Show source-provided references
1. 10.1016/j.ceramint.2011.11.00310.1016/j.ceramint.2011.11.003 ↗
2. 10.1016/j.scriptamat.2011.08.02510.1016/j.scriptamat.2011.08.025 ↗
3. 10.1016/j.scriptamat.2012.09.01210.1016/j.scriptamat.2012.09.012 ↗
4. 10.1016/j.materresbull.2007.04.02210.1016/j.materresbull.2007.04.022 ↗
5. 10.1016/j.jallcom.2010.04.17010.1016/j.jallcom.2010.04.170 ↗
6. Ertug B ed. Sintering applications, Chap. 2, Powder preparation, properties and industrial applications of hexagonal boron nitride, 3441 2013, Turkey, InTech.10.5772/53325 ↗
7. Hoeing CL, The United States of America as represented by the United States Department of Energy, Washington, DC High density hexagonal boron nitride prepared by hot isostatic, US patent 5116589, published 26 May 1992.
8. 10.3724/SP.J.1077.2012.0022510.3724/SP.J.1077.2012.00225 ↗
9. 10.1111/j.1151-2916.1989.tb07682.x10.1111/j.1151-2916.1989.tb07682.x ↗
10. 10.1111/j.1551-2916.2009.03437.x10.1111/j.1551-2916.2009.03437.x ↗
11. C Lei Y · J. Jiangsu Univ. Nat Sci Ed · 2005 · 26 · 357
12. Hagio T, Kobayashi K, Yoshida T, Ogawa I, Harada H, Yasunaga H and Nishikawa H, Agency of Industrial Science and Technology Pressureless sintered body of boron nitride, US patent 5063184, published 5 November 1992.
13. Ge L · Electron. Comput. Mater. · 2008 · 27 · 22
14. Standard test method for flexural strength of advanced ceramics at ambient temperature, C116113, ASTM International, West Conshohocken, PA, USA, 2013.
15. Standard test method for flexural strength of advanced ceramics at elevated temperatures, C121113, ASTM International, West Conshohocken, PA, USA, 2013.
16. Standard test method for determination of fracture toughness of advanced ceramics at ambient temperature, C142110, ASTM International, West Conshohocken, PA, USA, 2010.
17. Standard test method for vickers indentation hardness of advanced ceramics, C132708, ASTM International, West Conshohocken, PA, USA, 2008.
18. Standard test method for dynamic youngs modulus, shear modulus, and poissons ratio for advanced ceramics by impulse excitation of vibration, C125914, ASTM International, West Conshohocken, PA, USA, 2014.
19. C Lei Y · Ordnance Mater. Sci. Eng. · 2005 · 28 · 20
20. d Gu L New inorganic nonmetal materialboron nitride ceramics, Chap. 1, Thermal properties, 56 1982, China, China Architecture Building Press.