Piezoelectric sensors fabricated by depositing solution-grown ZnO nanorods on flexible graphene-derivative electrodes

Abstract Zinc oxide nanorods (ZnO-NRs) with high-aspect ratios can significantly enhance the voltage output of mechanically flexible piezoelectric materials. A versatile chemical synthesis process for growing long narrow ZnO-NR from nanoparticle (NP) seeds by regulating the polarity of reaction solvents is introduced in this paper. The efficient nanorod (NR) growth method produces large quantities of high-aspect ratio ZnO-NRs in the reaction solvent. For ultra-small NP seeds (AVG 10.54 nm, SD 3.69), the synthesis process creates NRs with a minimal lateral growth (AVG 13.92 nm, SD 4.77) and significant longitudinal growth (AVG 150.85 nm, SD 64.93). The average aspect ratio of ZnO-NRs in the solution is ∼10.8 (SD 2.48). Once synthesized, the ZnO-NRs are mixed with polydimethylsiloxane (PDMS) to create a thin flexible piezoelectric layer/film. The composite polymer material is spin coated on an inkjet printed graphene/carboxymethyl cellulose (G-CMC) interdigitated electrode (IDE) to form the piezoelectric layer. A dielectrophoretic alignment technique is then used to reposition the NR orientations in the composite prior to final polymer curing. In this study, three different piezoelectric composites are investigated and compared: polyhedral NPs (ZnO-NP/PDMS), non-aligned nanorods (ZnO-NR _NA /PDMS), and aligned nanorods (ZnO-NR _A /PDMS). Each composite is deposited on a similar IDE and tested for impact loading and low frequency mechanical bending. Under bending, the NP ZnO-NP/PDMS sensor generated 3–4 mV while the non-aligned NR ZnO-NR _NA /PDMS sensor produced 70–80 mV. In contrast, the horizontally aligned NR ZnO-NR _A /PDMS sensor generated 150–170 mV under the same bending conditions.