Various Applications of Gadolinium Molybdate Down‐Conversion and Up‐Conversion Fluorescent Nanoparticles
Source abstract
Abstract
Abstract Crystalline α‐Gd2(MoO4)3 is synthesized by sintering at 800 °C using a coprecipitation method to prepare the precursor. The resulting α‐Gd2(MoO4)3 displayed a monocrystalline structure with a strong main peak (‐221) in the X‐ray diffraction signal. To develop a light‐emitting material, rare earth ions are added during synthesis. By doping with Tb3+ and Eu3+, the Gd2(MoO4)3 down‐conversion phosphor shows potential for use in UV–LED chips, counterfeit money prevention, and fingerprint identification. Additionally, co‐doping with [Er3+]/[Yb3+] and [Ho3+]/[Yb3+] ions produce green and red emissions when applied to a 980 nm LED chip, useful for anti‐counterfeit ink. The magnetic properties of gadolinium are leveraged to confirm magnetic resonance imaging luminescence. A flexible composite for heat detection and explored various applications for its use is also developed.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Luminescence Properties of Advanced Materials · Glass properties and applications · Luminescence and Fluorescent Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Marine‐Bionics Convergence Technology Center Pukyong National University Busan 48513 Republic of Korea
Department of Electrical Electronics and Software Engineering Pukyong National University Busan 48513 Republic of Korea
Funding
National Research Foundation of Korea · Ministry of Education
References (64)
Show source-provided references
1. 10.1016/j.jlumin.2009.11.01610.1016/j.jlumin.2009.11.016 ↗
2. 10.1021/acs.cgd.2c0138710.1021/acs.cgd.2c01387 ↗
3. 10.1016/j.ceramint.2016.09.00410.1016/j.ceramint.2016.09.004 ↗
4. 10.1021/acs.jpcc.3c0348210.1021/acs.jpcc.3c03482 ↗
5. 10.1016/j.mser.2010.07.00110.1016/j.mser.2010.07.001 ↗
6. 10.1002/adom.20190199310.1002/adom.201901993 ↗
7. 10.1016/S1002-0721(10)60390-010.1016/S1002-0721(10)60390-0 ↗
8. 10.1016/j.matt.2022.04.00910.1016/j.matt.2022.04.009 ↗
9. 10.1039/D0TC06043G10.1039/D0TC06043G ↗
10. 10.1016/j.ceramint.2022.08.24710.1016/j.ceramint.2022.08.247 ↗
11. 10.1016/j.jlumin.2023.12005310.1016/j.jlumin.2023.120053 ↗
12. 10.1016/j.pnsc.2022.09.01210.1016/j.pnsc.2022.09.012 ↗
13. 10.1039/D1TC03317D10.1039/D1TC03317D ↗
14. 10.1016/j.actbio.2022.06.00610.1016/j.actbio.2022.06.006 ↗
15. 10.1039/C5RA16986K10.1039/C5RA16986K ↗
16. 10.1016/j.jallcom.2022.16446210.1016/j.jallcom.2022.164462 ↗
17. 10.1039/D2NJ01105K10.1039/D2NJ01105K ↗
18. 10.1016/j.ceramint.2016.10.11410.1016/j.ceramint.2016.10.114 ↗
19. 10.1016/j.pmatsci.2019.10062210.1016/j.pmatsci.2019.100622 ↗
20. 10.1016/j.cej.2021.13174410.1016/j.cej.2021.131744 ↗
21. 10.1557/s43579-022-00227-z10.1557/s43579-022-00227-z ↗
22. 10.1016/j.jallcom.2020.15399410.1016/j.jallcom.2020.153994 ↗
23. 10.1039/D2RA04705E10.1039/D2RA04705E ↗
24. 10.1515/nanoph-2020-013610.1515/nanoph-2020-0136 ↗
25. 10.3390/ma1318416510.3390/ma13184165 ↗
26. 10.1016/j.snb.2008.01.06510.1016/j.snb.2008.01.065 ↗
27. 10.4028/www.scientific.net/SSP.213.16510.4028/www.scientific.net/SSP.213.165 ↗
28. 10.1016/j.matpr.2020.04.12410.1016/j.matpr.2020.04.124 ↗
29. 10.1016/j.jallcom.2021.16269410.1016/j.jallcom.2021.162694 ↗
30. 10.1016/j.jallcom.2023.17235310.1016/j.jallcom.2023.172353 ↗
31. 10.1016/j.saa.2020.11850110.1016/j.saa.2020.118501 ↗
32. 10.1016/j.jssc.2020.12157610.1016/j.jssc.2020.121576 ↗
33. 10.1016/0022-3697(65)90213-110.1016/0022-3697(65)90213-1 ↗
34. 10.1039/D0CP04596A10.1039/D0CP04596A ↗
35. 10.1016/j.matchemphys.2023.12801710.1016/j.matchemphys.2023.128017 ↗
36. 10.1016/j.mtcomm.2022.10339010.1016/j.mtcomm.2022.103390 ↗
37. 10.1016/j.est.2022.10531410.1016/j.est.2022.105314 ↗
38. 10.1021/acs.jpclett.1c0304710.1021/acs.jpclett.1c03047 ↗
39. 10.1016/j.jallcom.2019.15338110.1016/j.jallcom.2019.153381 ↗
40. 10.1016/j.cej.2020.12594410.1016/j.cej.2020.125944 ↗
41. 10.1016/j.jallcom.2024.17396310.1016/j.jallcom.2024.173963 ↗
42. 10.1002/aenm.20190383310.1002/aenm.201903833 ↗
43. 10.1016/j.carbpol.2021.11838610.1016/j.carbpol.2021.118386 ↗
44. 10.1016/j.inoche.2023.11134110.1016/j.inoche.2023.111341 ↗
45. 10.1016/j.matlet.2021.13092910.1016/j.matlet.2021.130929 ↗
46. 10.1016/j.jlumin.2021.11843310.1016/j.jlumin.2021.118433 ↗
47. 10.1016/j.mtchem.2022.10101310.1016/j.mtchem.2022.101013 ↗
48. 10.1016/j.ceramint.2020.08.25910.1016/j.ceramint.2020.08.259 ↗
49. 10.1039/C6RA20442B10.1039/C6RA20442B ↗
50. 10.1002/chem.20200190810.1002/chem.202001908 ↗
51. Sahiner N. · Carbohydr. Polym. · 2021 · 277 · 1
52. 10.1016/j.ceramint.2023.10.14910.1016/j.ceramint.2023.10.149 ↗
53. 10.1016/j.ceramint.2020.04.17310.1016/j.ceramint.2020.04.173 ↗
54. 10.1021/acs.inorgchem.0c0268410.1021/acs.inorgchem.0c02684 ↗
55. 10.1016/j.ceramint.2022.10.21410.1016/j.ceramint.2022.10.214 ↗
56. 10.1016/j.ceramint.2020.06.20510.1016/j.ceramint.2020.06.205 ↗
57. Cao T. M. D. · Proc. Conversation Biomol. Stereodyn., 11th · 2020 · 1210
58. 10.1016/j.optmat.2020.11005010.1016/j.optmat.2020.110050 ↗
59. 10.1016/j.cej.2019.12390610.1016/j.cej.2019.123906 ↗
60. 10.1016/j.molstruc.2019.12764710.1016/j.molstruc.2019.127647 ↗
61. 10.1016/j.jlumin.2020.11719210.1016/j.jlumin.2020.117192 ↗
62. 10.1016/j.ceramint.2020.02.21010.1016/j.ceramint.2020.02.210 ↗
63. 10.1016/j.jlumin.2022.11896210.1016/j.jlumin.2022.118962 ↗
64. 10.1021/acs.jpclett.0c0061910.1021/acs.jpclett.0c00619 ↗