Electrically Conductive Dense and Porous Alumina with In‐Situ‐Synthesized Nanoscale Carbon Networks
Source abstract
Abstract
Electrically conductive dense and porous alumina compacts are fabricated by sintering dried gel-cast alumina samples with a homogeneous gel-binder distribution under an argon atmosphere. Sintering at an optimal temperature of 1700 °C leads to the uniform formation of electrically conductive nanoscale graphitic conduits throughout the composite, as shown in the figure.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Advanced ceramic materials synthesis · Aerogels and thermal insulation · Glass properties and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (39)
Show source-provided references
1. 10.1016/j.jmatprotec.2003.11.05510.1016/j.jmatprotec.2003.11.055 ↗
2. 10.1007/s11664-001-0200-210.1007/s11664-001-0200-2 ↗
3. 10.1016/0360-1285(96)00001-910.1016/0360-1285(96)00001-9 ↗
4. 10.1016/S0926-860X(01)00818-310.1016/S0926-860X(01)00818-3 ↗
5. 10.1088/0953-2048/16/5/31110.1088/0953-2048/16/5/311 ↗
6. S. Y.Hong K.Ku C. H.Ra B.Shi K.Do US Patent5 668 070 1997.
7. G.Zhan J. D.Kuntz A. K.Mukherjee US Patent6 875 374 2005.
8. 10.1007/BF0035779910.1007/BF00357799 ↗
9. 10.1016/j.msec.2003.09.08510.1016/j.msec.2003.09.085 ↗
10. P. K. T.Liu R. K.Bergstrom D. G.Gatty US Patent4 795 735 1989.
11. 10.1016/j.actamat.2003.10.03810.1016/j.actamat.2003.10.038 ↗
12. 10.1111/j.1744-7402.2004.tb00166.x10.1111/j.1744-7402.2004.tb00166.x ↗
13. 10.1063/1.160051110.1063/1.1600511 ↗
14. 10.1111/j.1551-2916.2005.00774.x10.1111/j.1551-2916.2005.00774.x ↗
15. 10.1016/j.powtec.2007.03.03610.1016/j.powtec.2007.03.036 ↗
16. 10.1111/j.1151-2916.2002.tb00337.x10.1111/j.1151-2916.2002.tb00337.x ↗
17. 10.1007/s10853-007-2155-z10.1007/s10853-007-2155-z ↗
18. 10.1111/j.1151-2916.1991.tb04068.x10.1111/j.1151-2916.1991.tb04068.x ↗
19. 10.1016/S0955-2219(99)00024-210.1016/S0955-2219(99)00024-2 ↗
20. 10.1111/j.1151-2916.1999.tb01795.x10.1111/j.1151-2916.1999.tb01795.x ↗
21. 10.1002/adma.20030624110.1002/adma.200306241 ↗
22. Menchavez R. L. · J. Eur. Ceram. Soc.
23. 10.1016/j.matlet.2006.05.07210.1016/j.matlet.2006.05.072 ↗
24. 10.1016/S0008-6223(03)00048-410.1016/S0008-6223(03)00048-4 ↗
25. 10.1016/0955-2219(95)00186-710.1016/0955-2219(95)00186-7 ↗
26. 10.1016/S0955-2219(99)00065-510.1016/S0955-2219(99)00065-5 ↗
27. 10.1007/BF0059146410.1007/BF00591464 ↗
28. Ryabkov Y. I. · Russ. J. Gen. Chem. · 2002 · 72 · 181
29. 10.1111/j.1151-2916.1989.tb06306.x10.1111/j.1151-2916.1989.tb06306.x ↗
30. 10.4028/www.scientific.net/MSF.561-565.212310.4028/www.scientific.net/MSF.561-565.2123 ↗
31. 10.1139/v63-09510.1139/v63-095 ↗
32. 10.1149/1.211384710.1149/1.2113847 ↗
33. 10.1007/s10853-006-4496-410.1007/s10853-006-4496-4 ↗
34. Cohen J. · Am. Ceram. Bull. · 1959 · 38 · 441
35. Palilla F. C. · Am. Ceram. Bull. · 1985 · 64 · 580
36. Bondar A. M. · J. Optoelectron. Adv. Mater. · 2006 · 8 · 631
37. 10.1111/j.1551-2916.2005.00539.x10.1111/j.1551-2916.2005.00539.x ↗
38. van der Pauw L. J. · Philips Res. Rep. · 1958 · 13 · 1
39. 10.1088/0957-0233/3/9/01910.1088/0957-0233/3/9/019 ↗