Highly Size‐Selective Ionically Crosslinked Multilayer Polymer Films for Light Gas Separation
Source abstract
Abstract
Exceptionally high hydrogen permselectivity, exceeding that of any polymeric or porous inorganic systems, is achieved using an ionically crosslinked multilayer polymer thin film. As a service to our authors and readers, this journal provides supporting information supplied by the authors. Such materials are peer reviewed and may be re-organized for online delivery, but are not copy-edited or typeset. Technical support issues arising from supporting information (other than missing files) should be addressed to the authors. Please note: The publisher is not responsible for the content or functionality of any supporting information supplied by the authors. Any queries (other than missing content) should be directed to the corresponding author for the article.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Membrane Separation and Gas Transport · Covalent Organic Framework Applications · Ammonia Synthesis and Nitrogen Reduction
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Artie McFerrin Department of Chemical Engineering Texas A&M University 3122 TAMU College Station TX 77843–3122 United States
Fire Division, National Institute of standards and Technology (NIST) 100 Bureau Drive, Stop 1070 Gaithersburg MD 20899 United States
Department of Mechanical Engineering Texas A&M University 3123 TAMU College Station TX 77843–3123 United States
References (70)
Show source-provided references
1. 10.1016/S1093-0191(01)00112-510.1016/S1093-0191(01)00112-5 ↗
2. 10.1021/ef070044u10.1021/ef070044u ↗
3. Jochem E. · 2003
4. 10.1021/cr050179210.1021/cr0501792 ↗
5. 10.1021/ie801903210.1021/ie8019032 ↗
6. 10.1016/0376-7388(91)80060-J10.1016/0376-7388(91)80060-J ↗
7. 10.1016/j.memsci.2008.04.03010.1016/j.memsci.2008.04.030 ↗
8. 10.1021/ma981454810.1021/ma9814548 ↗
9. 10.1016/j.carbon.2003.10.02210.1016/j.carbon.2003.10.022 ↗
10. 10.1002/anie.20060491010.1002/anie.200604910 ↗
11. 10.1021/ie202038m10.1021/ie202038m ↗
12. 10.1126/science.113991510.1126/science.1139915 ↗
13. 10.1126/science.109204810.1126/science.1092048 ↗
14. 10.1016/j.progpolymsci.2007.01.00810.1016/j.progpolymsci.2007.01.008 ↗
15. 10.1002/anie.20100614110.1002/anie.201006141 ↗
16. 10.1021/ma100639610.1021/ma1006396 ↗
17. 10.1126/science.122803210.1126/science.1228032 ↗
18. 10.1126/science.114674410.1126/science.1146744 ↗
19. 10.1021/cm702239k10.1021/cm702239k ↗
20. 10.1126/science.277.5330.123210.1126/science.277.5330.1232 ↗
21. 10.1039/b700410a10.1039/b700410a ↗
22. 10.1002/(SICI)1521-3927(20000401)21:7<319::AID-MARC319>3.0.CO;2-710.1002/(SICI)1521-3927(20000401)21:7<319::AID-MARC319>3.0.CO;2-7 ↗
23. 10.1021/cm001175a10.1021/cm001175a ↗
24. 10.1126/science.114317610.1126/science.1143176 ↗
25. 10.1021/ja00127a02610.1021/ja00127a026 ↗
26. 10.1016/j.biomaterials.2003.08.03910.1016/j.biomaterials.2003.08.039 ↗
27. 10.1021/la302488710.1021/la3024887 ↗
28. 10.1002/adma.20110187110.1002/adma.201101871 ↗
29. 10.1021/ma102612710.1021/ma1026127 ↗
30. 10.1039/b701203a10.1039/b701203a ↗
31. 10.1021/cm020639x10.1021/cm020639x ↗
32. 10.1021/ie50670a00710.1021/ie50670a007 ↗
33. Baker R. W. · 1991
34. 10.1021/ma060629810.1021/ma0606298 ↗
35. 10.1021/ma800732j10.1021/ma800732j ↗
36. 10.1021/ma011293z10.1021/ma011293z ↗
37. 10.1021/ma048596o10.1021/ma048596o ↗
38. 10.1002/polb.2172310.1002/polb.21723 ↗
39. 10.1021/ma961245s10.1021/ma961245s ↗
40. 10.1039/c1cc14051e10.1039/c1cc14051e ↗
41. 10.1021/la102409e10.1021/la102409e ↗
42. 10.1021/ja907359t10.1021/ja907359t ↗
43. 10.1016/j.micromeso.2009.03.03610.1016/j.micromeso.2009.03.036 ↗
44. 10.1021/cm902032y10.1021/cm902032y ↗
45. 10.1021/la200103w10.1021/la200103w ↗
46. 10.1039/b924536g10.1039/b924536g ↗
47. 10.1016/j.memsci.2007.09.03510.1016/j.memsci.2007.09.035 ↗
48. 10.1016/S0376-7388(97)00120-810.1016/S0376-7388(97)00120-8 ↗
49. 10.1016/S0011-9164(02)00476-910.1016/S0011-9164(02)00476-9 ↗
50. 10.1016/S0376-7388(97)00008-210.1016/S0376-7388(97)00008-2 ↗
51. 10.1016/j.memsci.2007.06.06210.1016/j.memsci.2007.06.062 ↗
52. 10.1016/j.memsci.2010.06.01710.1016/j.memsci.2010.06.017 ↗
53. 10.1016/j.memsci.2007.07.01010.1016/j.memsci.2007.07.010 ↗
54. 10.1016/j.memsci.2008.01.03110.1016/j.memsci.2008.01.031 ↗
55. 10.1016/j.memsci.2010.12.03910.1016/j.memsci.2010.12.039 ↗
56. 10.1016/j.memsci.2012.09.03510.1016/j.memsci.2012.09.035 ↗
57. 10.1016/j.memsci.2005.01.00910.1016/j.memsci.2005.01.009 ↗
58. 10.1021/ma901430q10.1021/ma901430q ↗
59. 10.1002/adma.20120239310.1002/adma.201202393 ↗
60. 10.1016/j.ijhydene.2009.07.11510.1016/j.ijhydene.2009.07.115 ↗
61. 10.1021/ma702360p10.1021/ma702360p ↗
62. 10.1016/j.memsci.2008.12.00510.1016/j.memsci.2008.12.005 ↗
63. 10.1016/j.ijhydene.2011.08.06010.1016/j.ijhydene.2011.08.060 ↗
64. 10.1016/j.memsci.2011.02.02710.1016/j.memsci.2011.02.027 ↗
65. 10.1016/j.ijhydene.2011.03.14610.1016/j.ijhydene.2011.03.146 ↗
66. 10.1016/j.memsci.2009.12.02610.1016/j.memsci.2009.12.026 ↗
67. 10.1016/j.memsci.2011.10.03110.1016/j.memsci.2011.10.031 ↗
68. 10.1063/1.208444710.1063/1.2084447 ↗
69. 10.1063/1.331008810.1063/1.3310088 ↗
70. ASTM D3985–02 Standard Test Method for Oxygen Gas Transmission Rate Through Plastic Film and Sheeting Using a Coulometric Sensor West Conshohocken PA 2002.