Surface damage on new AS60 rail caused by wheel slip
Source abstract
Abstract
A metallurgical investigation was carried out of new AS60 rail samples, subjected to severe wheel slip, which caused skid marks on the rail crown, 10-18. mm wide. Sections, studied using optical and scanning electron microscopy revealed that the surface damage was a white etching layer (WEL). The WEL had a high hardness of 884. HV consistent with martensite. The microstructure was consistent with wheel slip causing severe plastic deformation of the rail surface, and the heat generated caused a transformation to austenite, which was quenched to martensite by the steel of the cold bulk rail extracting heat from the hot surface. The WEL depths in two samples were measured to be between ~230 and 310. μm. This is indicative that there was more heat available in one sample to produce a thicker martensite layer. This is attributed to more intense wheel slip in that rail.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Metal Alloys Wear and Properties · Railway Engineering and Dynamics · Microstructure and Mechanical Properties of Steels
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (39)
Show source-provided references
1. A transmission electron microscopy study of the white-etching layer on a rail head10.1016/0025-5416(84)90180-0 ↗
2. Microscopic investigation of surface layers on rails10.1016/j.apsusc.2004.05.289 ↗
3. Investigation of white etching layers on rails by optical microscopy, electron microscopy, X-ray and synchrotron X-ray diffraction10.1016/S0921-5093(00)01842-6 ↗
4. Nanostructure formation on the surface of railway tracks10.1016/S0921-5093(00)01947-X ↗
5. Formation of white-etching layers on rail treads10.1016/0043-1648(95)06733-7 ↗
6. Influential microstructural changes on rolling contact fatigue crack initiation in pearlitic rail steels10.1179/174328405X43207 ↗
7. Structure and properties of white layers formed at high velocities of friction10.1007/BF00754768 ↗
8. White layers and thermal modeling of hard turned surfaces10.1016/S0890-6955(99)00036-X ↗
9. Surface modification, corrugation and nanostructure formation of high speed railway tracks10.1016/S0965-9773(97)00162-1 ↗
10. Microstructural investigation of white etching layer on pearlite steel rail10.1016/j.msea.2006.01.033 ↗
11. The metallography of worn surfaces and some theories of wear10.1016/0043-1648(78)90254-5 ↗
12. Smallman · 1985
13. Isothermal martensitic transformation as an internal-stress-increasing process10.1051/jp4:1995823 ↗
14. The characterization of white layers formed on digger teeth10.1016/0043-1648(93)90123-4 ↗
15. Abrasive wear and its application to digger teeth10.1016/0301-679X(85)90104-5 ↗
16. The flash temperature concept10.1016/0043-1648(63)90283-7 ↗
17. Moving sources of heat and temperature at sliding
18. The temperature of rubbing surfaces10.1016/0043-1648(59)90159-0 ↗
19. Determination of temperatures for sliding contact with applications for wheel–rail systems10.1016/0043-1648(95)06666-7 ↗
20. On the temperature in the wheel–rail rolling contact∗10.1046/j.1460-2695.2003.00700.x ↗
21. Temperature rise due to slip between wheel and rail–an analytical solution for hertzian contact10.1016/0043-1648(80)90293-8 ↗
22. Pau M, Aymerich F, Ginesu F, Ishida M, Chen H. Evaluation of the influence of surface conditions on wheel–rail contact performances. In: World Congress of Railway Research (WCRR), Cologne; 2001.
23. Surface analysis of corrugated rail treads10.1016/0043-1648(91)90012-J ↗
24. The role of deformed rail microstructure on rolling contact fatigue initiation10.1016/j.wear.2008.02.042 ↗
25. Nano structure and transformation mechanism of white layer for AISI1045 steel during impact wear10.1016/j.wear.2004.06.002 ↗
26. Decarburisation and rolling contact fatigue of a rail steel10.1016/j.wear.2005.03.005 ↗
27. Rail rolling contact fatigue research by the European Rail Research Institute10.1016/0043-1648(95)06650-0 ↗
28. Introduction to the damage tolerance behaviour of railway rails – a review10.1016/j.engfracmech.2009.09.003 ↗
29. Rail rolling contact fatigue. The performance of naturally hard and head-hardened rails in track10.1016/0043-1648(95)06702-7 ↗
30. Tribological layers and the wear of ductile materials10.1016/S0043-1648(00)00480-4 ↗
31. Computer simulation of wear and rolling contact fatigue10.1016/S0043-1648(01)00732-3 ↗
32. Computer simulation of strain accumulation and hardening for pearlitic rail steel undergoing repeated contact10.1243/0309324041223935 ↗
33. Wang · 2002
34. Alleviation of rolling contact fatigue on Sweden’s heavy haul railway10.1016/S0043-1648(02)00081-9 ↗
35. Worth AW, Hornaday JR, Richards PR. Prolonging rail life through rail grinding. In: Third international heavy haul railway conference, Vancouver; 1986.
36. Lamson ST, Roney MD. Development of rail profile grinding on CP Rail. In: Third international heavy haul railway conference, Vancouver; 1986.
37. Australian Standard: Railway track materials – Part 1: Steel Rails (AS1085.1-2002): North Sydney.
38. Hardness of tempered martensite in carbon and low-alloy steels10.1007/BF02646882 ↗
39. Rolling contact fatigue of white etching layer: Part 1: crack morphology10.1016/j.wear.2007.01.003 ↗