Surface‐Roughness‐Induced Plasticity in a Biodegradable Zn Alloy
Source abstract
Abstract
Abstract Improving plasticity has been an eternal theme of developing metallic materials. It is difficult to increase room‐temperature elongation of metallic materials over 100% without sacrificing strength using existing methods. Herein, surface‐roughness‐induced plasticity (SRIP) is discovered in biodegradable Zn–0.4Mn alloy. Surprisingly, in the good surface range that meets the international standard ISO 6892, reducing surface roughness results in significant increase in plasticity without loss of strength. From unground to 5000# sandpaper ground states, the surface roughness Ra of the alloy decreases from 0.63 to 0.05 µm, while its room temperature elongation increases from 74% to 143%. SRIP is the synergistic result of increased microstructure damage tolerance and decreased surface roughness. It provides a new method for improving plasticity.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: Magnesium Alloys: Properties and Applications · Corrosion Behavior and Inhibition · Microstructure and mechanical properties
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Beijing Advanced Innovation Center for Materials Genome Engineering School of Materials Science and Engineering University of Science and Technology Beijing 30 Xueyuan Road, Haidian District Beijing 100083 P. R. China
Funding
National Natural Science Foundation of China · Fundamental Research Funds for the Central Universities
References (55)
Show source-provided references
1. 10.1007/s10853-009-3780-510.1007/s10853-009-3780-5 ↗
2. 10.1016/j.actamat.2022.11776610.1016/j.actamat.2022.117766 ↗
3. 10.1016/j.actamat.2020.07.04210.1016/j.actamat.2020.07.042 ↗
4. 10.1016/j.actamat.2016.09.05410.1016/j.actamat.2016.09.054 ↗
5. 10.1126/science.287.5457.146310.1126/science.287.5457.1463 ↗
6. 10.1016/j.msea.2018.03.05210.1016/j.msea.2018.03.052 ↗
7. 10.1016/j.actamat.2020.10.01610.1016/j.actamat.2020.10.016 ↗
8. Zhang C. · Mater. Sci. Eng. A · 2020 · 794
9. 10.1016/j.msea.2020.14002310.1016/j.msea.2020.140023 ↗
10. Naghizadeh M. · Steel Res. Int. · 2019 · 90
11. 10.1016/j.actamat.2017.06.04610.1016/j.actamat.2017.06.046 ↗
12. 10.1016/j.scriptamat.2020.06.02910.1016/j.scriptamat.2020.06.029 ↗
13. 10.1126/science.abe725210.1126/science.abe7252 ↗
14. 10.1016/j.scriptamat.2019.02.01810.1016/j.scriptamat.2019.02.018 ↗
15. 10.1126/science.abj811410.1126/science.abj8114 ↗
16. 10.1016/j.actbio.2020.02.02410.1016/j.actbio.2020.02.024 ↗
17. 10.1021/acsami.8b2063410.1021/acsami.8b20634 ↗
18. 10.1016/j.actbio.2019.08.01210.1016/j.actbio.2019.08.012 ↗
19. 10.1016/j.biomaterials.2021.12130110.1016/j.biomaterials.2021.121301 ↗
20. 10.1016/j.msec.2017.04.02310.1016/j.msec.2017.04.023 ↗
21. 10.1016/j.actbio.2018.10.01510.1016/j.actbio.2018.10.015 ↗
22. 10.1016/j.matdes.2018.02.04910.1016/j.matdes.2018.02.049 ↗
23. 10.1016/j.actbio.2020.03.00910.1016/j.actbio.2020.03.009 ↗
24. 10.1016/j.jmst.2020.10.07610.1016/j.jmst.2020.10.076 ↗
25. 10.1016/j.msea.2019.13854310.1016/j.msea.2019.138543 ↗
26. 10.1016/j.mattod.2019.09.02310.1016/j.mattod.2019.09.023 ↗
27. 10.1016/j.ijfatigue.2020.10587910.1016/j.ijfatigue.2020.105879 ↗
28. 10.1016/j.jnucmat.2020.15206510.1016/j.jnucmat.2020.152065 ↗
29. 10.1016/j.jnucmat.2011.11.04310.1016/j.jnucmat.2011.11.043 ↗
30. 10.1016/j.scriptamat.2010.11.01910.1016/j.scriptamat.2010.11.019 ↗
31. 10.1038/s41467-017-01330-910.1038/s41467-017-01330-9 ↗
32. 10.1016/j.msec.2020.11117210.1016/j.msec.2020.111172 ↗
33. 10.1016/j.msea.2015.07.04110.1016/j.msea.2015.07.041 ↗
34. 10.1016/j.msea.2019.01.08910.1016/j.msea.2019.01.089 ↗
35. 10.1016/j.msea.2019.05.02910.1016/j.msea.2019.05.029 ↗
36. 10.1007/BF0034994110.1007/BF00349941 ↗
37. 10.1016/j.jallcom.2020.15842510.1016/j.jallcom.2020.158425 ↗
38. 10.1016/j.msea.2022.14385010.1016/j.msea.2022.143850 ↗
39. 10.1016/j.msea.2022.14377510.1016/j.msea.2022.143775 ↗
40. 10.1016/j.msea.2021.14180910.1016/j.msea.2021.141809 ↗
41. 10.1016/j.matchar.2022.11192810.1016/j.matchar.2022.111928 ↗
42. 10.1016/j.matdes.2019.10815410.1016/j.matdes.2019.108154 ↗
43. 10.1016/j.mechmat.2021.10410310.1016/j.mechmat.2021.104103 ↗
44. 10.1016/j.bioactmat.2021.03.01710.1016/j.bioactmat.2021.03.017 ↗
45. 10.1016/j.msea.2017.06.03710.1016/j.msea.2017.06.037 ↗
46. 10.1002/adem.20150006810.1002/adem.201500068 ↗
47. 10.1016/j.pmatsci.2018.02.00210.1016/j.pmatsci.2018.02.002 ↗
48. 10.1016/j.actamat.2019.07.02610.1016/j.actamat.2019.07.026 ↗
49. 10.1016/j.scriptamat.2020.08.03810.1016/j.scriptamat.2020.08.038 ↗
50. 10.1038/s41467-021-24939-310.1038/s41467-021-24939-3 ↗
51. 10.1126/science.115961010.1126/science.1159610 ↗
52. 10.1016/j.msea.2015.04.00410.1016/j.msea.2015.04.004 ↗
53. 10.1016/j.actamat.2022.11824310.1016/j.actamat.2022.118243 ↗
54. 10.1016/j.msea.2019.01.11710.1016/j.msea.2019.01.117 ↗
55. 10.1016/j.jallcom.2022.16587110.1016/j.jallcom.2022.165871 ↗