Room Temperature Homogeneous Ductility of Micrometer‐Sized Metallic Glass
Source abstract
Abstract
Homogeneous ductile flow of metallic glasses is observed at the micrometer scale. It is shown that this unusual deformation mode of an otherwise brittle material depends on both specimen size and applied loading rate. The results are explained by intrinsic length-scale effects of nanometer-sized defects, and provide a rationale for the long term debated brittle-to-ductile transition of amorphous metals.
Source: europepmc · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Metallic Glasses and Amorphous Alloys · Cultural Heritage Materials Analysis · Glass properties and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
University of Göttingen Institute of Materials Physics Friedrich‐Hund‐Platz 1 37077 Göttingen Germany
References (49)
Show source-provided references
1. 10.1016/j.actamat.2007.01.05210.1016/j.actamat.2007.01.052 ↗
2. 10.2320/matertrans.43.189210.2320/matertrans.43.1892 ↗
3. 10.1063/1.12427310.1063/1.124273 ↗
4. 10.1002/adma.20100214810.1002/adma.201002148 ↗
5. 10.1126/science.120136210.1126/science.1201362 ↗
6. 10.1016/0001-6160(81)90177-210.1016/0001-6160(81)90177-2 ↗
7. 10.1016/j.actamat.2009.06.01310.1016/j.actamat.2009.06.013 ↗
8. 10.1063/1.481174410.1063/1.4811744 ↗
9. 10.1103/PhysRevLett.107.18550210.1103/PhysRevLett.107.185502 ↗
10. 10.1016/j.actamat.2011.01.06010.1016/j.actamat.2011.01.060 ↗
11. 10.1063/1.368487110.1063/1.3684871 ↗
12. 10.1063/1.360231510.1063/1.3602315 ↗
13. 10.1016/j.intermet.2004.04.03310.1016/j.intermet.2004.04.033 ↗
14. 10.1038/nature0659810.1038/nature06598 ↗
15. 10.1080/0950083050008047410.1080/09500830500080474 ↗
16. 10.1080/1478643070176261910.1080/14786430701762619 ↗
17. 10.2320/matertrans.MRA200834210.2320/matertrans.MRA2008342 ↗
18. 10.1063/1.288458410.1063/1.2884584 ↗
19. 10.1016/j.ijplas.2010.09.01010.1016/j.ijplas.2010.09.010 ↗
20. 10.1016/j.actamat.2009.08.07010.1016/j.actamat.2009.08.070 ↗
21. 10.1016/j.scriptamat.2012.05.01910.1016/j.scriptamat.2012.05.019 ↗
22. 10.1016/j.pmatsci.2011.01.00510.1016/j.pmatsci.2011.01.005 ↗
23. 10.1038/nmat198410.1038/nmat1984 ↗
24. 10.1016/j.actamat.2008.06.02810.1016/j.actamat.2008.06.028 ↗
25. 10.1016/j.scriptamat.2008.12.01310.1016/j.scriptamat.2008.12.013 ↗
26. 10.1557/jmr.2011.17810.1557/jmr.2011.178 ↗
27. 10.1038/srep0109610.1038/srep01096 ↗
28. 10.1016/0001-6160(87)90047-210.1016/0001-6160(87)90047-2 ↗
29. 10.1016/0036-9748(83)90099-610.1016/0036-9748(83)90099-6 ↗
30. 10.1063/1.479356210.1063/1.4793562 ↗
31. 10.1063/1.158255510.1063/1.1582555 ↗
32. 10.1016/j.pmatsci.2010.04.00210.1016/j.pmatsci.2010.04.002 ↗
33. 10.1016/j.actamat.2010.06.05410.1016/j.actamat.2010.06.054 ↗
34. 10.1016/S1359-6454(03)00164-210.1016/S1359-6454(03)00164-2 ↗
35. 10.1016/j.actamat.2008.10.02710.1016/j.actamat.2008.10.027 ↗
36. 10.1016/j.mser.2013.04.00110.1016/j.mser.2013.04.001 ↗
37. 10.1103/PhysRevLett.105.03550110.1103/PhysRevLett.105.035501 ↗
38. 10.1103/PhysRevLett.104.20570110.1103/PhysRevLett.104.205701 ↗
39. 10.1016/j.actamat.2006.05.02410.1016/j.actamat.2006.05.024 ↗
40. 10.1016/j.actamat.2009.07.01610.1016/j.actamat.2009.07.016 ↗
41. 10.1016/S1359-6462(97)00105-X10.1016/S1359-6462(97)00105-X ↗
42. 10.1016/S1359-6462(98)00163-810.1016/S1359-6462(98)00163-8 ↗
43. 10.1073/pnas.080605110510.1073/pnas.0806051105 ↗
44. 10.1016/j.ijplas.2007.01.01510.1016/j.ijplas.2007.01.015 ↗
45. 10.1557/jmr.2006.026610.1557/jmr.2006.0266 ↗
46. 10.1016/j.jmps.2008.01.00810.1016/j.jmps.2008.01.008 ↗
47. 10.1080/14786435.2013.82639610.1080/14786435.2013.826396 ↗
48. 10.1103/PhysRevB.80.18420310.1103/PhysRevB.80.184203 ↗
49. 10.1103/PhysRevLett.95.19550110.1103/PhysRevLett.95.195501 ↗