journal article·2013-04-24

Structural and Electronic Reconstructions at the LaAlO3/SrTiO3 Interface

M. Salluzzo, S. Gariglio, X. Torrelles, Z. Ristic, R. Di Capua, J. Drnec, M. Moretti Sala, G. Ghiringhelli, R. Felici, N. B. Brookes

Advanced Materials· Volume 25· Issue 16
Publisher page

Abstract

A full understanding of the mechanism of the formation of a two-dimensional electron gas (2DEG) at the interface between insulating LaAlO3 (LAO) thin films and bulk SrTiO3 (STO) crystals is a prerequisite for the full exploitation of this class of materials. Here, by using a combination of advanced X-ray synchrotron-based spectroscopic and structural measurements, it is shown that a structural and electronic reconstruction of the interface occurs before the realization of the 2DEG.
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: Electronic and Structural Properties of Oxides · Magnetic and transport properties of perovskites and related materials · Semiconductor materials and devices

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (33)

Show source-provided references
1. 10.1146/annurev-conmatphys-062910-14044510.1146/annurev-conmatphys-062910-140445 ↗
2. 10.1038/nature0230810.1038/nature02308 ↗
3. 10.1126/science.118186210.1126/science.1181862 ↗
4. 10.1038/nature0972010.1038/nature09720 ↗
5. 10.1038/nmat294310.1038/nmat2943 ↗
6. 10.1103/PhysRevB.86.15542510.1103/PhysRevB.86.155425 ↗
7. 10.1103/PhysRevLett.102.16680410.1103/PhysRevLett.102.166804 ↗
8. While oxygen vacancies could be created by the fracturing process still there is no direct proof that oxygen vacancies are created in a such a density which might explain the experimental results.
9. 10.1038/nmat156910.1038/nmat1569 ↗
10. 10.1088/0953-8984/22/4/04300110.1088/0953-8984/22/4/043001 ↗
11. 10.1126/science.113109110.1126/science.1131091 ↗
12. 10.1103/PhysRevLett.107.05610210.1103/PhysRevLett.107.056102 ↗
13. 10.1103/PhysRevLett.106.16680710.1103/PhysRevLett.106.166807 ↗
14. 10.1103/PhysRevLett.106.03610110.1103/PhysRevLett.106.036101 ↗
15. 10.1103/PhysRevB.80.07511010.1103/PhysRevB.80.075110 ↗
16. 10.1103/PhysRevB.83.15540510.1103/PhysRevB.83.155405 ↗
17. 10.1103/PhysRevLett.107.03610410.1103/PhysRevLett.107.036104 ↗
18. 10.1209/0295-5075/91/1700410.1209/0295-5075/91/17004 ↗
19. 10.1103/PhysRevB.41.92810.1103/PhysRevB.41.928 ↗
20. To rescale the calculated XLD spectra we used the ratio between the contribution to the total signal of the first STO 6 unit cells and the remaining part of the sample i.e. 1‐exp(‐6 cSTO/d) = 0.48 (d = 4 nm is the TEY probing depth). The data are quantitatively reproduced using the following parameters: 10Dq = 2.22 eV t2gsplitting 50 meV eg splitting 100 meV.
21. This result shows that the electrons transferred at the interface partially occupy states that do not have a pure 3d1character and in particular bands associated to the hybridization between O2p and Ti3d orbitals. Indeed these spectra can be equally reproduced introducing explicitly p‐d charge transfer effects in the atomic multiplet calculations for a 3d0system.
22. Vlieg E. · J. Appl. Crystallogr. · 1998 · 31
23. 10.1063/1.277997210.1063/1.2779972 ↗
24. 10.1103/PhysRevB.86.04512710.1103/PhysRevB.86.045127 ↗
25. 10.1103/PhysRevLett.99.15550210.1103/PhysRevLett.99.155502 ↗
26. 10.1103/PhysRevLett.102.10760210.1103/PhysRevLett.102.107602 ↗
27. 10.1103/PhysRevLett.106.13680310.1103/PhysRevLett.106.136803 ↗
28. 10.1002/adma.20120066710.1002/adma.201200667 ↗
29. 10.1103/PhysRevB.86.14010210.1103/PhysRevB.86.140102 ↗
30. 10.1016/S0039-6028(98)00670-010.1016/S0039-6028(98)00670-0 ↗
31. 10.1103/PhysRevB.62.1040910.1103/PhysRevB.62.10409 ↗
32. 10.1103/PhysRevB.77.19540810.1103/PhysRevB.77.195408 ↗
33. 10.1103/PhysRevLett.105.21760110.1103/PhysRevLett.105.217601 ↗