In Situ Control of Separate Electronic Phases on SrTiO₃ Surfaces by Oxygen Dosing

Insulating SrTiO3 (STO) can host 2D electron systems (2DESs) on its surfaces, caused by oxygen defects. This study shows that the STO surface exhibits phase separation once the 2DES is formed and relates this inhomogeneity to recently reported magnetic order at STO surfaces and interfaces. The results open pathways to exploit oxygen defects for engineering the electronic and magnetic properties of oxides. As a service to our authors and readers, this journal provides supporting information supplied by the authors. Such materials are peer reviewed and may be re-organized for online delivery, but are not copy-edited or typeset. Technical support issues arising from supporting information (other than missing files) should be addressed to the authors. Please note: The publisher is not responsible for the content or functionality of any supporting information supplied by the authors. Any queries (other than missing content) should be directed to the corresponding author for the article.