Transparent, Polycrystalline Upconverting Nanoceramics: Towards 3‐D Displays
Source abstract
Abstract
Transparent, polycrystalline (Y0.86-Yb0.11Er0.03)2O3 with an average grain size of 400 nm on irradiation with 980 nm laser light through a mask upconverts the IR photons emitting red light at 662 nm. A model for a red pixel in a 3-D inverted planetarium display is presented (see figure).
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Luminescence Properties of Advanced Materials · Random lasers and scattering media · Advanced Optical Imaging Technologies
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (47)
Show source-provided references
1. 10.1063/1.166200810.1063/1.1662008 ↗
2. 10.1111/j.1151-2916.1995.tb08433.x10.1111/j.1151-2916.1995.tb08433.x ↗
3. 10.1063/1.128903910.1063/1.1289039 ↗
4. 10.1146/annurev.matsci.36.011205.15292610.1146/annurev.matsci.36.011205.152926 ↗
5. 10.1111/j.1551-2916.2006.01043.x10.1111/j.1551-2916.2006.01043.x ↗
6. 10.1111/j.1151-2916.2000.tb01305.x10.1111/j.1151-2916.2000.tb01305.x ↗
7. 10.1007/s00340000039410.1007/s003400000394 ↗
8. 10.1111/j.1151-2916.2003.tb03270.x10.1111/j.1151-2916.2003.tb03270.x ↗
9. 10.1111/j.1151-2916.2003.tb03325.x10.1111/j.1151-2916.2003.tb03325.x ↗
10. 10.1111/j.1551-2916.2006.00985.x10.1111/j.1551-2916.2006.00985.x ↗
11. 10.1109/MSPEC.2005.141372810.1109/MSPEC.2005.1413728 ↗
12. 10.1021/cr020357g10.1021/cr020357g ↗
13. 10.1007/s10895-006-0085-910.1007/s10895-006-0085-9 ↗
14. 10.1021/ac051094410.1021/ac0510944 ↗
15. 10.1364/JOSAB.15.00099610.1364/JOSAB.15.000996 ↗
16. 10.1364/OL.28.00017310.1364/OL.28.000173 ↗
17. 10.1016/S0022-3093(02)01951-810.1016/S0022-3093(02)01951-8 ↗
18. 10.1021/jp021869210.1021/jp0218692 ↗
19. 10.1016/j.materresbull.2006.10.02410.1016/j.materresbull.2006.10.024 ↗
20. 20aE. A.Downing US Patent5684621 1997.
21. 10.1126/science.273.5279.118510.1126/science.273.5279.1185 ↗
22. Arbuthnot L. · SID' 96 Digest · 1996
23. 10.1111/j.1151-2916.1993.tb07757.x10.1111/j.1151-2916.1993.tb07757.x ↗
24. 10.1111/j.1151-2916.1997.tb03148.x10.1111/j.1151-2916.1997.tb03148.x ↗
25. 10.1111/j.1151-2916.1998.tb02307.x10.1111/j.1151-2916.1998.tb02307.x ↗
26. L. J.Hornbeck US Patent4596992 1986.
27. L. J.Hornbeck US Patent4662746 1987.
28. 10.1021/cm021782t10.1021/cm021782t ↗
29. 10.1021/cm021783l10.1021/cm021783l ↗
30. 10.1002/adma.20040100110.1002/adma.200401001 ↗
31. 10.1038/nmat171110.1038/nmat1711 ↗
32. 10.1002/adma.20070212410.1002/adma.200702124 ↗
33. Li S. · 2002 · 221
34. 10.1103/PhysRevA.65.01380710.1103/PhysRevA.65.013807 ↗
35. 10.1117/12.93640910.1117/12.936409 ↗
36. 10.1021/jp035583o10.1021/jp035583o ↗
37. 10.1364/AO.2.00067510.1364/AO.2.000675 ↗
38. 10.1364/OL.27.00039410.1364/OL.27.000394 ↗
39. 10.1016/S0141-9382(98)00046-810.1016/S0141-9382(98)00046-8 ↗
40. 10.1016/S0022-2313(02)00638-510.1016/S0022-2313(02)00638-5 ↗
41. Livanova L. D. · Sov. Phys. Solid State · 1969 · 11 · 750
42. 10.1149/1.183640710.1149/1.1836407 ↗
43. 10.1002/adma.20040204610.1002/adma.200402046 ↗
44. 10.1002/adma.20040077210.1002/adma.200400772 ↗
45. 10.1103/PhysRevB.73.15542210.1103/PhysRevB.73.155422 ↗
46. Laine R. M. · 2004 · 18
47. 10.1111/j.1151-2916.1998.tb02448.x10.1111/j.1151-2916.1998.tb02448.x ↗