Indirect Bandgap Puddles in Monolayer MoS2 by Substrate‐Induced Local Strain
Source abstract
Abstract
An unusually large bandgap modulation of 1.23–2.65 eV in monolayer MoS2 on a SiO2/Si substrate is found due to the inherent local bending strain induced by the surface roughness of the substrate, reaching the direct-to-indirect bandgap transition. Approximately 80% of the surface area reveals an indirect bandgap, which is confirmed further by the degraded photoluminescence compared to that from suspended MoS2. As a service to our authors and readers, this journal provides supporting information supplied by the authors. Such materials are peer reviewed and may be re-organized for online delivery, but are not copy-edited or typeset. Technical support issues arising from supporting information (other than missing files) should be addressed to the authors. Please note: The publisher is not responsible for the content or functionality of any supporting information supplied by the authors. Any queries (other than missing content) should be directed to the corresponding author for the article.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: 2D Materials and Applications · MXene and MAX Phase Materials · Graphene research and applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
Affiliations
Center for Integrated Nanostructure Physics (CINAP) Institute for Basic Science (IBS) Suwon 16419 South Korea
Sungkyunkwan University Suwon 16419 South Korea
Department of Energy Science Sungkyunkwan University Suwon 16419 South Korea
Department of Physics Sungkyunkwan University Suwon 16419 South Korea
Sungkyunkwan Advanced Institute of Nanotechnology Sungkyunkwan University Suwon 16419 South Korea
References (35)
Show source-provided references
1. 10.1038/nmat406110.1038/nmat4061 ↗
2. 10.1021/nl501988y10.1021/nl501988y ↗
3. 10.1021/nl501133c10.1021/nl501133c ↗
4. 10.1103/PhysRevB.86.24120110.1103/PhysRevB.86.241201 ↗
5. 10.1038/srep0660810.1038/srep06608 ↗
6. 10.1021/acs.nanolett.5b0196710.1021/acs.nanolett.5b01967 ↗
7. 10.1103/PhysRevLett.111.21680510.1103/PhysRevLett.111.216805 ↗
8. 10.1021/nl401316610.1021/nl4013166 ↗
9. 10.1021/nl401474810.1021/nl4014748 ↗
10. 10.1038/ncomms838110.1038/ncomms8381 ↗
11. 10.1103/PhysRevB.91.12140910.1103/PhysRevB.91.121409 ↗
12. 10.1038/ncomms567310.1038/ncomms5673 ↗
13. 10.1063/1.34718110.1063/1.347181 ↗
14. 10.1063/1.37018210.1063/1.370182 ↗
15. 10.1149/1.323663110.1149/1.3236631 ↗
16. 10.1038/nmat296810.1038/nmat2968 ↗
17. 10.1038/nphys136510.1038/nphys1365 ↗
18. 10.1002/adma.20140380810.1002/adma.201403808 ↗
19. 10.1063/1.480380310.1063/1.4803803 ↗
20. 10.1103/PhysRevB.87.15530410.1103/PhysRevB.87.155304 ↗
21. 10.1103/PhysRevLett.112.18680210.1103/PhysRevLett.112.186802 ↗
22. 10.1103/PhysRevLett.85.14610.1103/PhysRevLett.85.146 ↗
23. 10.1103/PhysRevLett.92.02680210.1103/PhysRevLett.92.026802 ↗
24. 10.1021/nl402875m10.1021/nl402875m ↗
25. 10.1038/ncomms729810.1038/ncomms7298 ↗
26. 10.1103/PhysRevLett.87.19680310.1103/PhysRevLett.87.196803 ↗
27. A. J.Pearce G.Burkard arXiv:1511.06254 [cond‐mat.mes‐hall].
28. 10.1103/PhysRevB.92.19540210.1103/PhysRevB.92.195402 ↗
29. 10.1038/srep0348910.1038/srep03489 ↗
30. 10.1021/nn203879f10.1021/nn203879f ↗
31. 10.1002/andp.20140009810.1002/andp.201400098 ↗
32. 10.1038/nmat350510.1038/nmat3505 ↗
33. 10.1021/nl403036h10.1021/nl403036h ↗
34. 10.1103/PhysRevB.85.16140310.1103/PhysRevB.85.161403 ↗
35. 10.1063/1.494835710.1063/1.4948357 ↗