Flaky polyacrylic acid/aluminium composite particles prepared using in-situ polymerization
Source abstract
Abstract
In order to prevent corrosion of flaky aluminium particles, flaky polyacrylic acid/aluminium composite particles were prepared using in-situ polymerization. The influences of dosage of acrylic acid, ammonium persulphate, isopropanol and water, as well as reaction temperature and reaction time, on corrosion inhibition efficiency and gloss were investigated. Maximum corrosion inhibition efficiency was 99.7% and the gloss was 88.3 Gs. Using TGA, SEM, laser particle size analysis, FTIR and XPS, polyacrylic acid was found to be coated on the surface of clear aluminium particles.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Surface Modification and Superhydrophobicity · Corrosion Behavior and Inhibition · Material Properties and Applications
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (12)
Show source-provided references
1. Aluminium pigments for powder coating applications10.1016/S1364-5439(05)70329-4 ↗
2. Optimisation of the shear stability of aluminium pigmented waterborne basecoats10.1016/S0300-9440(02)00058-9 ↗
3. Epoxy ester resins as corrosion inhibitors for aluminium and zinc pigments10.1016/j.corsci.2005.10.002 ↗
4. Activation of aluminium metal and its reaction with water10.1016/j.jallcom.2004.11.065 ↗
5. Surface modification for aluminium pigment inhibition10.1016/j.cis.2006.11.010 ↗
6. Nitro- and aminophenols as corrosion inhibitors for aluminium and zinc pigments10.1016/S0010-938X(98)00186-3 ↗
7. Encapsulated aluminium pigments10.1016/S0300-9440(99)00075-2 ↗
8. Corrosion protection of aluminium pigments by sol–gel coatings10.1016/j.corsci.2007.03.014 ↗
9. Adsorption characteristics of poly(acrylic acid) and poly(vinyl pyrrolidone) on alumina from their mixtures in aqueous solution10.1006/jcis.1996.4602 ↗
10. Polymeric corrosion inhibitors for aluminium pigment10.1016/S1381-5148(97)00179-X ↗
11. Coloured paints based on iron oxide and silicon oxide coated flakes of aluminium as the pigment, for energy efficient paint: optical and thermal experiments10.1016/S0927-0248(02)00410-5 ↗
12. Corrosion inhibition of zinc pigments in aqueous alkaline media by polymers10.1016/S0300-9440(97)00042-8 ↗