Study on microstructure and friction and wear properties of wear-resistant coatings prepared by thermal spraying
Source abstract
Abstract
In this paper, Cr2O3-2TiO2 and Al2O3 coatings are prepared by atmospheric plasma spraying (APS), and WC-10Co4Cr was prepared by high velocity oxygen fuel (HVOF). The powders and coatings are characterized with scanning electron microscopy (SEM) and energy dispersive spectrometry. X-ray diffraction (XRD) is used to qualitatively analyze the phase. The generation of new material is analyzed. The Vickers hardness of each coating is tested by microhardness tester. The tribological properties of the coatings are tested with the multifunctional material surface tester and the friction coefficient curves are drawn with the collected data. It is found that the friction and wear properties of the Cr2O3-2TiO2 coating are good due to the high degree of flattening during spraying. Cr2O3-2TiO2 coating has the highest average hardness. The phase structure is stable before and after spraying. Compared with the powder, the X-ray diffraction peaks of Al2O3 coating are seriously widened, some diffraction peaks are offset, and the intensity of the derived peaks is significantly reduced. Al2O3 coating has the largest hardness and lowest average hardness. However, compared with the other two coatings, Al2O3 coating has the worst wear resistance. It is also found that decarburization occurred during HVOF of WC-10Co4Cr. However, CoCr phase will wrap the WC, which can greatly reduce decarburization of WC during spraying. The bonding strength, wear resistance and toughness of the coating will be significantly enhanced. Compared with Al2O3 coating and Cr2O3-2TiO2 coating, the wear resistance of WC-10Co4Cr coating is slightly better.
Source: crossref · Quality: baseline
Research context
OpenAlex topics: High-Temperature Coating Behaviors · Advanced materials and composites · Metal and Thin Film Mechanics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (28)
Show source-provided references
1. "[1] L. Chen , G. J. Yang , Ch. X. Li et al., Advanced Ceramics 1, 3 (2016)
2. [2] J. J. Bai, Dalian University of Technology, (2012)
3. [3] Y. Ren , X. Ch. Lu , Y. Huang, Heat Treatment 1, 12 (2009)
4. [4] G. M. Xia , J. Q. Zhou , X. B. Min, Metal Materials and Metallurgy Engineering 1, 53 (2012)
5. [5] Y. Cui , F. Lin , X. J. Song et al., Nonferrous Metals S1, 65 (2006)
6. [6] B. S. Xu , S. H. Zhu , Theories and Technologies on Surface Engineering, (1999)
7. [7] C. X. Hu, Fundamentals and Application of Thermal Spraying, (1994)
8. [8] J. K. Murthy , D. S. Rao , B. Venkataraman, Wear 249(7), 592 (2001); https://doi.org/10.1016/S0043-1648(01)00682-210.1016/S0043-1648(01)00682-2 ↗
9. [9] P. Fauchais , Journal of Physics D Applied Physics 37(37), 86.(2004); https://doi.org/10.1088/0022-3727/37/9/R0210.1088/0022-3727/37/9/R02 ↗
10. [10] J. Zhang , Y. H. Niu, Ordnance Material Science and Engineering 41(04), 76 (2018)
11. [11] G. Li , T. Dong , H. Wang et al., Materials and Design 88(5), 906 (2015); https://doi.org/10.1016/j.matdes.2015.09.08510.1016/j.matdes.2015.09.085 ↗
12. [12] D. P. Weston , P. H. Shipway , S. J. Harris, Wear 267(5), 934 (2009); https://doi.org/10.1016/j.wear.2009.01.00610.1016/j.wear.2009.01.006 ↗
13. [13] R. J. K. Wood , S. Herd , M. R. Thakare, Tribology International 119, 491 (2018); https://doi.org/10.1016/j.triboint.2017.10.00610.1016/j.triboint.2017.10.006 ↗
14. [14] G. Xie, X. Song, D. Zhang et al. Applied Surface Science 256(21), 6354 (2010); https://doi.org/10.1016/j.apsusc.2010.04.01610.1016/j.apsusc.2010.04.016 ↗
15. [15] J. M. Marshall , M. Giraudel, International Journal of Refractory Metals and Hard Materials 49, 57 (2015); https://doi.org/10.1016/j.ijrmhm.2014.09.02810.1016/j.ijrmhm.2014.09.028 ↗
16. [16] T. Sudarpasert , P. H. Shipway , D. G. Mccartney, Wear 255(7), 943 (2003); https://doi.org/10.1016/S0043-1648(03)00293-X10.1016/S0043-1648(03)00293-X ↗
17. [17] V. A. D. Souza, A. Neville, Journal of Thermal Spray Technology 15(1), 106 (2006); https://doi.org/10.1361/105996306X9267710.1361/105996306X92677 ↗
18. [18] J. E. Cho, S. Y. Hwang, K.Y. Kim, Surface and Coating Technology 200(8), 2653 (2006); https://doi.org/10.1016/j.surfcoat.2004.10.14210.1016/j.surfcoat.2004.10.142 ↗
19. [19] Ch. J. Chen et al., Surface Technology 48(09), 224 (2019)
20. [20] H. M. Liu, Equipment Environmental Engineering 14(09), 6 (2017)
21. [21] D. I. Pantelis , P. Psyllaki, N. Alexopoulos, Wear 237(2), 197 (2000); https://doi.org/10.1016/S0043-1648(99)00324-510.1016/S0043-1648(99)00324-5 ↗
22. [22] R. Z. Li et al., SURFACE TECHNOLOGY 50(09), 184 (2021)
23. [23] Z. P. Zhao, H. L. Si, Zh. Sh. Li et al., Surface Technology 48(08), 225 (2019)
24. [24] Y. P. Song, Nanjing University Of Aeronautics And Astronautics, (2018)
25. [25] J. Zhao, X. M. Chen, L. Fu et al., Corrosion & Protection 41(05), 1 (2020)
26. [26] Q. Wang, Sh. Y. Zhang et al., Surface and Coatings Technology 218, 127 (2013); https://doi.org/10.1016/j.surfcoat.2012.12.04110.1016/j.surfcoat.2012.12.041 ↗
27. [27] J. F. Ni et al., Surface Technology 47(03), 210 (2018)
28. [28] P. B. Mi, T. Wang, F. X. Ye, International Journal of Refractory Metals and Hard Materials 69, 158 (2017); https://doi.org/10.1016/j.ijrmhm.2017.08.012"10.1016/j.ijrmhm.2017.08.012 ↗