Friction force microscopy study of diamond films modified by a glow discharge treatment

Abstract A glow discharge treatment technique has been developed which enables control of the surface roughness and morphology of diamond films for applications in optical and electrical components. A conventional hot filament chemical vapour deposition (CVD) system was used to deposit the diamond films onto silicon substrates via a three-step sequential process: (i) deposition under normal conditions; (ii) exposure to either a pure hydrogen plasma or 3% methane in an excess of hydrogen using DC-bias; and (iii) diamond deposition for a further 2 h under standard conditions. The frictional characteristics and roughness of the film surfaces were investigated by atomic force microscopy (AFM) and the morphology and the growth rates determined from scanning electron microscope images. Lateral force microscopy (LFM) has revealed significant differences in frictional behaviour between the high quality diamond films and those modified by a glow discharge treatment. Friction forces on the diamond films were very low, with coefficients ∼0.01 against silicon nitride probe tips in air. However, friction forces and coefficients were significantly greater on the DC-biased films indicating the presence of a mechanically weaker material such as an amorphous carbon layer. A combination of growth rate and frictional data indicated that the exposure to the H 2 plasma etched the diamond surface whereas exposure to CH 4 /H 2 plasma resulted in film growth. Re-Nucleation of diamond was possible (stage iii) after exposure to either plasma treatment. The resultant friction forces on these films were as low as on the standard diamond film.