Synthesis of dimethacryloxy ethyl-1,1,6,6-tetrahydro-perfluorohexamethylene-1,6-dicarbamate as dental base monomers and the mechanical properties ofthe copolymers of the monomer and methyl methacrylate
Source abstract
Abstract
To recognize good mechanical properties and water-resistance of a dental resin, dimethacryloxyethyl-1,1,6,6-tetrahydro-perfluoro-hexamethylene-1,6-dicarbamate (FDMHD) was newly synthesized. FDMHD initially was a white powder with m.p. 98.5-99.5°C. The copolymers of FDMHD and methyl methacrylate (MMA), FDMHD/MMA copolymers, were prepared to estimate the basic properties for dental resin materials. The compressive strength of FDMHD/MMA copolymers was almost the same compared with those of the copolymers of Bis-GMA or dimethacryloxyethyl-hexamethylene-1,6-carbamate (DMHD) and MMA. The bending, tensile, diametral tensile, impact strength and toughness of FDMHD/MMA copolymers containing 10.4 mol% FDMHD were higher than those of Bis-GMA/MMA copolymer, and the water sorption of FDMHD/MMA copolymers was lower than those of DMHD/MMA copolymers.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Photopolymerization techniques and applications · Silicone and Siloxane Chemistry · Dental materials and restorations
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (25)
Show source-provided references
1. 1) Paul GS, editor. New dental materials. 1st ed. New Jersey: Noyes Data Co; 1980. p. 29-98.
2. 2) Miyamoto R, Itoh K, Nagata K, Nakabayashi N. Preparation of 1,3-Bis(methacryloyloxyethyloxy)benzene and the application to composite resin. J J Dent Mater 1985; 4: 45-48.
3. 3) Kawaguchi M, Fukushima T, Miyazaki K, Horibe T, Habu T, Sawamura N. Synthesis and physical properties of polyfunctional methacrylates (Part 4). Synthesis and physical properties of aromatic dimethacrylate copolymer. Dent Mater J 1984; 3: 272-279.10.4012/dmj.3.272 ↗
4. 4) Anzai M, Yoshihashi K, Kikuchi H, Hirose H, Kojima S, Nishiyama M. Synthesis of cyclophosphazene linear monomers and mechanical properties of bulk polymers. J J Dent Mater 1993; 12: 257-264.
5. 5) Tomari M, Matsukawa S. Effect of polybutadiene polymethacrylates on the toughness of cured resin. J J Dent Mater 1993; 12: 326-335.
6. 6) Nakabayashi N, Arakane M. Preparation of 2’-acryloxyethyl 2-methacryloxyethylcarbamate and the application to light cured hard resin. J J Dent Mater 1987; 6: 131-134.
7. 7) Kawaguchi M, Fukushima T, Miyazaki K, Horibe T. Syntheses and physical properties of polyfunctional methacrylates (6) physical properties of spiro dimethacrylate copolymer. Dent Mater J 1985; 4: 201-207.10.4012/dmj.4.201 ↗
8. 8) Miyazaki K, Takata T, Endo T, Inanaga A. Thermal-and photo-polymerization of (meth)acrylates containing a spiro ortho ester moiety and the properties of poly[(meth)acrylate]s. Dent Mater J 1994; 13: 9-18.10.4012/dmj.13.9 ↗
9. 9) Kawaguchi M, Fukushima T, Horibe T. Effect of monomer structure on mechanical properties of light-cured composite resins. Dent Mater J 1989; 8: 40-45.10.4012/dmj.8.40 ↗
10. 10) Hirabayashi S, Hirasawa T. The application of fluorinated aromatic dimethacrylates and diacrylates to light-cured composite resins. Part 1 Improvement of transmittance of composite. J J Dent Mater 1990; 9: 778-785.
11. 11) Hirabayashi S, Hirasawa T. Improvements to light transmittance in light-cured composite resins by the utilization of low refractive index dimethacrylates. Dent Mater J 1990; 9: 203-214.10.4012/dmj.9.203 ↗
12. 12) Hirabayashi S, Hirasawa T. The application of fluorinated aromatic dimethacrylates and diacrylates to light-cured composite resins. Part 2 Improvement of transmittance and physical properties of composite. J J Dent Mater 1992; 11: 830-836.
13. 10.1016/S0109-5641(99)00028-710.1016/S0109-5641(99)00028-7 ↗
14. 14) Tanaka J, Inoue K, Masamura H, Matsumura K, Nakai H, Inoue K. The application of fluorinated aromatic dimethacrylates to experimental light-cured radiopaque composite resin, containing barium-borosilicate glass filler. Dent Mater J 1993; 12: 1-11.10.4012/dmj.12.1 ↗
15. 10.1016/0010-4361(92)90436-X10.1016/0010-4361(92)90436-X ↗
16. 16) Miyashita H. Fundamental studies on the copolymers of crystalline monomers having urethane linkages and hydroxypropyl methacrylate. 2.Physical properties of the copolymer. J Hiroshima Univ Soc 1979; 11: 181-204.
17. 17) Kawaguchi M. Development of new dental resin materials. Relationship between the structure and physical properties of urethane dimethacrylate polymers. J J Dent Mater 1988; 7: 143-158.
18. 1994 · 10 · 343
19. 10.1016/S0109-5641(98)00010-410.1016/S0109-5641(98)00010-4 ↗
20. 20) Kawaguchi M, Fukushima T, Horibe T, Watanabe T. Effect of aliphatic dimethacrylate diluent on the properties of UDMA resin systems. J J Dent Mater 1988; 7: 715-719.
21. 21) Takahashi K. Improvement of photo cured composite resin using low viscosity monomer substituted by fluorine. J J Dent Mater 2000; 19: 367-381.
22. 22) Miyashita H. Fundamental studies on the copolymers of crystalline monomers having urethane linkages and hydroxypropyl methacrylate. 1. Synthesis of the monomers. J Hiroshima Univ Soc 1979; 11: 151-180.
23. 23) Chambers RD: author. Fluorine in organic chemistry. 1st ed. New York: John Wiley; 1973. p. 5.
24. 24) Nagata K, Suzuki S, Nakabayashi N,Masuhara E. Preparation of hard crown and bridge resin without PMMA powder (II). J Jpn Soc Dent Apparat Mat 1979; 20: 151-154.
25. 25) Kurata S, Yamazaki N. Molecular composite resins for dental use. II.Physical properties of copolymers of MMA-polyfunctional siloxane oligomers. J J Dent Mater 1986; 5: 106-109.