Effects of silane coupling agents and solutions of different polarity on PMMA bonding to alumina
Source abstract
Abstract
The objective of this study was to clarify the effects of silane coupling agents and solutions of different polarity on polymethyl methacrylate (PMMA) bonding to alumina. Three silane coupling agents (3-methacryloxypropyltrimethoxysilane (MPS),3-aminopropyltriethoxysilane (APS) and N-2 (aminoethyl) 3-aminopropyltriethoxysilane) and 3 different polar solutions, 70% ethanol, isopropanol and toluene, were selected for silanization. Shear bond strengths were statistically compared with Tukey HSD(α=0.05). The alumina surfaces after silanization and shear bond test were examined with an energy dispersive spectrometer (EDS).The bond strengths of PMMA on the alumina with MPS (15.0 MPa), APS (13.8 MPa) in ethanol were greater than the others in nonthermocyclings. The bond strength decreased after thermocyclings. The ethanol groups were greater than the others. EDS revealed Si remaining on the alumina surface after the shear bond test. The results indicated that the silanization using MPS and APS with ethanol solution was effective.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Dental materials and restorations · Innovations in Concrete and Construction Materials · Silicone and Siloxane Chemistry
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (21)
Show source-provided references
1. 1) Darbar UR, Huggett R, Harrison A. Denture fracture 窶蚤 survey. Br Dent 1994; 176: 342-345.10.1038/sj.bdj.4808449 ↗
2. 10.1016/j.dental.2007.07.00310.1016/j.dental.2007.07.003 ↗
3. 3) Tu MG, Liang WM, Wu TC, Chen SY. Improving the mechanical properties of fiber-reinforced acrylic denture-base resin. Mater and Design 2009; 30: 2468-2472.10.1016/j.matdes.2008.10.009 ↗
4. 4) Abboud M, Vol S, Duguet E. PMMA-based composite materials with reactive ceramic fillers, Part III: Radiopacifying particle reinforced bond cement. J Mater Sci: Mater in Med 2000; 11: 295-300.10.1023/A:1008981917653 ↗
5. 5) Ellakwa AE, Morsy MA, El-Sheikh AM. Effect of aluminum oxide addition on the flexural strength and thermal diffusivity of heat-polymerized acrylic resin. J Prosthodont 2008; 17: 439-444.10.1111/j.1532-849X.2008.00318.x ↗
6. 6) Alhareb AO, Ahmad ZA. Effect of Al2O3/ZrO2 reinforcement on the mechanical properties of PMMA denture base. J Reinf Plast Compos 2011; 30: 85-83.
7. 10.1002/app.1987.07034042110.1002/app.1987.070340421 ↗
8. 10.4012/dmj.23.3110.4012/dmj.23.31 ↗
9. 9) Matinlinna JP, Lassila LVJ, Ozcan M, Yli-Urpo A, Vallittu PK. An introduction to silanes and their clinical applications in dentistry. Int J Prosthodont 2004; 17: 155-164.
10. 10.1016/S0022-3913(05)80200-810.1016/S0022-3913(05)80200-8 ↗
11. 11) Blixt M, Adamczak E, Linden LA, Oden A, Arvidson K. Bonding to densely sintered alumina surfaces: effect of sandblasting and silica coating on shear bond strength of luting cements. Int J Prosthodont 2000; 13: 221-226.
12. 15) Choi YS, Chung IJ. Poly(n-butyl acrylate-co-methyl methacrylate) and poly(n-butyl acrylate-co-styrene)/silicate nanocomposites prepared by emulsion polymerization. Macromol Res 2003; 11: 425-430.10.1007/BF03218971 ↗
13. 10.1016/S0079-6700(03)00045-510.1016/S0079-6700(03)00045-5 ↗
14. 17) Chen TM, Brauer GM. Solvent effects on bonding organosilane to silica surfaces. J Dent Res 1982; 61: 1439-1443.10.1177/00220345820610121301 ↗
15. 19) Stanford CJ, Dagenais M, Park JH, DeShong P. Real-Time monitoring of siloxane monolayer film formation on silica using a fiber bragg grating. Curr Anal Chem 2008; 4: 356- 361.10.2174/157341108785914916 ↗
16. 20) Vallant T, Brunner H, Mayer U, Hoffman H, Leitner T, Resch R, Friedbacher G. Formation of self-assembled octadecylsiloxane monolayers on mica and silicon surfaces studied by atomic force microscopy and infrared spectroscopy. J Phy Chem B 1998; 102: 7190-7197.10.1021/jp981282g ↗
17. 10.1016/j.dental.2010.11.00210.1016/j.dental.2010.11.002 ↗
18. 23) Nakamura S, Yoshida K, Kamada K, Atsuta M. Bonding between resin luting cement and glass infiltrated alumina-reinforced ceramics with silane coupling agent. J Oral Rehabil 2004; 31: 785-789.10.1111/j.1365-2842.2004.01304.x ↗
19. 24) Plueddemann EP. Silane Coupling Agents. New York: Plenum Press; 1991. p. 56-58.10.1007/978-1-4899-2070-6 ↗
20. 10.1016/j.dental.2006.06.05210.1016/j.dental.2006.06.052 ↗
21. 27) Arkles B, Steinmetz JR, Zazyczny J, Mehta P. In: Mittal KL, editor. Silanes and other coupling agents. Utrecht: VSP; 1992. p. 91-104.