Effect of composition of experimental fluorinated soft lining materials on bond strength to denture base resin
Source abstract
Abstract
The purpose of the present study was to investigate the effect of the composition of experimental fluorinated soft lining materials on bond strength to denture base resin. Vinylidene fluoride/hexafluoro propylene copolymer (2-6F), tridecafluorooctyl methacrylate (13FMA), methoxy diethylene glycol methacrylate (MDGMA), and silica (as filler) were used for fabrication of the experimental soft lining materials. Nine experimental soft lining materials having various compositions of 2-6F, 13FMA, and MDGMA were prepared. Shear and tensile bond strength tests were performed before and after immersion in water. The water sorption for the materials was also measured. An increase in the content of acrylic monomer, MDGMA, in the experimental materials increased the bond strength before immersion in water but reduced the bond strength after immersion in water as compared to that before immersion in water. The inclusion of fluorinated monomer (13FMA) in the materials appeared to affect water sorption.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Dental materials and restorations · Dental Erosion and Treatment · Dental Implant Techniques and Outcomes
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (41)
Show source-provided references
1. 1) Fenlon MR, Sherriff M. Investigation of new complete denture quality and patients’ satisfaction with and use of dentures after two years. J Dent 2004; 32: 327-333.10.1016/j.jdent.2004.01.007 ↗
2. 2) Braden M, Wright PS, Parker S. Soft lining materials—a review. Eur J Prosthodont Restor Dent 1995; 3: 163-174.
3. 3) Garcia LT, Jones JD. Soft liners. Dent Clin North Am 2004; 48: 709-720.10.1016/j.cden.2004.03.001 ↗
4. 4) Mack PJ. Denture soft lining materials: clinical indications. Aust Dent J 1989; 34: 454-458.10.1111/j.1834-7819.1989.tb00704.x ↗
5. 5) McCabe JF. A polyvinylsiloxane denture soft lining material. J Dent 1998; 26: 521-526.10.1016/S0300-5712(98)00022-0 ↗
6. 6) Moriya N, Akagawa Y. The state and future of denture base soft lining materials. J Hiroshima Univ Dent Soc 1994; 26: 360-368.
7. 7) Jones DW, Hall GC, Sutow EJ, Langman MF, Robertson KN. Chemical and molecular weight analyses of prosthodontic soft polymers. J Dent Res 1991; 70: 874-879.10.1177/00220345910700050201 ↗
8. 8) Morii K, Miwa J, Okuno Y, Suginaka H. Microbiological aspects of filth on acryl soft liners. J Jpn Prosthodont Soc 1978; 22: 679-683.10.2186/jjps.22.679 ↗
9. 9) Giunta JL, Grauer I, Zablotsky N. Allergic contact stomatitis caused by acrylic resin. J Prosthet Dent 1979; 42: 188-190.10.1016/0022-3913(79)90173-2 ↗
10. 10) Hensten-Pettersen A, Jacobsen N. Perceived side effects of biomaterials in prosthetic dentistry. J Prosthet Dent 1991; 65: 138-144.10.1016/0022-3913(91)90066-6 ↗
11. 11) Kutay O. Comparison of tensile and peel bond strengths of resilient liners. J Prosthet Dent 1994; 71: 525-531.10.1016/0022-3913(94)90194-5 ↗
12. 12) Ishimoto T. A study on adhesion of Candida albicans to silicone soft lining materials. J Jpn Prosthodont Soc 2004; 48: 94-103.10.2186/jjps.48.94 ↗
13. 13) Hayakawa I, Akiba N, Keh E, Kasuga Y. Physical properties of a new denture lining material containing a fluoroalkyl methacrylate polymer. J Prosthet Dent 2006; 96: 53-58.10.1016/j.prosdent.2006.05.012 ↗
14. 14) Akiba N, Keh E, Hayakawa, Hatanaka K. A new denture relining material with fluorocarbon chain. J J Dent Mater 2002; 21: 323-327.
15. 15) Hayakawa I, Kawae M, Tsuji Y, Masuhara E, Eng B. Soft denture liner of fluoroetylene copolymer and its clinical evaluation. J Prosthet Dent 1984; 51: 310-313.10.1016/0022-3913(84)90210-5 ↗
16. 16) Hayakawa I, Nomura T, Matsui K, Suzuki K, Nagao M, Masuhara E. Development of soft denture Liner (dough- type) of fluoroetylene copolymer. J Jpn Prosthodont Soc 1986; 30: 321-325.10.2186/jjps.30.321 ↗
17. 17) United Nations Environment Programme. Montreal protocol on substances that deplete the ozone layer. Article 2D: Carbon tetrachloride, 1987.
18. 18) Ohe Y, Kadoma Y, Imai Y. Study on visible-light curing soft resins consisting of fluoropolymers (Part 3) Application of flow molecular weight fluoropolymer. J Jpn Dent Mater 1990; 9: 654-658.
19. 19) Hirano H, Ohe Y, Kadoma Y, Imai Y. Study on denture liner consisting of fluoropolymer and MMA. J Jpn Dent Mater 1992; 11: 947-954.
20. 20) Suzuki T, Imai Y. Light curing soft denture liner using liquid fluoropolymer. part II. effect of cross-linking agents. J Jpn Dent Mater 1994; 13: 541-544.
21. 21) Kasuga Y, Akiba N, Minakuchi S, Uchida T, Matsushita N, Hishimoto M, Hayakawa I. Development of soft denture lining materials containing fluorinated monomers. J Jpn Prosthodont Soc 2008; 52: 183-188.10.2186/jjps.52.183 ↗
22. 22) Kasuga Y,Takahashi H, Akiba N , Minakuchi S ,Matsushita N,Hishimoto M. Basic evaluation on physical properties of experimental fluorinated softlining materials. Dent Mater J 2011; 30: 45-51.10.4012/dmj.2010-084 ↗
23. 23) Al-Athel MS, Jagger RG. Effect of test method on the bond strength of a silicone resilient denture lining material. J Prosthet Dent 1996; 76: 535-540.10.1016/S0022-3913(96)90014-1 ↗
24. 24) Aydin AK, Terzioglu H, Akinay AE, Ulubayram K, Hasirci N.Bond strength and failure analysis of lining materials to denture resin. Dent Mater 1999; 15: 211-218.10.1016/S0109-5641(99)00038-X ↗
25. 25) Baysan A, Parker S, Wright PS. Adhesion and tear energy of a long-term soft lining material activated by rapid microwave energy. J Prosthet Dent 1998; 79: 182-187.10.1016/S0022-3913(98)70214-8 ↗
26. 26) Mutluay MM, Ruyter IE. Evaluation of bond strength of soft relining materials to denture base polymers. Dent Mater 2007; 23: 1373-1381.10.1016/j.dental.2006.11.014 ↗
27. 27) Mutluay MM, Oguz S, Fløystrand F, Saxegaard E, Dogan A, Bek B, Ruyter IE. A prospective study on the clinical performance of polysiloxane soft liners: one-year results. Dent Mater J 2008; 27: 440-447.10.4012/dmj.27.440 ↗
28. 28) Usumez A, Inan O, Aykent F. Bond strength of a silicone lining material to alumina-abraded and lased denture resin. J Biomed Mater Res 2004; 71B: 196-200.10.1002/jbm.b.30078 ↗
29. 29) Wright PS. Characterization of the adhesion of soft lining materials to poly (methyl methacrylate). J Dent Res 1982; 61: 1002-1005.10.1177/00220345820610080101 ↗
30. 30) Weight PS. The success and failure of denture soft-lining materials in clinical use. J Dent 1984; 12: 319-327.10.1016/0300-5712(84)90090-3 ↗
31. 31) International Organization for Standardization. ISO 10139-2. Dentistry –Soft lining materials for removable dentures–Part 2: Materials for long-term use, 2nd ed, 2009.
32. 32) McCabe JF, Carrick TE, Kamohara H. Adhesive bond strength and compliance for denture soft lining materials. Biomaterials 2002; 23: 1347-1352.10.1016/S0142-9612(01)00253-8 ↗
33. 33) El-Hadary A, Drummond JL. Comparative study of water sorption, solubility, and tensile bond strength of two soft lining materials. J Prosthet Dent 2000; 83: 356-361.10.1016/S0022-3913(00)70140-5 ↗
34. 34) Kutay O, Bilgin T, Sakar O, Beyli M. Tensile bond strength of a soft lining with acrylic denture base resins. Eur J Prosthodont Restor Dent 1994; 2: 123-126.
35. 35) Sertgoz A, Kulak Y, Gedik H, Taskonak B. The effect of thermocycling on peel strength of six soft lining materials. J Oral Rehabil 2002; 29: 583-587.10.1046/j.1365-2842.2002.00888.x ↗
36. 36) Tuna SH, Keyf F, Gumus HO, Uzun C. The Evaluation of water sorption/ solubility on various acrylic resins. Eur J Dent 2008; 2: 191-197.10.1055/s-0039-1697377 ↗
37. 37) Hayakawa I, Keh E, Morizawa M, Muraoka G, Hirano S. A new polyisoprene-based light-curing denture soft lining material. J Dent 2003; 31: 269-274.10.1016/S0300-5712(03)00031-9 ↗
38. 38) Stansbury JW, Antonucci JM. Dimethacrylate monomers with varied fluorine contents and distributions. Dent Mater 1999; 15: 166-173.10.1016/S0109-5641(99)00028-7 ↗
39. 39) Polyzois GL. Adhesion properties of resilient lining materials bonded to light-cured denture resins. J Prosthet Dent 1992; 68: 854-858.10.1016/0022-3913(92)90216-W ↗
40. 40) Alcântara CS, Macêdo AF, Gurgel BC, Jorge JH, Neppelenbroek KH, Urban VM. Peel bond strength of resilient liner modified by the addition of antimicrobial agents to denture base acrylic resin. J Appl Oral Sci 2012; 20: 607-612.10.1590/S1678-77572012000600004 ↗
41. 41) Barsby MJ. A denture base resin with low water absorption. J Dent 1992; 20: 240-244.10.1016/0300-5712(92)90094-S ↗