journal article·2018-10Open access

Intracoronal stress transfer through enamel following RBC photopolymerisation: A synchrotron X-ray study

Maisoon Al-Jawad, Owen Addison, Slobodan Sirovica, Samera Siddiqui, Richard A. Martin, David J. Wood, David C. Watts

Dental Materials· Volume 34· Issue 10

Abstract

Objectives To measure the spatial distribution of crystallographic strain in tooth enamel induced by the photo-polymerisation of a dimethacrylate resin based composite cavity restoration. Methods Six sound first premolar teeth, allocated into two groups (n=3), were prepared with mesio-occlusal distal cavities. The enamel was machined at the point of maximum convexity on the outer tooth to create a vertical fin of thickness 100μm and 0.5mm depth to allow for synchrotron X-ray diffraction measurements. 2D diffraction patterns were used to determine crystallite orientation and quantify changes in the hydroxyapatite crystal lattice parameters, before and after photo-polymerisation of a composite material placed in the cavity, to calculate strain in the respective axis. The composite was photo-polymerised with either relatively high (1200mWcm-2, group 1) or low (480mWcm-2, group 2) irradiances using LED or quartz halogen light sources, respectively. A paired t-test was used to determine significant differences in strain between irradiance protocols at ɑ=0.001. Results Photo-polymerisation of the composite in the adjacent cavity induced significant changes in both the crystallographic c and a axes of the enamel measurement area. However the magnitude of strain was low with ∼0.1% difference before and after composite photo-polymerisation. Strain in enamel was not uniformly distributed and varied spatially as a function of crystallite orientation. Increased alignment of crystallites perpendicular to the cavity wall was associated with higher c axis strain. Additionally, strain was significantly greater in the c (p<0.001) and a axis (p<0.001) when using a high irradiance photo-polymerisation protocol. Significance Although cuspal deflection is routinely measured to indirectly assess the 'global' effect of composite shrinkage on the tooth-restoration complex, here we show that absolute strains generated in enamel are low, indicating strain relief mechanisms may be operative. The use of low irradiance protocols for photo-polymerisation resulted in reduced strain.
Source: europepmc · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Dental materials and restorations · Laser Applications in Dentistry and Medicine · Photopolymerization techniques and applications

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (75)

Show source-provided references
1. Alternatives in polymerization contraction stress management10.1177/154411130401500306 ↗
2. Effects of monomer ratios and highly radiopaque fillers on degree of conversion and shrinkage-strain of dental resin composites10.1016/j.dental.2009.06.009 ↗
3. Intrinsic ‘soft-start’ polymerisation shrinkage-kinetics in an acrylate-based resin-composite10.1016/S0109-5641(99)00012-3 ↗
4. Effect of irradiation type (LED or QTH) on photo-activated composite shrinkage strain kinetics, temperature rise, and hardness10.1034/j.1600-0722.2002.21359.x ↗
5. In vitro cuspal deflection and microleakage of maxillary premolars restored with novel low-shrink dental composites10.1016/j.dental.2004.05.005 ↗
6. Chapter 5–Acrylic
7. Light intensity effects on resin-composite degree of conversion and shrinkage strain10.1016/S0109-5641(00)00020-8 ↗
8. Conversion-dependent shrinkage stress and strain in dental resins and composites10.1016/j.dental.2004.10.006 ↗
9. Cuspal deflection and microleakage in premolar teeth restored with resin-based composites with and without an intermediary flowable layer10.1016/j.jdent.2007.01.005 ↗
10. Cuspal deflection and microleakage in premolar teeth restored with bulk-fill flowable resin-based composite base materials10.1016/j.jdent.2012.02.015 ↗
11. Cuspal deflection, strain and microleakage of endodontically treated premolar teeth restored with direct resin composites10.1016/j.jdent.2009.05.027 ↗
12. Cuspal deflection and cervical microleakage scores to determine the adhesive potential of universal bonding systems10.1016/j.jdent.2014.05.013 ↗
13. Cuspal movement and microleakage in premolar teeth restored with resin-based filling materials cured using a ‘soft-start’ polymerisation protocol10.1016/j.dental.2006.06.002 ↗
14. Cuspal deflection during polymerisation of composite lutes of ceramic inlays10.1016/S0300-5712(98)00028-1 ↗
15. Effect on cusp deflection and gap formation in composite restorations
16. Non-destructive examination of interfacial debonding using acoustic emission10.1016/j.dental.2011.06.002 ↗
17. Developments in shrinkage control of adhesive restoratives10.1111/j.1708-8240.2000.tb00238.x ↗
18. Longevity of direct resin composite restorations in posterior teeth10.1007/s00784-003-0206-7 ↗
19. The Competition between the composite–dentin bond strength and the polymerization contraction stress10.1177/00220345840630121101 ↗
20. Polymerization shrinkage and polymerization shrinkage stress in polymer-based restoratives10.1016/S0300-5712(96)00063-2 ↗
21. Physicomechanical evaluation of low-shrinkage dental nanocomposites based on silsesquioxane cores10.1111/j.1600-0722.2007.00449.x ↗
22. Assessing the effect of composite formulation on polymerization stress10.14219/jada.archive.2000.0207 ↗
23. Effect of TEGDMA/BisGMA ratio on stress development and viscoelastic properties of experimental two-paste composites10.1177/154405910308201012 ↗
24. Light-curing units, polymerization, and clinical implications
25. Marginal adaptation of a restorative resin polymerized at reduced rate10.1111/j.1600-0722.1991.tb01052.x ↗
26. Physical properties and gap formation of light-cured composites with and without ‘softstart-polymerization’10.1016/S0300-5712(96)00044-9 ↗
27. The influence of plasma arc vs. halogen standard or soft-start irradiation on polymerization shrinkage kinetics of polymer matrix composites10.1016/S0300-5712(03)00089-7 ↗
28. Reduced light energy density decreases post-gel contraction while maintaining degree of conversion in composites10.1016/S0300-5712(97)00048-1 ↗
29. Setting stress in composite resin in relation to configuration of the restoration10.1177/00220345870660110601 ↗
30. Increased wall-to-wall curing contraction in thin bonded resin layers10.1177/00220345890680010701 ↗
31. Influence of cavity dimension and restoration methods on the cusp deflection of premolars in composite restoration10.1016/j.dental.2006.01.025 ↗
32. In vitro posterior composite polymerization recovery following hygroscopic expansion10.1111/j.1365-2842.1993.tb01636.x ↗
33. In vitro measurement of cuspal strain and displacement in composite restored teeth10.1016/S0300-5712(96)00047-4 ↗
34. Cusp movement in molar teeth using dentine adhesives and composite filling materials10.1016/0142-9612(87)90084-6 ↗
35. Interferometric measurements of cusp deformation of teeth restored with composites10.1177/00220345930720111201 ↗
36. Effect of liners on cusp deflection and gap formation in composite restorations
37. Structure and composition of enamel
38. Enamel—a “metallic-like” deformable biocomposite10.1016/j.jdent.2006.12.002 ↗
39. Influence of structural hierarchy on the fracture behaviour of tooth enamel
40. Organic matrix of tooth enamel10.1038/187411b0 ↗
41. Sheathlin: cloning, cDNA/polypeptide sequences, and immunolocalization of porcine enamel sheath proteins10.1177/00220345970760020501 ↗
42. Understanding the mechanical behaviour of human enamel from its structural and compositional characteristics10.1016/j.jmbbm.2007.05.001 ↗
43. Enamel matrix: structural proteins10.1177/00220345790580022901 ↗
44. Maximal bite force and its association with signs and symptoms of craniomandibular disorders in young Finnish non-patients10.3109/00016359509005982 ↗
45. Occlusal contact area of mandibular teeth during lateral excursion
46. Indentation damage and mechanical properties of human enamel and dentin10.1177/00220345980770030601 ↗
47. Compositional determinants of mechanical properties of enamel10.1177/154405910808700711 ↗
48. Beitrag zur Geschichte der Zähne
49. The nature of the Hunter–Schreger bands in enamel10.1016/0003-9969(65)90086-5 ↗
50. Protein interactions during assembly of the enamel organic extracellular matrix10.1359/jbmr.1997.12.2.221 ↗
51. Protein–protein interactions of the developing enamel matrix10.1016/S0070-2153(06)74003-0 ↗
52. Enamel matrix proteins and ameloblast biology10.3109/03008209509013710 ↗
53. Distribution of enamel crystallite orientation through an entire tooth crown studied using synchrotron X-ray diffraction10.1111/j.1600-0722.2011.00909.x ↗
54. 2D mapping of texture and lattice parameters of dental enamel10.1016/j.biomaterials.2007.02.019 ↗
55. Distribution of enamel crystallite orientation through an entire tooth crown studied using synchrotron x-ray diffraction10.1111/j.1600-0722.2011.00909.x ↗
56. A three-dimensional finite element model of prismatic enamel: a re-appraisal of the data on the Young’s modulus of enamel10.1177/00220345970760101101 ↗
57. Biological organization of hydroxyapatite crystallites into a fibrous continuum toughens and controls anisotropy in human enamel10.1177/00220345010800010501 ↗
58. Structural integrity of enamel: experimental and modelling10.1177/0022034509337130 ↗
59. Nanoindentation creep behavior of human enamel10.1002/jbm.a.32223 ↗
60. Marginal adaptation of a restorative resin polymerized at reduced rate
61. Physical properties and gap formation of light-cured composites with and without ‘softstart-polymerization’10.1016/S0300-5712(96)00044-9 ↗
62. Soft-start polymerization and marginal gap formation in vitro
63. Effect of light exposure on fracture toughness and flexural strength of light-cured composites10.1016/S0109-5641(96)80042-X ↗
64. Comparison of methods for measuring cuspal deformation in teeth10.1016/S0300-5712(00)00040-3 ↗
65. Factors involved in the development of polymerization shrinkage stress in resin-composites: a systematic review10.1016/j.dental.2005.04.018 ↗
66. A test beamline on Diamond Light Source10.1063/1.3463220 ↗
67. B16 Facility and Equipment Availability. http://www.diamond.ac.uk/Beamlines/Materials/B16/status.html. [Accessed 29 June 2017].
68. Recovery of crystallographic texture in remineralized dental enamel10.1371/journal.pone.0108879 ↗
69. Mixed-mode stress intensity factors for kink cracks with finite kink length loaded in tension and bending: application to dentin and enamel10.1016/j.jmbbm.2009.12.004 ↗
70. The fracture behaviour of dental enamel10.1016/j.biomaterials.2009.09.050 ↗
71. Compressive residual strains in mineral nanoparticles as a possible origin of enhanced crack resistance in human tooth dentin10.1021/acs.nanolett.5b00143 ↗
72. The effects of light intensity, temperature, and comonomer composition on the polymerization behavior of dimethacrylate dental resins10.1177/00220345990780081301 ↗
73. Odian · 1991
74. The reciprocity law concerning light dose relationships applied to BisGMA/TEGDMA photopolymers: theoretical analysis and experimental characterisation10.1016/j.dental.2014.02.021 ↗
75. Outline and arrangement of enamel rods in human deciduous and permanent enamel: 3D-reconstructions obtained from CLSM and SEM images based on serial ground sections10.1034/j.1600-0722.2001.00149.x ↗