Nanostructured Li₂MnSiO₄/C Cathodes with Hierarchical Macro‐/Mesoporosity for Lithium‐Ion Batteries

Li₂MnSiO₄/C nanocomposite with hierarchical macroporosity is prepared with poly(methyl methacrylate) (PMMA) colloidal crystals as a sacrificial hard‐template and water‐soluble phenol‐formaldehyde (PF) resin as the carbon source. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) analyses confirm that the periodic macropores are ≈400 nm in diameter with 20–40 nm walls comprising Li₂MnSiO₄/C nanocrystals that produce additional large mesopores (< 30 nm) between the nanocrystals. The nanostructured Li₂MnSiO₄/C cathode exhibits a high reversible discharge capacity of 200 mAh g⁻¹ at C/10 (16 mA g⁻¹) rate at 1.5–4.8 V at 45 °C. Although the discharge capacity can be further increased on operating at 55 °C, the sample exhibits a relatively fast capacity fade at 55 °C, which can be partially solved by simply narrowing the voltage window to avoid side reactions of the electrolyte. The good performance of the Li₂MnSiO₄/C cathodes is attributed to the unique macro‐/mesostructure of the silicate coupled with uniform carbon coating.