Microstructured Nematic Liquid Crystalline Elastomer Surfaces with Switchable Wetting Properties

Zi Liang Wu, Axel Buguin, Hong Yang, Jean‐Marie Taulemesse, Nicolas Le Moigne, Anne Bergeret, Xiaogong Wang, Patrick Keller

Advanced Functional Materials· Volume 23· Issue 24

Abstract

Abstract Inspired by the lotus leaf, scientists have developed many superhydrophobic surfaces, some of which show remarkable switching between hydrophobic and hydrophilic state under external stimuli. However, the switch usually relies on the change of chemical properties rather than on the modification of the topographic structure of the surface. In this paper, the roughness‐change‐related switchable wetting properties of microstructured responsive surfaces made of nematic liquid crystalline elastomers (LCEs) is reported. First, various carbonate LC monomers and side‐on LCEs are synthesized with low nematic‐to‐isotropic transition temperature, TNI. Then, LCEs prepared from 3″‐vinylcarbonyloxypropyl 2,5‐di(4′‐octyloxybenzoyloxy)benzoate monomer, with TNI of 76 °C and contraction of 34% are used to construct a surface covered with micropillar arrays by using a replica molding technique. The contraction of the micropillars induces a reversible roughness change of the microstructured surface. Water contact angle of this microstructured surface changed with temperature, indicating a successful approach at building a surface with switchable wetting properties.
Source: crossref · Quality: baseline

Research context

OpenAlex topics: Advanced Materials and Mechanics · Surface Modification and Superhydrophobicity · Advanced Sensor and Energy Harvesting Materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (64)

Show source-provided references
1. 10.1098/rsif.2007.021810.1098/rsif.2007.0218 ↗
2. 10.1038/nmat133910.1038/nmat1339 ↗
3. 10.1038/nature0860310.1038/nature08603 ↗
4. 10.1038/nature0194110.1038/nature01941 ↗
5. 10.1002/adma.20029002010.1002/adma.200290020 ↗
6. 10.1039/c2cs15267c10.1039/c2cs15267c ↗
7. 10.1073/pnas.153470110010.1073/pnas.1534701100 ↗
8. 10.1039/B712575P10.1039/B712575P ↗
9. 10.1002/ange.20046033310.1002/ange.200460333 ↗
10. 10.1021/la061400o10.1021/la061400o ↗
11. 10.1039/C1SM07003G10.1039/C1SM07003G ↗
12. 10.1039/b602486f10.1039/b602486f ↗
13. 10.1039/B803951H10.1039/B803951H ↗
14. 10.1021/cm903831c10.1021/cm903831c ↗
15. 10.1002/adma.20110046910.1002/adma.201100469 ↗
16. 10.1021/ja069257910.1021/ja0692579 ↗
17. 10.1021/ja038636o10.1021/ja038636o ↗
18. 10.1002/adma.20090090310.1002/adma.200900903 ↗
19. 10.1088/0953-8984/17/1/R0110.1088/0953-8984/17/1/R01 ↗
20. 10.1103/PhysRevLett.95.12430110.1103/PhysRevLett.95.124301 ↗
21. 10.1038/nmat111810.1038/nmat1118 ↗
22. 10.1098/rsta.2006.185310.1098/rsta.2006.1853 ↗
23. 10.1038/nmat248710.1038/nmat2487 ↗
24. 10.1002/anie.20060237210.1002/anie.200602372 ↗
25. 10.1002/adma.20110013110.1002/adma.201100131 ↗
26. 10.1002/macp.20090030810.1002/macp.200900308 ↗
27. 10.1002/adma.20030455210.1002/adma.200304552 ↗
28. 10.1002/adma.20040065810.1002/adma.200400658 ↗
29. 10.1016/S0079-6700(97)00007-510.1016/S0079-6700(97)00007-5 ↗
30. 10.1002/marc.1991.03012121110.1002/marc.1991.030121211 ↗
31. 10.1021/ma001639q10.1021/ma001639q ↗
32. 10.1073/pnas.101765810810.1073/pnas.1017658108 ↗
33. 10.1002/adma.20090405910.1002/adma.200904059 ↗
34. 10.1039/C0SM00734J10.1039/C0SM00734J ↗
35. 10.1002/adma.20120089510.1002/adma.201200895 ↗
36. 10.1002/adma.20090152210.1002/adma.200901522 ↗
37. 10.1002/adfm.20100117810.1002/adfm.201001178 ↗
38. 10.1021/ja109525410.1021/ja1095254 ↗
39. 10.1038/ncomms219310.1038/ncomms2193 ↗
40. 10.1021/ja057507010.1021/ja0575070 ↗
41. 10.1021/ja905363f10.1021/ja905363f ↗
42. 10.1063/1.472914310.1063/1.4729143 ↗
43. 10.1002/marc.1982.03003080610.1002/marc.1982.030030806 ↗
44. 10.1016/0014-3057(95)00030-510.1016/0014-3057(95)00030-5 ↗
45. 10.1021/ma00067a01310.1021/ma00067a013 ↗
46. 10.1039/c1jm13658e10.1039/c1jm13658e ↗
47. 10.1007/BF0025496310.1007/BF00254963 ↗
48. 10.1021/ma00050a03210.1021/ma00050a032 ↗
49. 10.1021/ja963687p10.1021/ja963687p ↗
50. 10.1002/polb.1005810.1002/polb.10058 ↗
51. E‐VC8 (n= 3) could not be used to prepare surface with long pillars (dimension: diameter = 20 μm length = 100 μm spacing = 100 μm). When peeling off the mold most the pillars made of E‐VC8 (n= 3) were broken because of its softness and lacking sufficient mechanical strength even in the glassy state.
52. 10.1039/tf944400054610.1039/tf9444000546 ↗
53. 10.1039/b501657f10.1039/b501657f ↗
54. 10.1038/nmat92410.1038/nmat924 ↗
55. 10.1021/la020088p10.1021/la020088p ↗
56. 10.1021/la049329e10.1021/la049329e ↗
57. 10.1021/ja038026o10.1021/ja038026o ↗
58. 10.1088/0953-8984/20/22/22501010.1088/0953-8984/20/22/225010 ↗
59. 10.1016/0032-3861(82)90145-810.1016/0032-3861(82)90145-8 ↗
60. 10.1016/0032-3861(85)90209-510.1016/0032-3861(85)90209-5 ↗
61. 10.1002/pola.2447610.1002/pola.24476 ↗
62. 10.1039/C1CS15232G10.1039/C1CS15232G ↗
63. This process would not lead to the hydrolysis of carbonate group in the LCEs. The LCEs before and after dissolving the glass cell had the sameTNI as confirmed by thermal optical polarizing microscopy.
64. 10.1002/(SICI)1521-3773(19980316)37:5<550::AID-ANIE550>3.0.CO;2-G10.1002/(SICI)1521-3773(19980316)37:5<550::AID-ANIE550>3.0.CO;2-G ↗